CN103952088B - 一种纸塑复合胶及其制备方法 - Google Patents

一种纸塑复合胶及其制备方法 Download PDF

Info

Publication number
CN103952088B
CN103952088B CN201410110405.0A CN201410110405A CN103952088B CN 103952088 B CN103952088 B CN 103952088B CN 201410110405 A CN201410110405 A CN 201410110405A CN 103952088 B CN103952088 B CN 103952088B
Authority
CN
China
Prior art keywords
parts
paper
butyl acetate
stirring reaction
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201410110405.0A
Other languages
English (en)
Other versions
CN103952088A (zh
Inventor
胡文进
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TONGLING SONGMA FOOD PACKING MACHINERY MANUFACTURING Co Ltd
Original Assignee
TONGLING SONGMA FOOD PACKING MACHINERY MANUFACTURING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TONGLING SONGMA FOOD PACKING MACHINERY MANUFACTURING Co Ltd filed Critical TONGLING SONGMA FOOD PACKING MACHINERY MANUFACTURING Co Ltd
Priority to CN201410110405.0A priority Critical patent/CN103952088B/zh
Publication of CN103952088A publication Critical patent/CN103952088A/zh
Application granted granted Critical
Publication of CN103952088B publication Critical patent/CN103952088B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种纸塑复合胶及其制备方法，其特征在于由下列重量份的原料制成：弹性聚氨酯树脂30-35、聚酯树脂12-14、萜烯树脂5-7、白油4-6、邻苯二甲酸酐8-10、壬基酚聚氧乙烯醚2-3、乙烯基三乙氧基硅烷2-3、丙酸乙烯酯12-14、丙烯腈3-5、异戊二烯4-6、醋酸丁酯24-27、儿茶酚1-2、乙酸乙酯12-14、增粘助剂4-5。本发明涂胶后形成的胶膜能够适应纸背面弯曲的形状，永远保持圆形，具有较高的粘结强度，固化速度快。

Description

一种纸塑复合胶及其制备方法
技术领域
本发明涉及一种热封胶，更具体地说，是一种纸塑复合胶及其制备方法。
背景技术
包装行业在我国规模很大，包装时，纸纸粘合、纸塑粘合、纸纸粘合、塑铁粘合，均需要用于包装胶，现有包装热封胶多存在有毒溶剂残留，粘接强度不高等问题。不能满足现在的包装无害粘接需要。
发明内容
本发明的目的是提供一种纸塑复合胶及其制备方法，粘接力强。
本发明所采用的技术方案是：
    一种纸塑复合胶，其特征在于由下列重量份的原料制成：
弹性聚氨酯树脂30-35、聚酯树脂12-14、萜烯树脂5-7、白油4-6、邻苯二甲酸酐8-10、壬基酚聚氧乙烯醚2-3、乙烯基三乙氧基硅烷2-3、丙酸乙烯酯12-14、丙烯腈3-5、异戊二烯4-6、醋酸丁酯24-27、儿茶酚1-2、乙酸乙酯12-14、增粘助剂4-5。
    所述的增粘助剂由以下重量份的原料制得：热塑性丙烯酸树脂3-4、硅烷偶联剂KH550 1-2、582-2 氨基树脂3-4、聚异丁烯2-3、、醋酸丁酯6-8、环烷酸钴0.1-0.2、双环戊二烯基铁0.4-0.6；
    制备方法是：将热塑性丙烯酸树脂、582-2 氨基树脂加入到醋酸丁酯中，然入加入硅烷偶联剂KH550，加热至90-100℃，搅拌反应30-40分钟，然后加入聚异丁烯、双环戊二烯基铁、环烷酸钴，搅拌反应20-40分钟即得。
所述的纸塑复合胶的制备方法，其特征在于包括以下步骤：
将萜烯树脂、白油、邻苯二甲酸酐、壬基酚聚氧乙烯醚、乙烯基三乙氧基硅烷、丙酸乙烯酯、丙烯腈、异戊二烯、醋酸丁酯混合，加热至75-95℃，搅拌反应1-2小时；然后加入其它成分，继续搅拌反应2-3小时即得。
    本发明涂胶后形成的胶膜能够适应纸背面弯曲的形状，永远保持圆形，具有较高的粘结强度，固化速度快。
具体实施方式
    一种纸塑复合胶，由下列重量份（公斤）的原料制成：
弹性聚氨酯树脂35、聚酯树脂14、萜烯树脂7、白油4、邻苯二甲酸酐10、壬基酚聚氧乙烯醚3、乙烯基三乙氧基硅烷3、丙酸乙烯酯12、丙烯腈5、异戊二烯6、醋酸丁酯27、儿茶酚2、乙酸乙酯14、增粘助剂5。
    所述的增粘助剂由以下重量份（公斤）的原料制得：
热塑性丙烯酸树脂4、硅烷偶联剂KH550 2、582-2 氨基树脂4、聚异丁烯3、、醋酸丁酯8、环烷酸钴0.2、双环戊二烯基铁0.6；
制备方法是：将热塑性丙烯酸树脂、582-2 氨基树脂加入到醋酸丁酯中，然入加入硅烷偶联剂KH550，加热至90-100℃，搅拌反应30-40分钟，然后加入聚异丁烯、双环戊二烯基铁、环烷酸钴，搅拌反应20-40分钟即得。
纸塑复合胶的制备方法，包括以下步骤：
将萜烯树脂、白油、邻苯二甲酸酐、壬基酚聚氧乙烯醚、乙烯基三乙氧基硅烷、丙酸乙烯酯、丙烯腈、异戊二烯、醋酸丁酯混合，加热至85-95℃，搅拌反应1-2小时；然后加入其它成分，继续搅拌反应2-3小时即得。
本发明于纸塑粘接，5小时后粘接剪切强度达到6 Mpa。

Claims (1)

1.一种纸塑复合胶，其特征在于由下列重量份的原料制成：
弹性聚氨酯树脂30-35、聚酯树脂12-14、萜烯树脂5-7、白油4-6、邻苯二甲酸酐8-10、壬基酚聚氧乙烯醚2-3、乙烯基三乙氧基硅烷2-3、丙酸乙烯酯12-14、丙烯腈3-5、异戊二烯4-6、醋酸丁酯24-27、儿茶酚1-2、乙酸乙酯12-14、增粘助剂4-5；所述的增粘助剂由以下重量份的原料制得：热塑性丙烯酸树脂3-4、硅烷偶联剂KH550 1-2、582-2 氨基树脂3-4、聚异丁烯2-3、、醋酸丁酯6-8、环烷酸钴0.1-0.2、双环戊二烯基铁0.4-0.6；
    该增粘助剂制备方法是：将热塑性丙烯酸树脂、582-2 氨基树脂加入到醋酸丁酯中，然后加入硅烷偶联剂KH550，加热至90-100℃，搅拌反应30-40分钟，然后加入聚异丁烯、双环戊二烯基铁、环烷酸钴，搅拌反应20-40分钟即得；
所述的纸塑复合胶的制备方法包括以下步骤：将萜烯树脂、白油、邻苯二甲酸酐、壬基酚聚氧乙烯醚、乙烯基三乙氧基硅烷、丙酸乙烯酯、丙烯腈、异戊二烯、醋酸丁酯混合，加热至75-95℃，搅拌反应1-2小时；然后加入其它成分，继续搅拌反应2-3小时即得。
CN201410110405.0A 2014-03-24 2014-03-24 一种纸塑复合胶及其制备方法 Expired - Fee Related CN103952088B (zh)