CN102758220A - 铝电解用预焙阳极的配料方法 - Google Patents

铝电解用预焙阳极的配料方法 Download PDF

Info

Publication number
CN102758220A
CN102758220A CN2012102603146A CN201210260314A CN102758220A CN 102758220 A CN102758220 A CN 102758220A CN 2012102603146 A CN2012102603146 A CN 2012102603146A CN 201210260314 A CN201210260314 A CN 201210260314A CN 102758220 A CN102758220 A CN 102758220A
Authority
CN
China
Prior art keywords
petroleum coke
prebaked anode
asphalt
weight percent
smithing petroleum
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012102603146A
Other languages
English (en)
Inventor
孙四清
周广新
魏民
翟庆申
高锋
林银芳
殷绍福
李跃
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JINAN HAICHUAN INVESTMENT GROUP CO Ltd
Original Assignee
JINAN HAICHUAN INVESTMENT GROUP CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JINAN HAICHUAN INVESTMENT GROUP CO Ltd filed Critical JINAN HAICHUAN INVESTMENT GROUP CO Ltd
Priority to CN2012102603146A priority Critical patent/CN102758220A/zh
Publication of CN102758220A publication Critical patent/CN102758220A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种铝电解用预焙阳极的配料方法属于炭素制品的生产方法，特别是铝电解用预焙阳极的生产方法。该铝电解用预焙阳极的配料方法，其特征在于：各原料的重量百分比为：煅后石油焦80±2％、收尘粉4％、沥青16±2％，其中在煅后石油焦中各粒级物料所占重量百分比为12-6mm为23±2％、6-3mm为17±2％、3-1mm为16±2％、1-0.15mm为9±2％、磨粉为36±2％。本发明的有益效果是通过大批量试验生产分析：生产中增加部分大颗粒粒级，相应降低沥青的加入量，可以有效降低预焙阳极制品的电阻率、增加强度，同时，由于沥青含量的降低，减少了焙烧过程中沥青烟气的挥发，降低环境污染。

Description

铝电解用预焙阳极的配料方法
技术领域
本发明属于炭素制品的生产方法，特别是铝电解用预焙阳极的生产方法。 
背景技术
生产铝电解用预焙阳极制品，需要具有良好的导电性能、强度等质量指标。《铝电解用预焙阳极》(YS/T285-2007)中规定“预焙阳极一级品要求标准电阻率≤55μΩ.m”，炭素预焙阳极传统的生产配方为6-3mm、3-1mm、1-0.15mm、磨粉，按照一定比例掺配后，通过成型、焙烧等工艺流程生产出预焙阳极制品，其电阻率为56-57.2μΩ.m，达不到“预焙阳极一级品要求标准电阻率≤55μΩ.m”的标准。 
发明内容
本发明的目的是提供一种降低预焙阳极电阻率的铝电解用预焙阳极的配料方法。 
本发明的技术方案为，一种铝电解用预焙阳极的配料方法，其特征在于：各原料的重量百分比为：煅后石油焦80±2％、收尘粉4％、沥青16±2％，其中在煅后石油焦中各粒级物料所占重量百分比为12-6mm为23±2％、6-3mm为17±2％、3-1mm为16±2％、1-0.15mm为9±2％、磨粉为36±2％： 
其中煅后石油焦的质量标准：水分≤0.5％，灰分≤0.5％，挥发份≤0.5％，碎焦电阻≤530μΩ/mm，真密度≥2.04g/cm3， 
煤沥青以改质沥青为主，软化点105-110℃，甲苯不溶物比值≥28％，喹啉不溶物比值≤12％，结焦值≥54％； 
磨粉纯度为65-70％。 
优选的各原料的重量百分比为：煅后石油焦80％、收尘粉4％、沥青16％，其中在煅后石油焦中各粒级物料所占重量百分比为12-6mm 为22％、6-3mm为18％、3-1mm为16％、1-0.15mm为7％、磨粉为37％。 
使用原配方和新配方制成的预焙阳极的各项性能指标对照表 
Figure BDA00001934687900021
本发明的有益效果是通过大批量试验生产分析：生产中增加部分大颗粒粒级，相应降低沥青的加入量，可以有效降低预焙阳极制品的电阻率、增加强度，同时，由于沥青含量的降低，减少了焙烧过程中沥青烟气的挥发，降低环境污染。 
多粒级大颗粒配方的使用可改善预焙阳极的内在质量：1.降低阳极电阻率、提高强度，一级成品率较高；2.提高阳极的电流密度，加大阳极的热导率；3.提高抗振热性，增加二氧化碳反应残余量；4.增加空气反应性残余量；5.减少设备的使用频率，延长了设备使用寿命；6.降低粉尘和沥青烟气的排放量，符合国家节能减排环保要求，创造了较好的社会效益。 
具体实施方式
本发明的具体实施方式是： 
实施例1，一种铝电解用预焙阳极的配料方法，其特征在于：各原料的重量百分比为：煅后石油焦80％、收尘粉4％、沥青16％，其中在煅后石油焦中各粒级物料所占重量百分比为12-6mm为22％、6-3mm为18％、3-1mm为16％、1-0.15mm为7％、磨粉为37％。 
其中煅后石油焦的质量标准：水分≤0.5％，灰分≤0.5％，挥发份≤0.5％，碎焦电阻≤530μΩ/mm，真密度≥2.04g/cm3， 
煤沥青以改质沥青为主，软化点105-110℃，甲苯不溶物比值≥28％，喹啉不溶物比值≤12％，结焦值≥54％； 
磨粉纯度为65-70％。 

Claims (2)

1.一种铝电解用预焙阳极的配料方法，其特征在于：各原料的重量百分比为：煅后石油焦80±2％、收尘粉4％、沥青16±2％，其中在煅后石油焦中各粒级物料所占重量百分比为12-6mm为23±2％、6-3mm为17±2％、3-1mm为16±2％、1-0.15mm为9±2％、磨粉为36±2％：
其中煅后石油焦的质量标准：水分≤0.5％，灰分≤0.5％，挥发份≤0.5％，碎焦电阻≤530μΩ/mm，真密度≥2.04g/cm3，
煤沥青以改质沥青为主，软化点105-110℃，甲苯不溶物比值≥28％，喹啉不溶物比值≤12％，结焦值≥54％；
磨粉纯度为65-70％。
2.由权利要求1所述的铝电解用预焙阳极的配料方法，其特征在于：各原料的重量百分比为：煅后石油焦80％、收尘粉4％、沥青16％，其中在煅后石油焦中各粒级物料所占重量百分比为12-6mm为22％、6-3mm为18％、3-1mm为16％、1-0.15mm为7％、磨粉为37％。
CN2012102603146A 2012-07-26 2012-07-26 铝电解用预焙阳极的配料方法 Pending CN102758220A (zh)