CN102806314A - 一种铝合金薄壁细孔铸件的铸造方法 - Google Patents
一种铝合金薄壁细孔铸件的铸造方法 Download PDFInfo
- Publication number
- CN102806314A CN102806314A CN2012103220428A CN201210322042A CN102806314A CN 102806314 A CN102806314 A CN 102806314A CN 2012103220428 A CN2012103220428 A CN 2012103220428A CN 201210322042 A CN201210322042 A CN 201210322042A CN 102806314 A CN102806314 A CN 102806314A
- Authority
- CN
- China
- Prior art keywords
- casting
- thin
- ceramic core
- hole
- wax
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种铝合金薄壁细孔铸件的铸造方法,主要包括陶瓷型芯制作、蜡模压制、制壳、浇注、清壳步骤,蜡模压制成型后,在薄壁细孔处增加刷蜡2mm-5mm厚,铸件浇注后采用高压水力清砂清理陶瓷型芯,陶瓷芯清除后采用打磨方法将铸件薄壁细孔处多余的材料打磨掉,本发明在铸造过程中增加薄壁细孔处的壁厚,避免了去除陶瓷芯过程中铸件薄壁细孔被打裂的现象。
Description
技术领域
本发明属于熔模铸造技术领域,特别涉及一种铝合金薄壁孔铸件的铸造方法。
背景技术
铝合金熔模铸件多用于航空件。结构千变万化,针对深孔、窄槽的铸造工艺难度很大,针对铝合金薄壁细孔(孔径≤5mm,壁厚≤3mm)铸造无法直接采用涂料涂挂进行铸造。通常采用预先埋管进行铸造。管材有铜管、不锈钢管及石英玻璃管。使用以上预埋管容易出现变形、不锈钢管不易取出等困难。采用陶瓷芯时,在清理陶瓷芯易将铸件的薄壁细孔打裂。
发明内容
为解决现有技术中存在的问题,本发明提供了一种铝合金薄壁孔铸件的铸造方法,避免了去除陶瓷芯过程中铸件薄壁细孔被打裂的现象。
本发明的技术方案如下所述:
一种铝合金薄壁细孔铸件的铸造方法,主要包括陶瓷型芯制作、蜡模压制、制壳、浇注、清壳步骤,蜡模压制成型后,在薄壁细孔处增加刷蜡2mm-5mm厚,铸件浇注后采用高压水力清砂清理陶瓷型芯,陶瓷芯清除后采用打磨方法将铸件薄壁细孔处多余的材料打磨掉。
本发明的有益效果是:在铸造过程中增加薄壁细孔处的壁厚,避免了去除陶瓷芯过程中铸件薄壁细孔被打裂的现象。
附图说明
图1是本发明铸件示意图
具体实施方式
下面结合附图,对本发明作进一步详细说明:
一种铝合金薄壁细孔铸件的铸造方法,主要包括陶瓷型芯制作、蜡模压制、制壳、浇注、清壳步骤,蜡模压制成型后,在薄壁细孔2处增加刷蜡2mm-5mm,铸件1浇注后采用高压水力清砂清理陶瓷型芯,陶瓷芯清除后采用打磨方法将铸件1薄壁细孔处多余的材料3打磨掉。
Claims (1)
1.一种铝合金薄壁细孔铸件的铸造方法,主要包括陶瓷型芯制作、蜡模压制、制壳、浇注、清壳步骤,其特征在于:蜡模压制成型后,在薄壁细孔(2)处增加刷蜡2mm-5mm,铸件(1)浇注后采用高压水力清砂清理陶瓷型芯,陶瓷芯清除后采用打磨方法将铸件(1)薄壁细孔处多余的材料(3)打磨掉。