CN102796469A - 一种封面装订热熔胶 - Google Patents
一种封面装订热熔胶 Download PDFInfo
- Publication number
- CN102796469A CN102796469A CN201210327209XA CN201210327209A CN102796469A CN 102796469 A CN102796469 A CN 102796469A CN 201210327209X A CN201210327209X A CN 201210327209XA CN 201210327209 A CN201210327209 A CN 201210327209A CN 102796469 A CN102796469 A CN 102796469A
- Authority
- CN
- China
- Prior art keywords
- parts
- melt adhesive
- hot melt
- paraffin
- front cover
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种封面装订热熔胶。以重量份计，本发明由以下物质组成：乙烯-乙酸乙烯酯共聚物：30～50，氯丁烯树脂：10～30，氢化松香：10～20，白油：10～20，石蜡：10～20，硫酸钡：3～8，轻质碳酸钙：5～8，2，6-二叔丁基对甲酚：0.1～0.3。本发明涂胶后形成的胶膜能够适应书本背面弯曲的形状，永远保持圆形，具有较高的粘结强度，固化速度快，能用于连续生产的圆形硬封面书本的装订。
Description
技术领域
本发明属于日用化学品技术领域，更具体是涉及一种封面装订热熔胶。
背景技术
封面装订在进行装订的时候，通常会使用到热熔胶，热熔胶的质量对书籍封面的装订影响很大。
通常要求热熔胶热稳定性好，抗老化能力强，否则胶老化后颜色会变浑，影响书的美观，也会影响书的粘接强度。书刊用胶具备了以上特性后，具有优良的强度，韧性及抗老化的性能，才能保证图书的胶订质量。
目前常用的热熔胶较难达到上述要求。
发明内容
本发明的目的在于克服现有技术存在的不足，提供一种封面装订热熔胶。
为达到上述目的，本发明采取了如下技术方案：
一种封面装订热熔胶，以重量份计，由以下物质组成：
乙烯-乙酸乙烯酯共聚物：30～50，氯丁烯树脂：10～30，
氢化松香：10～20，白油：10～20，石蜡：10～20，
硫酸钡：3～8，轻质碳酸钙：5～8，
2，6-二叔丁基对甲酚：0.1～0.3。
上述技术方案中，所述的封面装订热熔胶的制备工艺如下：
(1)在反应釜中先加入石蜡，升温至100～120℃，使其完全溶解后，加入其它物料，在充分搅拌下升温至160～180℃，反应2～5小时；
(2)反应结束后，趁热出料，通过模口放到冷却钢带上冷却成型。
与现有技术相比，本发明涂胶后形成的胶膜能够适应书本背面弯曲的形状，永远保持圆形，具有较高的粘结强度，固化速度快，能用于连续生产的圆形硬封面书本的装订。
具体实施方式
以下结合具体实施例来对本发明作进一步的描述。
实施例1
一种封面装订热熔胶，以重量份计，由以下物质组成：
乙烯-乙酸乙烯酯共聚物：30，氯丁烯树脂：10，
氢化松香：10，白油：10，石蜡：10，
硫酸钡：3，轻质碳酸钙：5，2，6-二叔丁基对甲酚：0.1。
上述技术方案中，所述的封面装订热熔胶的制备工艺如下：
(1)在反应釜中先加入石蜡，升温至100～120℃，使其完全溶解后，加入其它物料，在充分搅拌下升温至160～180℃，反应2～5小时；
(2)反应结束后，趁热出料，通过模口放到冷却钢带上冷却成型。
实施例2
一种封面装订热熔胶，以重量份计，由以下物质组成：
乙烯-乙酸乙烯酯共聚物：50，氯丁烯树脂：30，
氢化松香：20，白油：20，石蜡：20，
硫酸钡：8，轻质碳酸钙：8，2，6-二叔丁基对甲酚：0.3。
制备方法同实施例1。
实施例3
一种封面装订热熔胶，以重量份计，由以下物质组成：
乙烯-乙酸乙烯酯共聚物：40，氯丁烯树脂：20，
氢化松香：16，白油：16，石蜡：16，
硫酸钡：6，轻质碳酸钙：6，2，6-二叔丁基对甲酚：0.2。
制备方法同实施例1。
产品应用：使用时先将热熔胶放入胶槽中加热至140～160℃，使其成为熔融状态，然后用任何一种涂胶方法将热熔胶涂覆到书籍上，使胶液渗入到书籍的每一书页中，最后采用强制冷却的方法使热熔胶迅速固化。
Claims (4)
1.一种封面装订热熔胶，其特征在于，以重量份计，由以下物质组成：
乙烯-乙酸乙烯酯共聚物：30～50，氯丁烯树脂：10～30，
氢化松香：10～20，白油：10～20，石蜡：10～20，
硫酸钡：3～8，轻质碳酸钙：5～8，
2，6-二叔丁基对甲酚：0.1～0.3。
2.根据权利要求1所述的一种封面装订热熔胶，其特征在于，以重量份计，由以下物质组成：
乙烯-乙酸乙烯酯共聚物：30，氯丁烯树脂：10，
氢化松香：10，白油：10，石蜡：10，
硫酸钡：3，轻质碳酸钙：5，
2，6-二叔丁基对甲酚：0.1。
3.根据权利要求1所述的一种封面装订热熔胶，其特征在于，以重量份计，由以下物质组成：
乙烯-乙酸乙烯酯共聚物：50，氯丁烯树脂：30，
氢化松香：20，白油：20，石蜡：20，
硫酸钡：8，轻质碳酸钙：8，
2，6-二叔丁基对甲酚：0.3。
4.根据权利要求1所述的一种封面装订热熔胶，其特征在于，以重量份计，由以下物质组成：
乙烯-乙酸乙烯酯共聚物：40，氯丁烯树脂：20，
氢化松香：16，白油：16，石蜡：16，
硫酸钡：6，轻质碳酸钙：6，
2，6-二叔丁基对甲酚：0.2。