CN101649148A - Preparation of painting coating used by mineral wool board ceiling and construction technology - Google Patents
Preparation of painting coating used by mineral wool board ceiling and construction technology Download PDFInfo
- Publication number
- CN101649148A CN101649148A CN200910051278A CN200910051278A CN101649148A CN 101649148 A CN101649148 A CN 101649148A CN 200910051278 A CN200910051278 A CN 200910051278A CN 200910051278 A CN200910051278 A CN 200910051278A CN 101649148 A CN101649148 A CN 101649148A
- Authority
- CN
- China
- Prior art keywords
- painting coating
- mineral wool
- wool board
- board ceiling
- coating used
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation of painting coating used by mineral wool board ceiling and construction technology. The painting coating used by mineral wool board ceiling comprises a layer material which is a liquid material. The construction technology is as follows: testing board ceiling material, spraying the painting coating, and drying at high temperature. The invention has whiteness,beauty, luxuriousness, elegance, stereoscopic impression, strong decoration and favourable fire-proof and damp-proof characteristics, increases board ceiling material strength, prevents mildew, and also has the characteristics of long service life, yellowing resistance, low VOC, convenient construction and the like. Because the painting coating is matched with the mineral wool board ceiling, the painting coating has special stereoscopic impression, can change the visual effect of habitable room space, has the effect of lowering noise, and is suitable for the decoration of the ceiling decorative finish of various buildings.
Description
Technical field
The present invention relates to a kind of preparation and construction technology of painting coating, painting coating used by mineral wool board ceiling and the construction technology of specifically a kind of construction on mineral cotton ceiling floor.
Background technology
The indoor top surface finishing material that occurs various class in the market all is that its decorative effect is more single based on the ceiling board of aluminium, rock wool, lime carbonate or gypsum material generally.All there are some shortcomings in addition:
The ceiling board surface smoother of aluminium, cost is also higher, and is big to the light reflection, causes indoor light effects contrast big, gives people's visual effect bad;
The ceiling board light weight of rock wool material, but waterproof effect is relatively poor, and it is sagging to be easy to make moist after the time is long;
The ceiling board of lime carbonate or gypsum material, easily broken, cause construction inconvenience, and suction easily.
Through market survey, the present domestic supporting technical products of coating and mineral wool board that also do not use.
Summary of the invention
The present invention is exactly in order to address the above problem, and overcomes the problem of indoor top surface finishing material, and a kind of preparation and construction technology of painting coating used by mineral wool board ceiling is provided.This invention is applicable to that the face of indoor top surface finishing material is coated with use.Painting coating used by mineral wool board ceiling and construction technology that a kind of and mineral cotton ceiling floor that the objective of the invention is to provide at the deficiencies in the prior art is used in combination, combined decoration effect than traditional aluminium, rock wool, lime carbonate or gypsum material ceiling board is stronger, has that sound insulation and noise reduction is effective, the fire-proof and damp-proof performance is good, long service life, makes that indoor sharpness is better, premium propertiess such as more quick are decorated in construction.
The technical problem that will solve required for the present invention can be achieved through the following technical solutions:
A kind of painting coating used by mineral wool board ceiling is the single-component prescription, and main component (by weight) is:
Painting coating: synthetic emulsion 5-10 part, lime carbonate 50-60 part, kaolin 0-5 part, dispersion agent 0.4-1 part, ether of cellulose and derivative 0.1-1 part thereof, biocide mildewcide 0.1-1.0 part, defoamer 0.1-0.5 part, water 20-40 part.
Described dispersion agent is polyacrylic acid dipersant, silicate dispersion agent or condensed phosphoric acid salt dispersion agent.
Described synthetic emulsion is a kind of of pure acrylic acid emulsion, interpolymer latex of polystyrene and acrylic ester, vinegar uncle copolymer emulsion, vinegar-third copolymer emulsion, aqueous polyvinyl acetate emulsion.
Described ether of cellulose and derivative thereof are a kind of of methylcellulose gum, ethyl cellulose, Walocel MT 20.000PV, Natvosol, hydroxypropylcellulose, carboxymethyl cellulose, methylhydroxypropylcellulose class.
Described defoamer is siloxane-based defoamer, or siloxane-based defoamer is composite.
