CN102795889A - Preparation technology of engraved colored ceramic product - Google Patents
Preparation technology of engraved colored ceramic product Download PDFInfo
- Publication number
- CN102795889A CN102795889A CN2012102843351A CN201210284335A CN102795889A CN 102795889 A CN102795889 A CN 102795889A CN 2012102843351 A CN2012102843351 A CN 2012102843351A CN 201210284335 A CN201210284335 A CN 201210284335A CN 102795889 A CN102795889 A CN 102795889A
- Authority
- CN
- China
- Prior art keywords
- engraved
- porcelain
- ceramic product
- preparation technology
- product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an engraved colored ceramic product, particularly relates to a preparation technology of the engraved colored ceramic product. The preparation technology disclosed herein is characterized by coating an inorganic ceramic decorative material on an engraved ceramic product and then sintering. According to the invention, by painting the inorganic ceramic decorative material on the engraved ceramic section and sintering at 750-900 DEG C, the ceramic product can be preserved for a long time without losing color, fading and other problems on the premise of keeping original artistic characteristics of the engraved ceramic product, can be washed with water without loss, and is easy to clean. The technology disclosed herein is suitable for engraving decoration of ceramics, porcelain, glass, colored glaze and other vessels, and is a novel breakthrough and innovation in engraving decoration technology.
Description
Technical field
The present invention relates to the carved porcelain product, be specifically related to the preparation technology that a kind of carved porcelain is composed color product.
Background technology
Carved porcelain is technical and an artistry and the skill of depositing, and the author writes on one's behalf with cutter according to its creation thought, depicts the depth of texture, the variation of level etc., and arranges in pairs or groups each other with different decorative colors.Be coated with paint operation be to carved porcelain picture and decorative effect carry out perfect at last, rather than random color is filled.
The technical process of traditional Chinese manual carved porcelain art is following:
(1) skeletonizing on porcelain;
(2) delineate, cut a hole, engrave with icking tool according to grain pattern that sketch is painted;
(3) in carving good texture, be coated with and paint color, the artistic effect of picture is shown.
Used being coated with of tradition carved porcelain painted color and is generally common normal temperature pigment such as Chinese painting color, oil colour, do not use the inorganic ceramic finishing material, so the color keeping quality is poor, as long as the shelf-time one is long, color relation can change to some extent, even fades.And be coated with the Chinese painting color painted or oil colour and meet water etc. and be cleaned easily or scrape and wipe, this is because porcelain body does not absorb water.So traditional carved porcelain durability of product is relatively poor, finally influence whole attractive in appearance, the artistic value of carved porcelain works, artistic effect and reserve value.
Summary of the invention
Technical problem to be solved by this invention provides the preparation technology that a kind of carved porcelain is composed color product, makes the carved porcelain works on the basis that keeps its original artistic value, can can't harm preservation, colour-fast and easy to clean for a long time.
Carved porcelain of the present invention is composed the preparation technology of color product, is with behind the product coating inorganic ceramic decoration material behind the carved porcelain, product is burnt till again.
Described firing temperature is 750 ~ 900 ℃.
The present invention adopts traditional-handwork carved porcelain skill, carries out the seal cutting of porcelain body glaze, carcass with instruments (or power tool) such as icking tool, cutter, hammers, and then will carve the creation idea of good texture according to the author; Be coated with and paint suitable inorganic ceramic finishing material, treat thorough drying after, through 750 ~ 900 ℃ of easy fireds; Adopt the fast calcining system in slow earlier back; Fire, make inorganic ceramic finishing material color development, and firmly be attached to ceramic surface.
Described inorganic ceramic finishing material comprises pigment, colorant that is applicable to pottery, glass and the glaze that contains painted or chromonic material.
The inorganic ceramic finishing material is through easy fired, and fusion also is attached to the porcelain surface, forms articulamentum closely, and can not come off, fade, and can water-fast flushing and wiping.And the setting of calcining system should adjust accordingly according to the carved porcelain works, considers shape, size of the coefficient of expansion and the ceramic of porcelain base etc. simultaneously.The carved porcelain works through the delineation of instruments such as icking tool, hammer, beat, porcelain base inside may produce the tiny crack of part, if burn till improperly, just possibly cause cracking, this creation to the carved porcelain works is catastrophic.So calcining system should be followed the fast principle in earlier slow back, and in the porcelain base quartzy transition temperature point, suitably slow down the speed of burning till, to guarantee the integrity of product.
Before and after the inorganic ceramic finishing material burns till tangible tone difference is arranged, belong to the back chromonic materials, accomplish to know what's what so the author should burn the back color development to it in advance in the process of using, and rationally decorate.
Beneficial effect of the present invention is following:
The present invention uses the inorganic ceramic finishing material to be coated with and is painted on the ceramic cross section of scribing moulding; And under 750 ~ 900 ℃, fire and form; Make the carved porcelain works under the prerequisite that keeps original artistic characteristic, can preserve for a long time, the problems such as coming off, fade of color can not occur; Used water can't harm scrubs, easy to clean.This method is adapted to the carved porcelain of vessel such as pottery, porcelain, glass, coloured glaze and decorates, and is that carved porcelain is decorated new breakthrough in skill aspect and innovation.
Embodiment
Below in conjunction with embodiment the present invention is done further description.
Embodiment 1
With the quartz enriched porcelain is example:
Behind the product coating inorganic ceramic decoration material behind the carved porcelain, treat thorough drying after, through 900 ℃ of easy fireds, sintering curve is following: room temperature ~ 300 ℃, 3 ℃/min; 300 ~ 550 ℃, 3.5 ℃/min; 550 ~ 600 ℃, 2.5 ℃/min; 600 ~ 900 ℃, 4.5 ℃/min, insulation 15min.
Room temperature ~ 300 ℃ mainly are the moisture evaporation stages, the discharge of planar water, and maybe be with the conversion of β-cristobalite to α-Fang Shiying; 300 ~ 550 ℃ mainly is the discharge of crystal water and organic oxidation etc.; 550 ~ 600 ℃, relate generally to the crystal formation conversion of alpha-quartz and β-quartz; 600 ~ 900 ℃, normal color development such as pigment.
Embodiment 2
With the fine pottery is example:
Behind the product coating inorganic ceramic decoration material behind the carved porcelain, treat thorough drying after, through 820 ℃ of easy fireds, sintering curve is following: room temperature ~ 550 ℃, 4.5 ℃/min; 550 ~ 600 ℃, 2.5 ℃/min; 600 ~ 820 ℃, 4.5 ℃/min, insulation 15min.Because pottery is with respect to porcelain, liquid composition is less relatively, so this sintering process can be suitably hurry up.
Claims (2)
1. a carved porcelain is composed the preparation technology of color product, it is characterized in that: behind the product coating inorganic ceramic decoration material behind the carved porcelain, product is burnt till again.
2. carved porcelain according to claim 1 is composed the preparation technology of color product, it is characterized in that: described firing temperature is 750 ~ 900 ℃.