CN102798638A - 电解铜箔渗透点和针孔的检测方法 - Google Patents
电解铜箔渗透点和针孔的检测方法 Download PDFInfo
- Publication number
- CN102798638A CN102798638A CN2011101359338A CN201110135933A CN102798638A CN 102798638 A CN102798638 A CN 102798638A CN 2011101359338 A CN2011101359338 A CN 2011101359338A CN 201110135933 A CN201110135933 A CN 201110135933A CN 102798638 A CN102798638 A CN 102798638A
- Authority
- CN
- China
- Prior art keywords
- copper foil
- sample
- pin hole
- electrolytic copper
- tank
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及电解铜箔工艺，公开了一种电解铜箔渗透点和针孔的检测方法，包括如下步骤：(1)、样品处理：选择一宽广的水槽为检测水槽，将待测铜箔修剪成无褶皱和折痕的样品，要求样品的大小为能平放入检测水槽中；(2)、调制渗透液：将染料按0.5g/L～5g/L的浓度溶解在酒精中，并将其充入检测水槽中；(3)、粗检：取样品光面朝下放入充有渗透液的检测水槽中，放置0.5分钟至2分钟的时间，观察渗透毛面的色点判断渗透点和针孔的数量和位置；(4)、尺寸测量：用不小于1000倍电子显微镜在色点的相应位置进一步放大检测，并测量针孔的尺寸。本发明具有操作简单且易于判断的特点，本发明使用的酒精具有较强的挥发性，不会对铜箔造成污染，不会影响样品的回收再利用。
Description
技术领域
本发明涉及电解铜箔工艺，尤其是涉及一种操作简单、易于判断且不影响到样品的回收利用的电解铜箔渗透点和针孔的检测方法。
背景技术
针孔和渗透点为影响铜箔性能的重要因素；所谓针孔，就是铜箔在暗室中透光检查结果时，有直径小于1毫米的零星的微小透光孔；渗透点则是不透光但在铜箔的一面用渗透剂染色，在反面出现染色剂斑点的现象。简单的讲，针孔为直孔，渗透点是曲孔。对于PCB用电解铜箔，针孔和渗透点过去一直是电解铜箔厂家深感头疼的问题。有关铜箔孔隙产生原因及孔隙程度是电解铜箔生产技术中一个重要的参数，尤其对于厚度小于18微米的电解铜箔，产生空隙频率更高。针孔和渗透点在覆铜板压合过程中，融化的树脂会从铜箔孔隙中流出，在铜箔表面形成树脂点，影响覆铜板质量。
目前铜箔制造厂在生产线上只能用精密仪器监测约15微米以上的针孔，对于小于15微米的针孔和所有的渗透点，只能采用水渗透检测法或者采用煤油渗透检测法，但是水渗透的效果并不直观明显，煤油渗透性比较明显，但是煤油附着在检测样品表面会影响到样品的回收利用。
发明内容
为了克服现有技术中水渗透的效果并不直观明显，煤油渗透性检测法影响到样品的回收利用的缺点，本发明目的在于提供一种操作简单、易于判断且不影响到样品的回收利用的电解铜箔渗透点和针孔的检测方法。
本发明是通过以下技术措施实现的，一种电解铜箔渗透点和针孔的检测方法，包括如下步骤：
(1)、样品处理：选择一宽广的水槽为检测水槽，将待测铜箔修剪成无褶皱和折痕的样品，要求样品的大小为能平放入检测水槽中；
(2)、调制渗透液：将染料按0.5g/L～5g/L的浓度溶解在酒精中，并将其充入检测水槽中；
(3)、粗检：取样品光面朝下放入充有渗透液的检测水槽中，放置0.5分钟至2分钟的时间，观察渗透毛面的色点判断渗透点和针孔的数量和位置；
(4)、尺寸测量：用不小于1000倍电子显微镜在色点的相应位置进一步放大检测，并测量针孔的尺寸。
作为一种优选方式，在有必要时所述步骤(1)中还对样品进行清洗处理。
具体的，其特征在于：所述步骤(2)中染料按1g/L的浓度溶解在酒精。
具体的，所述步骤(3)中观察渗透毛面的色点的检测人员的矫正视力为2.0。
具体的，所述步骤(3)中样品在检测水槽中的放置时间如在20℃的温度条件下为1分钟。就已能得到高灵敏度的渗透效果。
本发明使用直观的方法就能检测电解铜箔渗透点和针孔，使检测结果更加直观和明了，具有操作简单且易于判断的特点，本发明使用的酒精具有较强的挥发性，不会对铜箔造成污染，不会影响样品的回收再利用。
具体实施方式
下面结合实施例对本发明作进一步详细说明。
一种电解铜箔渗透点和针孔的检测方法，包括如下步骤：
(1)、样品处理：选择130cm*50cm的水槽为检测水槽，将待测铜箔修剪成无褶皱和折痕120cm*46cm的样品；
(2)、调制渗透液：将染料按1g/L的浓度溶解在酒精中，并将其充入检测水槽中；
(3)、粗检：取样品光面朝下放入充有渗透液的检测水槽中，在20℃的温度条件放置1分钟的时间，矫正视力为2.0的检测人员观察渗透毛面的色点，判断渗透点和针孔的数量和位置；
(4)、尺寸测量：用不小于1000倍电子显微镜在色点的相应位置进一步放大检测，并测量针孔的尺寸。
以上是对本发明电解铜箔渗透点和针孔的检测方法进行了阐述，用于帮助理解本发明，但本发明的实施方式并不受上述实施例的限制，任何未背离本发明原理下所作的改变、修饰、替代、组合、简化，均应为等效的置换方式，都包含在本发明的保护范围之内。
Claims (5)
1.一种电解铜箔渗透点和针孔的检测方法，其特征在于包括如下步骤：
(1)、样品处理：选择一宽广的水槽为检测水槽，将待测铜箔修剪成无褶皱和折痕的样品，要求样品的大小为能平放入检测水槽中；
(2)、调制渗透液：将染料按0.5g/L～5g/L的浓度溶解在酒精中，并将其充入检测水槽中；
(3)、粗检：取样品光面朝下放入充有渗透液的检测水槽中，放置0.5分钟至2分钟的时间，观察渗透毛面的色点判断渗透点和针孔的数量和位置；
(4)、尺寸测量：用不小于1000倍电子显微镜在色点的相应位置进一步放大检测，并测量针孔的尺寸。
2.根据权利要求1所述的电解铜箔渗透点和针孔的检测方法，其特征在于：所述步骤(1)中还对样品进行清洗处理。
3.根据权利要求1所述的电解铜箔渗透点和针孔的检测方法，其特征在于：所述步骤(2)中染料按1g/L的浓度溶解在酒精。
4.根据权利要求1所述的电解铜箔渗透点和针孔的检测方法，其特征在于：所述步骤(3)中观察渗透毛面的色点的检测人员的矫正视力为2.0。
5.根据权利要求1所述的电解铜箔渗透点和针孔的检测方法，其特征在于：所述步骤(3)中样品在检测水槽中的放置时间如在20℃的温度条件下为1分钟。