Described biocide mildewcide is organic antibacterial agent or inorganic antiseptic or adopts organic and inorganic complex antimicrobials.
Described inorganic antiseptic is the slow release type or the nano titanium oxide of silver, zinc, cupric ion.
A kind of construction technology of painting coating used by mineral wool board ceiling is characterized in that, it comprises following operation: sheet material test → spraying painting coating → hyperthermia drying.
Described spraying painting coating step adopts high-pressure spray gun evenly to be sprayed in the basic unit.
Described hyperthermia drying step is to dry through 100-300 ℃ of high temperature oven in second at 3-10, coating is at high temperature solidified rapidly form.
Owing to adopted technique scheme, the present invention has pure white attractive in appearance, elegant luxurious, match volume, ornamental strong, reach good fire-proof and damp-proof, strengthen timber intensity, mildew-resistant, also have characteristics such as long service life, anti-xanthochromia, low VOC, easy construction simultaneously.
Because of itself and the supporting use of mineral cotton ceiling floor, have unique match volume, can change the visual effect of room space but also have the effect that reduces noise.It is applicable to the decoration of various top-grade building thing furred ceiling facings.
Embodiment
In order to make technique means of the present invention, creation characteristic, to reach purpose and effect is easy to understand,, further set forth the present invention below in conjunction with specific embodiment.
Embodiment 1:
Painting coating: get 10 parts of synthetic emulsions, 50 parts in lime carbonate, 5 parts of kaolin, 0.4 part of dispersion agent, 0.3 part in ether of cellulose and derivative thereof, 0.1 part of biocide mildewcide, 0.2 part of defoamer, 34 parts in water; Water is injected reactor, added condensed phosphoric acid dipersant high speed dispersion 5 minutes, added the Walocel MT 20.000PV high speed dispersion 5 minutes, added lime carbonate and kaolin high speed dispersion 35 minutes, add aqueous polyvinyl acetate emulsion and stirred at a slow speed 10 minutes, add biocide mildewcide and stirred at a slow speed 5 minutes, add defoamer and stirred at a slow speed 5 minutes, stop to stir, obtain the finishing coat material.
Construction technology of the present invention is: sheet material test → spraying face is coated with → hyperthermia drying.
Concrete construction technological process:
1, sheet material test:
(1) sheet material must clean drying, can not contain stain, greasy dirt, floating ash etc.
(2) performances such as the water ratio of sheet material, intensity are tested, reach certain standard and enter operational procedure again.
2, spraying painting coating:
Utilize high-pressure spray gun, painting coating evenly is sprayed on the sheet material front.
3, hyperthermia drying:
Through drying through 100-300 ℃ of high temperature oven in second at 3-10, mineral wool sheet material is carried out smooth sealing, strengthen the intensity of sheet material.
Embodiment 2:
Painting coating: get 5 parts of synthetic emulsions, 55 parts in lime carbonate, 1 part of kaolin, 0.4 part of dispersion agent, 0.3 part in ether of cellulose and derivative thereof, 0.1 part of biocide mildewcide, defoamer 0.1 minute, 38 parts in water; Water is injected reactor, added condensed phosphoric acid dipersant high speed dispersion 5 minutes, added the Walocel MT 20.000PV high speed dispersion 5 minutes, added lime carbonate and kaolin high speed dispersion 35 minutes, add aqueous polyvinyl acetate emulsion and stirred at a slow speed 10 minutes, add biocide mildewcide and stirred at a slow speed 5 minutes, add defoamer and stirred at a slow speed 5 minutes, stop to stir, obtain the finishing coat material.
Concrete construction technological process:
1, sheet material test:
(1) sheet material must clean drying, can not contain stain, greasy dirt, floating ash etc.
(2) performances such as the water ratio of sheet material, intensity are tested, reach certain standard and enter operational procedure again.
2, spraying painting coating:
Utilize high-pressure spray gun, painting coating evenly is sprayed on the sheet material front.
3, hyperthermia drying:
Through drying through 100-300 ℃ of high temperature oven in second at 3-10, mineral wool sheet material is carried out smooth sealing, strengthen the intensity of sheet material.
