CN103525144B - A kind of high-temperature burning sticking preventing coating - Google Patents
A kind of high-temperature burning sticking preventing coating Download PDFInfo
- Publication number
- CN103525144B CN103525144B CN201310419062.1A CN201310419062A CN103525144B CN 103525144 B CN103525144 B CN 103525144B CN 201310419062 A CN201310419062 A CN 201310419062A CN 103525144 B CN103525144 B CN 103525144B
- Authority
- CN
- China
- Prior art keywords
- add
- raw material
- preventing coating
- adhesive aid
- sticking preventing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of high-temperature burning sticking preventing coating, it is made up of the raw material of following weight parts: organosilicon crylic acid latex 10-15, molybdenumdisulphide 1-2, ultra-fine barium sulfate 3-5, antimonous oxide 1-2, ceric fluoride 0.1-0.2, aluminum oxide 4-6, magnesium hydroxide 2-3, potassium pyrophosphate 0.1-0.2, Calucium Silicate powder 4-5, ethyl propenoate 2-3, adhesive aid 5-8, deionized water 40-60; Dope layer of the present invention has good cohesive force to metal substrate, weather resisteant, excellent burn-out-proof glue function and protection function, and coating at room temperature can quick self-drying, uses easy to operate.
Description
Technical field
The present invention relates generally to a kind of coating, particularly relates to a kind of high-temperature burning sticking preventing coating.
Background technology
Coating should have anticorrosion, waterproof, grease proofing, chemicals-resistant, fast light, heatproof etc., and object is exposed among air, is subject to the erosion of oxygen, moisture etc., causes the breakoff phenomenons such as corrosion of metal, foxy, cement weathering.Be coated with coating at article surface, form layer protecting film, can stop or postpone generation and the development of these breakoff phenomenons, the work-ing life of various material is extended.So provide protection is a Main Function of coating, improve the provide protection of traditional coating, the quality of coating could be improved further.
Summary of the invention
The object of the invention is exactly to provide a kind of high-temperature burning sticking preventing coating.
The present invention is achieved by the following technical solutions:
A kind of high-temperature burning sticking preventing coating, it is made up of the raw material of following weight parts:
Organosilicon crylic acid latex 10-15, molybdenumdisulphide 1-2, ultra-fine barium sulfate 3-5, antimonous oxide 1-2, ceric fluoride 0.1-0.2, aluminum oxide 4-6, magnesium hydroxide 2-3, potassium pyrophosphate 0.1-0.2, Calucium Silicate powder 4-5, ethyl propenoate 2-3, adhesive aid 5-8, deionized water 40-60;
Described adhesive aid is made up of the raw material of following weight parts:
Benzene emulsion 60-70, tragacanth gum 6-8, Zinc Pyrithione 1-2, sodium silicoaluminate 4-6, butyl polyacrylate 1-2, Natvosol 2-4,2,6 ditertiary butyl p cresol 0.1-0.3, water are appropriate;
The 10-20% of above-mentioned weight tragacanth gum is joined in 10-15 times of water, add Natvosol and 2,6 ditertiary butyl p cresol, dispersed with stirring 10-15 minute under the speed of 400-600 rev/min, raised temperature is 60-80 DEG C, add Zinc Pyrithione, sodium silicoaluminate, butyl polyacrylate, fully after mixing, add each raw material of residue, the steam heating of 80-100 DEG C is crossed after stirring, the system solid content of making is 60-65%, is cooled to normal temperature, obtains described adhesive aid.
A preparation method for high-temperature burning sticking preventing coating, comprises the following steps:
By above-mentioned molybdenumdisulphide, ultra-fine barium sulfate, antimonous oxide, ceric fluoride, aluminum oxide, magnesium hydroxide, potassium pyrophosphate, Calucium Silicate powder, ethyl propenoate mixing, put into ball grinder, add the 40-50% of above-mentioned weight deionized water, abundant grinding, adds adhesive aid, insulated and stirred 1-2 hour at 60-80 DEG C, cooling, add each raw material of residue, stir, obtain described high-temperature burning sticking preventing coating.
