CN102584339A - 一种以赤泥为原材料的棕色陶瓷色料的制备方法 - Google Patents

一种以赤泥为原材料的棕色陶瓷色料的制备方法 Download PDF

Info

Publication number
CN102584339A
CN102584339A CN2012100687081A CN201210068708A CN102584339A CN 102584339 A CN102584339 A CN 102584339A CN 2012100687081 A CN2012100687081 A CN 2012100687081A CN 201210068708 A CN201210068708 A CN 201210068708A CN 102584339 A CN102584339 A CN 102584339A
Authority
CN
China
Prior art keywords
red mud
ceramic pigment
brown ceramic
red
oxide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012100687081A
Other languages
English (en)
Inventor
王新平
胡猛
朱峰
徐荣丰
赵勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
FOSHAN SANSHUI JINYING INORGANIC MATERIALS Co Ltd
Original Assignee
FOSHAN SANSHUI JINYING INORGANIC MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by FOSHAN SANSHUI JINYING INORGANIC MATERIALS Co Ltd filed Critical FOSHAN SANSHUI JINYING INORGANIC MATERIALS Co Ltd
Priority to CN2012100687081A priority Critical patent/CN102584339A/zh
Publication of CN102584339A publication Critical patent/CN102584339A/zh
Pending legal-status Critical Current

Abstract

一种以赤泥为原材料的棕色陶瓷色料的制备方法，属于无机化工技术领域。本发明在分析赤泥化学成分的基础上，研制了以赤泥为原材料制备棕色陶瓷色料的最佳配方，按配方以赤泥为原材料配以其它化工原料，球磨均匀，高温煅烧，冷却后粉碎，得棕色陶瓷色料。喷釉试验表明，制得的棕色陶瓷色料发色效果良好，可大大降低陶瓷色料生产成本，因而可用于陶瓷色料的制备生产。

Description

一种以赤泥为原材料的棕色陶瓷色料的制备方法
技术领域
本发明涉及一种以赤泥为原材料的棕色陶瓷色料的制备方法，属于无机化工技术领域。
背景技术
陶瓷色料是陶瓷制品不可缺少的极其重要的装饰材料。随着人们生活质量的提高和居住环境的美化，建筑卫生陶瓷制品已进入千家万户。因此，陶瓷色料的稳定性和色调的多样性，已成为陶瓷色料厂追求的目标。特别是，随着对废弃资源回收再用的重视，以价格低廉的废弃资源为原材料研究开发出高品质的陶瓷色料以降低生产成本已成为陶瓷色料生产厂家研究开发的重点。
赤泥是铝土矿经各种物理和化学处理，制取三氧化二铝后所剩的红褐色粉泥状强碱性固体废料，每吨三氧化二铝产出约在0.8～1.5t，目前，国内赤泥年排放量超过3000万t。据报道，赤泥已在多方面得到了运用，比如利用赤泥生产普通硅酸盐水泥，生产硅钙肥，生产硅酸钙绝热材料，生产建筑材料，生产燃煤脱硫剂，生产PVC塑料填料等，以及从赤泥中回收有效成分(刘福刚.赤泥综合利用技术应用回顾和展望.《化学工程师》.2011年，第6期，45-46，59页)。但未见利用赤泥制备陶瓷色料的相关专利和报道。
我们对赤泥化学成分分析表明，赤泥中三氧化二铁和氧化铝含量很高，可用于制备陶瓷色料。
发明内容
本发明的目的在于以廉价的废弃资源赤泥为原材料制备发色效果良好的棕色陶瓷色料。
本发明为了达到上述目的而采用的技术解决方案如下：
首先对赤泥化学成分进行分析，然后除去水、二氧化碳及易挥发物质，按比例配以其它化工原料，经高温煅烧，冷却后粉碎，制得棕色陶瓷色料。
本发明的试验证明，赤泥与其它化工原料组成新的配方，经高温煅烧后，可制得品质良好的棕色陶瓷色料。
下面结合实施例对本发明做进一步说明。
具体实施方式
1.赤泥化学成分分析
原材料：赤泥(山某铝厂得到的直接排放固体废料)。
赤泥经风干后，通过多元素快速分析仪测定其化学成分，结果见表1。
表1赤泥的化学成分分析结果
Figure BSA00000684983900011
化学成分分析表明，该赤泥样品含有三氧化二铁高达29.84％，氧化铝高达20.96％，可用于制备陶瓷色料。
2.以赤泥为原材料的棕色陶瓷色料配方
研究了以上述赤泥样品为原材料，除去水、二氧化碳及易挥发物质后，配以其它化工原料，经高温煅烧，冷却后粉碎，制得品质良好的棕色陶瓷色料的最佳化工配方，配方见表2。
表2以赤泥为原材料的棕色陶瓷色料配方
Figure BSA00000684983900021
注：针对化学成分含量不同的赤泥样品，需要调整表格中化工原料的比例。
3.以赤泥为原材料的棕色陶瓷色料制备方法
取上述除去水、二氧化碳及易挥发物质后的赤泥样品，球磨，过筛，按表2配方比例配以表2中的其它化工原料，球磨均匀，盛放于耐火匣中，放入电炉中程序升温至1250℃，保温1小时，冷却后球磨粉碎，制得棕色陶瓷色料。
4.以赤泥为原材料制得的棕色陶瓷色料的喷釉试验
取上述制得的棕色陶瓷色料，按2％与坯泥(1175A)混合，另加0.4％三聚磷酸钠，放入球磨机中加少量水使其充分混合后，喷釉，经1065℃～1085℃烧成。结果见表3。
表3喷釉的色度数据
Figure BSA00000684983900022
试验结果表明，以赤泥为原材料制得的棕色陶瓷色料发色效果良好，可大大降低棕色陶瓷色料的生产成本，因而可应用于棕色陶瓷色料的制备生产。

Claims (1)

1.一种以赤泥为原材料的棕色陶瓷色料的制备方法，其特征是首先对赤泥的化学成分进行分析，然后研制出以除去水、二氧化碳和易挥发性物质的赤泥为原材料配以氧化铬、铁红、氢氧化铝或氧化铝、氧化锌等化工原料制备棕色陶瓷色料的最佳化工配方，最后按配方比例以除去水、二氧化碳和易挥发性物质的赤泥为原材料配以氧化铬、铁红、氢氧化铝或氧化铝、氧化锌等化工原料，球磨均匀，盛放于耐火匣中，放入电炉中程序升温至1250℃，保温1小时，冷却后粉碎，得棕色陶瓷色料。
CN2012100687081A 2012-03-12 2012-03-12 一种以赤泥为原材料的棕色陶瓷色料的制备方法 Pending CN102584339A (zh)