CN102815887A - Lightweight sound-absorbing environment-friendly interior wall paint - Google Patents
Lightweight sound-absorbing environment-friendly interior wall paint Download PDFInfo
- Publication number
- CN102815887A CN102815887A CN2012102839341A CN201210283934A CN102815887A CN 102815887 A CN102815887 A CN 102815887A CN 2012102839341 A CN2012102839341 A CN 2012102839341A CN 201210283934 A CN201210283934 A CN 201210283934A CN 102815887 A CN102815887 A CN 102815887A
- Authority
- CN
- China
- Prior art keywords
- interior wall
- emulsion
- paint
- environment
- light
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a lightweight sound-absorbing environment-friendly interior wall paint. According to the invention, an emulsion is adopted as an adhesive, lightweight perlite is adopted as a main aggregate, and the novel environment-friendly interior wall paint is prepared. A coating prepared with the paint has good sound-absorbing function. The paint comprises the components of: water, the emulsion, titanium dioxide, lightweight perlite, a surfactant, an antiseptic, a film-forming additive, and a thickening agent. The interior wall paint prepared with the lightweight perlite and the other components has the advantages that: the coating has a porous characteristic, such that a sound-absorbing quantification effect can be achieved through the controlling over the thickness of the coating; compared with a perlite decorative board material, the paint can perfectly merge with a coated base material, such that a seamless decorative plane is formed; the color can be adjusted according to requirements, such that a better decorative function is provided. The paint can be used for creating a quiet, beautiful and comfortable environment. The paint can be widely applied in hospitals, hotels, theaters, conference halls and home decorations.
Description
Technical field
The present invention relates to a kind of interior wall coating, particularly a kind of novel light sound-absorbing environment protection interior wall coating that adopts light pearl stone as main aggregate.
Background technology
Along with the development of society, our city of life is more and more crowded, and the noise in the environment is increasing, has a strong impact on the common people's physical and mental health, and reality presses for to the mankind provide peace and quiet, comfortable environment improves the place of having a rest and working.General interior wall coating does not have sound absorption function, can not be with helping solve noise problem.
Summary of the invention
The object of the invention provides the dope for inner wall of architecture of the certain technology construction of a kind of process, and has certain sound absorption function.
The present invention adopts following technical formula and technology to realize above-mentioned purpose, and a kind of emulsion that adopts is that sticker, light pearl stone are the interior wall coating of main aggregate, and its concrete composition and proportioning be (mass ratio) as follows:
The constituent mass proportioning
1. water 25 ~ 30
2. tensio-active agent 0.5 ~ 1.5
3. anticorrosion and bactericidal agent 0.1 ~ 0.3
4. white titanium pigment 10 ~ 15
5. film coalescence aid 2 ~ 5
6. thickener soln 12 ~ 15
7. emulsion 25 ~ 35
8. light pearl stone 8 ~ 12
Wherein said thickener soln preferably adopts the 3.2% hydroxyethylmethyl-cellulose aqueous solution.
Said emulsion preferably adopts benzene emulsion, acrylate and vinyl acetate emulsion, vinegar uncle emulsion or the vinyl acetate-ethylene copolymerization emulsions that contains admittedly for 40%-60%.
Said light pearl stone preferably adopts granularity to do
0.15-0.3The open pass pearlstone of mm.
Its preparation method is: water, tensio-active agent, anticorrosion and bactericidal agent are added in the container; Stirrer stirring at low speed (about 500 rev/mins); Slowly add white titanium pigment, improved stirring velocity high speed dispersion (about 1200 rev/mins) 20-30 minute, turn down stirrer speed then to 300-600 rev/min; Progressively slowly add film coalescence aid, thickener soln, emulsion, light pearl stone, disperseed 15-20 minute.
The invention has the advantages that:
1, has sound absorption function;
2, easily construction can blade coating, spraying;
3, texture is abundant, and good decorative property can be mixed colours;
4, heat insulation good, the moisture absorption, antisweat.
Embodiment
It is that sticker, light pearl stone are that main aggregate is formulated that the present invention adopts emulsion.
Its concrete composition and proportioning be (mass ratio) as follows:
The constituent mass proportioning
1. water 25 ~ 30
2. tensio-active agent 0.5 ~ 1.5
3. anticorrosion and bactericidal agent 0.1 ~ 0.3
4. white titanium pigment 10 ~ 15
5. film coalescence aid 2 ~ 5
6. thickener soln 12 ~ 15
7. emulsion 25 ~ 35
8. light pearl stone 8 ~ 12
Wherein:
Thickener soln adopts the 3.2% hydroxyethylmethyl-cellulose aqueous solution.
Emulsion adopts and contains benzene emulsion, acrylate and vinyl acetate emulsion, vinegar uncle emulsion or the vinyl acetate-ethylene copolymerization emulsions for 40%-60% admittedly.
Light pearl stone adopts granularity to do
0.15-0.3The open pass pearlstone of mm.
This light silencing environment-friendly interior wall coating preparation method is:
Water, tensio-active agent, anticorrosion and bactericidal agent are added in the container; Stirrer stirring at low speed (about 500 rev/mins); Slowly add white titanium pigment, improved stirring velocity high speed dispersion (about 1200 rev/mins) 20-30 minute, turn down stirrer speed then to 300-600 rev/min; Progressively slowly add film coalescence aid, thickener soln, emulsion, light pearl stone, disperseed 15-20 minute.