Embodiment 3:
Painting coating: get 10 parts of synthetic emulsions, 60 parts in lime carbonate, 0 part of kaolin, 0.4 part of dispersion agent, 0.3 part in ether of cellulose and derivative thereof, 0.1 part of biocide mildewcide, 0.2 part of defoamer, 28 parts in water; Water is injected reactor, added condensed phosphoric acid dipersant high speed dispersion 5 minutes, added the Walocel MT 20.000PV high speed dispersion 5 minutes, added lime carbonate and kaolin high speed dispersion 35 minutes, add aqueous polyvinyl acetate emulsion and stirred at a slow speed 10 minutes, add biocide mildewcide and stirred at a slow speed 5 minutes, add defoamer and stirred at a slow speed 5 minutes, stop to stir, obtain the finishing coat material.
Concrete construction technological process:
1, sheet material test:
(1) sheet material must clean drying, can not contain stain, greasy dirt, floating ash etc.
(2) performances such as the water ratio of sheet material, intensity are tested, reach certain standard and enter operational procedure again.
2, spraying painting coating:
Utilize high-pressure spray gun, painting coating evenly is sprayed on the sheet material front.
3, hyperthermia drying:
Through drying through 100-300 ℃ of high temperature oven in second at 3-10, mineral wool sheet material is carried out smooth sealing, strengthen the intensity of sheet material.
Pure white luxurious, the match volume attractive in appearance, elegant of decorative effect tool of the present invention, ornamental obvious characteristic such as strong are decorated with traditional ceiling board and to be compared, and are quantum jumps of ceiling decoration.
More than show and described ultimate principle of the present invention, principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; that describes in the foregoing description and the specification sheets just illustrates principle of the present invention; the present invention also has various changes and modifications without departing from the spirit and scope of the present invention, and these changes and improvements all fall in the claimed scope of the invention.The claimed scope of the present invention is defined by appending claims and equivalent thereof.
Claims (10)
1, a kind of painting coating used by mineral wool board ceiling is the single-component prescription, and main component (by weight) is:
Painting coating: synthetic emulsion 5-10 part, lime carbonate 50-60 part, kaolin 0-5 part, dispersion agent 0.4-1 part, ether of cellulose and derivative 0.1-1 part thereof, biocide mildewcide 0.1-1.0 part, defoamer 0.1-0.5 part, water 20-30 part.
2, painting coating used by mineral wool board ceiling according to claim 1 is characterized in that, described dispersion agent is polyacrylic acid dipersant, silicate dispersion agent or condensed phosphoric acid salt dispersion agent.
3, painting coating used by mineral wool board ceiling according to claim 1, it is characterized in that described synthetic emulsion is a kind of of pure acrylic acid emulsion, interpolymer latex of polystyrene and acrylic ester, vinegar uncle copolymer emulsion, vinegar-third copolymer emulsion, aqueous polyvinyl acetate emulsion.
4, painting coating used by mineral wool board ceiling according to claim 1, it is characterized in that described ether of cellulose and derivative thereof are a kind of of methylcellulose gum, ethyl cellulose, Walocel MT 20.000PV, Natvosol, hydroxypropylcellulose, carboxymethyl cellulose, methylhydroxypropylcellulose class.
5, painting coating used by mineral wool board ceiling according to claim 1 is characterized in that, described defoamer is siloxane-based defoamer, or siloxane-based defoamer is composite.
6, painting coating used by mineral wool board ceiling according to claim 1 is characterized in that, described biocide mildewcide is organic antibacterial agent or inorganic antiseptic or adopts organic and inorganic complex antimicrobials.
7, painting coating used by mineral wool board ceiling according to claim 6 is characterized in that, described inorganic antiseptic is the slow release type or the nano titanium oxide of silver, zinc, cupric ion.
8, the construction technology of the described painting coating used by mineral wool board ceiling of a kind of claim 1 is characterized in that, comprises following operation: sheet material test → spraying painting coating → hyperthermia drying.
9, construction technology according to claim 8 is characterized in that, described spraying painting coating step adopts high-pressure spray gun evenly to be sprayed in the basic unit.
10, construction technology according to claim 8 is characterized in that, described hyperthermia drying step is to dry through 100-300 ℃ of high temperature oven in second at 3-10, coating is at high temperature solidified rapidly form.