CN103952115B - 一种环保型药品泡罩包装用热封胶及其制备方法 - Google Patents
一种环保型药品泡罩包装用热封胶及其制备方法 Download PDFInfo
- Publication number
- CN103952115B CN103952115B CN201410110275.0A CN201410110275A CN103952115B CN 103952115 B CN103952115 B CN 103952115B CN 201410110275 A CN201410110275 A CN 201410110275A CN 103952115 B CN103952115 B CN 103952115B
- Authority
- CN
- China
- Prior art keywords
- seal adhesive
- butyl acetate
- environment
- preparation
- heat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种环保型药品泡罩包装用热封胶及其制备方法,其特征在于由下列重量份的原料制成:有机硅树脂30-34、丙烯酸乳液12-14、EVA乳液15-16、乙二醇20-23、丙三醇10-12、聚乙烯醇5-7、叔丁基过氧化氢1-2、苯基三乙氧基硅烷3-4、丙烯腈5-6、石油磺酸钠1-2、乙烯基三胺1-2、增粘助剂4-5、醋酸丁酯40-45。与现有技术相比热封强度高(可达17N/15MM)、抗回粘性好,可完全替代现有溶剂型VC热封胶,本发明热封胶所需工艺简单,生产效率高。
Description
技术领域
本发明涉及一种热封胶,更具体地说,是一种环保型药品泡罩包装用热封胶及其制备方法。
背景技术
包装行业在我国规模很大,包装时,纸塑粘合、纸纸粘合、塑铁粘合,均需要用于包装胶,现有包装热封胶多存在有毒溶剂残留,粘接强度不高等问题。不能满足现在的包装无害粘接需要。
发明内容
本发明的目的是提供一种环保型药品泡罩包装用热封胶及其制备方法。
本发明所采用的技术方案是:
一种环保型药品泡罩包装用热封胶,其特征在于由下列重量份的原料制成:有机硅树脂30-34、丙烯酸乳液12-14、EVA乳液15-16、乙二醇20-23、丙三醇10-12、聚乙烯醇5-7、叔丁基过氧化氢1-2、苯基三乙氧基硅烷3-4、丙烯腈5-6、石油磺酸钠1-2、乙烯基三胺1-2、增粘助剂4-5、醋酸丁酯40-45。
所述的增粘助剂由以下重量份的原料制得:热塑性丙烯酸树脂3-4、硅烷偶联剂KH570 1-2、582-2 氨基树脂3-4、丙烯酸-2- 羟基丙酯2-3、醋酸丁酯6-8、明矾粉0.3-0.4、苯乙烯4-6;
制备方法是:将热塑性丙烯酸树脂、582-2 氨基树脂加入到醋酸丁酯中,加热至110-120℃,再加入苯乙烯,搅拌反应40-60分钟后,加入明矾粉、丙烯酸-2- 羟基丙酯、硅烷偶联剂KH570,搅拌反应2-3小时,即得。
所述的环保型药品泡罩包装用热封胶的制备方法,其特征在于包括以下步骤:是将EVA乳液、乙二醇、丙三醇、聚乙烯醇、苯基三乙氧基硅烷、丙烯腈、石油磺酸钠、醋酸丁酯混合,加热至50-60℃,滴加叔丁基过氧化氢,搅拌反应60-70分钟,然后,加入其它剩余原料,加热至80-90℃同,反应1-2小时即得。
与现有技术相比热封强度高(可达17N/15MM)、抗回粘性好,可完全替代现有溶剂型VC热封胶,本发明热封胶所需工艺简单,生产效率高。
具体实施方式
一种环保型药品泡罩包装用热封胶,由下列重量份(公斤)的原料制成:
有机硅树脂34、丙烯酸乳液14、EVA乳液16、乙二醇23、丙三醇12、聚乙烯醇5、叔丁基过氧化氢2、苯基三乙氧基硅烷4、丙烯腈6、石油磺酸钠2、乙烯基三胺1、增粘助剂5、醋酸丁酯45。
所述的增粘助剂由以下重量份(公斤)的原料制得:热塑性丙烯酸树脂3、硅烷偶联剂KH570 2、582-2 氨基树脂4、丙烯酸-2- 羟基丙酯3、醋酸丁酯6、明矾粉0.4、苯乙烯6;
制备方法是:将热塑性丙烯酸树脂、582-2 氨基树脂加入到醋酸丁酯中,加热至110-120℃,再加入苯乙烯,搅拌反应40-60分钟后,加入明矾粉、丙烯酸-2- 羟基丙酯、硅烷偶联剂KH570,搅拌反应2-3小时,即得。
环保型药品泡罩包装用热封胶的制备方法,包括以下步骤:
是将EVA乳液、乙二醇、丙三醇、聚乙烯醇、苯基三乙氧基硅烷、丙烯腈、石油磺酸钠、醋酸丁酯混合,加热至50-60℃,滴加叔丁基过氧化氢,搅拌反应60-70分钟,然后,加入其它剩余原料,加热至80-90℃同,反应1-2小时即得。
将本发明用于印铁罐口与塑料薄膜的粘接,5小时后粘接强度达17N/15MM。
Claims (2)
1.一种环保型药品泡罩包装用热封胶,其特征在于由下列重量份的原料制成:有机硅树脂30-34、丙烯酸乳液12-14、EVA乳液15-16、乙二醇20-23、丙三醇10-12、聚乙烯醇5-7、叔丁基过氧化氢1-2、苯基三乙氧基硅烷3-4、丙烯腈5-6、石油磺酸钠1-2、乙烯基三胺1-2、增粘助剂4-5、醋酸丁酯40-45;
所述的增粘助剂由以下重量份的原料制得:热塑性丙烯酸树脂3-4、硅烷偶联剂KH570 1-2、582-2 氨基树脂3-4、丙烯酸-2- 羟基丙酯2-3、醋酸丁酯6-8、明矾粉0.3-0.4、苯乙烯4-6;
所述的增粘助剂制备方法是:将热塑性丙烯酸树脂、582-2 氨基树脂加入到醋酸丁酯中,加热至110-120℃,再加入苯乙烯,搅拌反应40-60分钟后,加入明矾粉、丙烯酸-2- 羟基丙酯、硅烷偶联剂KH570,搅拌反应2-3小时,即得。
2.根据权利要求1所述的环保型药品泡罩包装用热封胶的制备方法,其特征在于包括以下步骤:是将EVA乳液、乙二醇、丙三醇、聚乙烯醇、苯基三乙氧基硅烷、丙烯腈、石油磺酸钠、醋酸丁酯混合,加热至50-60℃,滴加叔丁基过氧化氢,搅拌反应60-70分钟,然后,加入其它剩余原料,加热至80-90℃,反应1-2小时即得。