The light silencing environment-friendly interior wall coating that goes out according to said ratio and explained hereafter is constructed on the interior wall by certain thickness (like 10mm), compares with common coating, has the good sound absorption effect, cooperates other sound-absorbing measure, and effect is better.
Embodiment one:
The constituent mass proportioning
1. water 25
2. tensio-active agent 0.5
3. anticorrosion and bactericidal agent 0.1
4. white titanium pigment 15
5. film coalescence aid 2
6. thickener soln 15
7. emulsion 34.4
8. light pearl stone 8
This light silencing environment-friendly interior wall coating preparation method is:
Water, tensio-active agent, anticorrosion and bactericidal agent are added in the container; Stirrer stirring at low speed (about 500 rev/mins); Slowly add white titanium pigment, improved stirring velocity high speed dispersion (about 1200 rev/mins) 20-30 minute, turn down stirrer speed then to 300-600 rev/min; Progressively slowly add film coalescence aid, thickener soln, emulsion, light pearl stone, disperseed 15-20 minute.
Embodiment two:
The constituent mass proportioning
1. water 30
2. tensio-active agent 1.5
3. anticorrosion and bactericidal agent 0.3
4. white titanium pigment 15
5. film coalescence aid 2
6. thickener soln 14.2
7. emulsion 25
8. light pearl stone 12
This light silencing environment-friendly interior wall coating preparation method is:
Water, tensio-active agent, anticorrosion and bactericidal agent are added in the container; Stirrer stirring at low speed (about 500 rev/mins); Slowly add white titanium pigment, improved stirring velocity high speed dispersion (about 1200 rev/mins) 20-30 minute, turn down stirrer speed then to 300-600 rev/min; Progressively slowly add film coalescence aid, thickener soln, emulsion, light pearl stone, disperseed 15-20 minute.
Embodiment three:
The constituent mass proportioning
1. water 26
2. tensio-active agent 1
3. anticorrosion and bactericidal agent 0.2
4. white titanium pigment 10
5. film coalescence aid 5
6. thickener soln 12.8
7. emulsion 34
8. light pearl stone 11
This light silencing environment-friendly interior wall coating preparation method is:
Water, tensio-active agent, anticorrosion and bactericidal agent are added in the container; Stirrer stirring at low speed (about 500 rev/mins); Slowly add white titanium pigment, improved stirring velocity high speed dispersion (about 1200 rev/mins) 20-30 minute, turn down stirrer speed then to 300-600 rev/min; Progressively slowly add film coalescence aid, thickener soln, emulsion, light pearl stone, disperseed 15-20 minute.
A preferred embodiment of the present invention:
The constituent mass proportioning
1. water 28
2. tensio-active agent 1.2
3. anticorrosion and bactericidal agent 0.2
4. white titanium pigment 13
5. film coalescence aid 4
6. thickener soln 13
7. emulsion 31.6
8. light pearl stone 9
This light silencing environment-friendly interior wall coating preparation method is:
Water, tensio-active agent, anticorrosion and bactericidal agent are added in the container; Stirrer stirring at low speed (about 500 rev/mins); Slowly add white titanium pigment, improved stirring velocity high speed dispersion (about 1200 rev/mins) 20-30 minute, turn down stirrer speed then to 300-600 rev/min; Progressively slowly add film coalescence aid, thickener soln, emulsion, light pearl stone, disperseed 15-20 minute.
Claims (5)
1. light silencing environment-friendly interior wall coating is characterized in that: be sticker, light pearl stone are main aggregate with the emulsion, and formulated novel environment friendly interior wall coating, it is following that its concrete composition and proportioning are pressed mass ratio:
The constituent mass proportioning
1. water 25 ~ 30
2. tensio-active agent 0.5 ~ 1.5
3. anticorrosion and bactericidal agent 0.1 ~ 0.3
4. white titanium pigment 10 ~ 15
5. film coalescence aid 2 ~ 5
6. thickener soln 12 ~ 15
7. emulsion 25 ~ 35
8. light pearl stone 8 ~ 12.
2. light silencing environment-friendly interior wall coating as claimed in claim 1 is characterized in that: said thickener soln preferably adopts the 3.2% hydroxyethylmethyl-cellulose aqueous solution.
3. light silencing environment-friendly interior wall coating as claimed in claim 1 is characterized in that: it is benzene emulsion, acrylate and vinyl acetate emulsion, vinegar uncle emulsion or the vinyl acetate-ethylene copolymerization emulsions of 40%-60% that said emulsion preferably adopts solid content.
4. light silencing environment-friendly interior wall coating as claimed in claim 1 is characterized in that: said light pearl stone preferably adopts granularity to do
0.15-0.3The open pass pearlstone of mm.
5. light silencing environment-friendly interior wall coating as claimed in claim 1; It is characterized in that: its preparation method is: water, tensio-active agent, anticorrosion and bactericidal agent are added in the container, and the stirrer stirring at low speed slowly adds white titanium pigment; Improved the stirring velocity high speed dispersion 20-30 minute; Turn down stirrer speed then to 300-600 rev/min, progressively slowly add film coalescence aid, thickener soln, emulsion, light pearl stone, disperseed 15-20 minute.