Advantage of the present invention is:
Dope layer of the present invention has good cohesive force to metal substrate, weather resisteant, excellent burn-out-proof glue function and protection function, and coating at room temperature can quick self-drying, uses easy to operate.
Embodiment
Embodiment 1
A kind of high-temperature burning sticking preventing coating, it is made up of the raw material of following weight parts (kilogram):
Organosilicon crylic acid latex 15, molybdenumdisulphide 1, ultra-fine barium sulfate 5, antimonous oxide 2, ceric fluoride 0.2, aluminum oxide 4, magnesium hydroxide 2, potassium pyrophosphate 0.2, Calucium Silicate powder 5, ethyl propenoate 3, adhesive aid 8, deionized water 60;
Described adhesive aid is made up of the raw material of following weight parts:
Benzene emulsion 70, tragacanth gum 8, Zinc Pyrithione 1, sodium silicoaluminate 6, butyl polyacrylate 1, Natvosol 4,2,6 ditertiary butyl p cresol 0.3, water are appropriate;
Join 20% of above-mentioned weight tragacanth gum in 15 times of water, add Natvosol and 2,6 ditertiary butyl p cresol, dispersed with stirring 15 minutes under the speed of 600 revs/min, raised temperature is 80 DEG C, add Zinc Pyrithione, sodium silicoaluminate, butyl polyacrylate, fully after mixing, add each raw material of residue, the steam heating of 100 DEG C is crossed after stirring, the system solid content of making is 65%, is cooled to normal temperature, obtains described adhesive aid.
A preparation method for high-temperature burning sticking preventing coating, comprises the following steps:
By above-mentioned molybdenumdisulphide, ultra-fine barium sulfate, antimonous oxide, ceric fluoride, aluminum oxide, magnesium hydroxide, potassium pyrophosphate, Calucium Silicate powder, ethyl propenoate mixing, put into ball grinder, add 50% of above-mentioned weight deionized water, abundant grinding, adds adhesive aid, insulated and stirred 2 hours at 80 DEG C, cooling, add each raw material of residue, stir, obtain described high-temperature burning sticking preventing coating.
Performance test:
Coating adhesion 1 grade;
Stability in storage: 1 year.
Claims (2)
1. a high-temperature burning sticking preventing coating, is characterized in that what it was made up of the raw material of following weight parts:
Organosilicon crylic acid latex 10-15, molybdenumdisulphide 1-2, ultra-fine barium sulfate 3-5, antimonous oxide 1-2, ceric fluoride 0.1-0.2, aluminum oxide 4-6, magnesium hydroxide 2-3, potassium pyrophosphate 0.1-0.2, Calucium Silicate powder 4-5, ethyl propenoate 2-3, adhesive aid 5-8, deionized water 40-60;
Described adhesive aid is made up of the raw material of following weight parts:
Benzene emulsion 60-70, tragacanth gum 6-8, Zinc Pyrithione 1-2, sodium silicoaluminate 4-6, butyl polyacrylate 1-2, Natvosol 2-4,2,6 ditertiary butyl p cresol 0.1-0.3, water are appropriate;
The 10-20% of above-mentioned weight tragacanth gum is joined in 10-15 times of water, add Natvosol and 2,6 ditertiary butyl p cresol, dispersed with stirring 10-15 minute under the speed of 400-600 rev/min, raised temperature is 60-80 DEG C, add Zinc Pyrithione, sodium silicoaluminate, butyl polyacrylate, fully after mixing, add each raw material of residue, the steam heating of 80-100 DEG C is crossed after stirring, the system solid content of making is 60-65%, is cooled to normal temperature, obtains described adhesive aid.
2. a preparation method for high-temperature burning sticking preventing coating as claimed in claim 1, is characterized in that comprising the following steps:
By above-mentioned molybdenumdisulphide, ultra-fine barium sulfate, antimonous oxide, ceric fluoride, aluminum oxide, magnesium hydroxide, potassium pyrophosphate, Calucium Silicate powder, ethyl propenoate mixing, put into ball grinder, add the 40-50% of above-mentioned weight deionized water, abundant grinding, adds adhesive aid, insulated and stirred 1-2 hour at 60-80 DEG C, cooling, add each raw material of residue, stir, obtain described high-temperature burning sticking preventing coating.