CN102746726A - 一种带锈腻子灰 - Google Patents

一种带锈腻子灰 Download PDF

Info

Publication number
CN102746726A
CN102746726A CN2012102541671A CN201210254167A CN102746726A CN 102746726 A CN102746726 A CN 102746726A CN 2012102541671 A CN2012102541671 A CN 2012102541671A CN 201210254167 A CN201210254167 A CN 201210254167A CN 102746726 A CN102746726 A CN 102746726A
Authority
CN
China
Prior art keywords
rust
putty
add
stir
solvent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012102541671A
Other languages
English (en)
Other versions
CN102746726B (zh
Inventor
江拥
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU HUAXIA PAINT-MAKING CO LTD
Original Assignee
JIANGSU HUAXIA PAINT-MAKING CO LTD
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU HUAXIA PAINT-MAKING CO LTD filed Critical JIANGSU HUAXIA PAINT-MAKING CO LTD
Priority to CN201210254167.1A priority Critical patent/CN102746726B/zh
Publication of CN102746726A publication Critical patent/CN102746726A/zh
Application granted granted Critical
Publication of CN102746726B publication Critical patent/CN102746726B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供了一种带锈腻子灰,属于涂料技术领域。包括有如下按重量百分比计的组分:过氯乙烯树脂4~6%、松香树脂0.85~1.64%、缓蚀剂0.5~3%、白碳黑0.2~0.5%、立德粉7~12%、重钙粉15~25%、重晶石粉25~45%、滑石粉5~10%、溶剂6~25%。可直接将底材的铁锈进行“钝化”处理,同时达到填充的功效,又达到了“自除锈-防腐”的效果。

Description

一种带锈腻子灰
技术领域
本发明提供了一种带锈腻子灰,属于涂料技术领域。
背景技术
现大型机床或机械以及各类大中型操作室在涂装时,一般采用的工艺为“除油-除锈-打磨-刮腻子灰-打磨-喷涂底漆1-喷涂底漆2-打磨-喷涂面漆1-喷涂面漆2-修补”,且防腐性能完全取决于底漆和面漆的保护能力,腻子灰在其中只能起到填充的功效,并且刮腻子灰之前必须对底材进行除油除锈打磨处理,否则会出现掉漆异常。不仅操作步骤多,而且喷涂漆面的质量经常不过关。
现研发一种带锈腻子灰,可直接将底材的铁锈进行“钝化”处理,同时达到填充的功效,又达到了“自除锈-防腐”的效果。
发明内容
根据上述问题,本发明提供了一种带锈腻子灰,可直接将底材的铁锈进行“钝化”处理,同时达到填充的功效,又达到了“自除锈-防腐”的效果。
本发明采用的技术方案是:
一种带锈腻子灰,包括有如下按重量百分比计的组分:
过氯乙烯树脂4~6%、松香树脂0.85~1.64%、缓蚀剂0.5~3%、白碳黑0.2~0.5%、立德粉7~12%、重钙粉15~25%、重晶石粉25~45%、滑石粉5~10%、溶剂6~25%。
上述的溶剂为二甲苯、醋酸丁酯、环己酮的任意比例混合物。
上述的松香树脂可以采用松香树脂424。
本发明提供的带锈腻子灰的制备方法是:
(a)在溶剂中加入松香树脂和过氯乙烯树脂,搅拌溶解;
(b)再加入缓蚀剂,搅拌;边搅拌边加入白碳黑、立德粉、重晶石粉、滑石粉、重钙粉,搅拌均匀;
(c)进行研磨。
作为本发明进一步优选的方案,为了防止带锈腻子灰其开裂收缩现象,可添加0.2~0.5%的二辛酯和2~6%的清油。
上述优选方案的带锈腻子灰的制备方法是:
(1)在溶剂中加入松香树脂和过氯乙烯树脂,搅拌溶解;
(2)再加入缓蚀剂,搅拌;边搅拌边加入白碳黑、立德粉、重晶石粉、滑石粉、重钙粉,搅拌均匀;
(3)再加入清油和二辛酯,搅拌均匀;
(4)进行研磨。
本发明提供的带锈腻子灰,具有优异的防腐性能,可直接在带锈的底材上进行施工,并且可以将铁锈通过“钝化”现象达到防腐作用,可大大节约原对底材除锈打磨处理工序所带来的成本,同时具备原过氯乙烯腻子灰的填充性、打磨性、配套性、收缩性。
具体实施方式
以下实施例所采用如下原料:
过氯乙烯树脂(河南鸿诚化工有限公司)
松香树脂(松香树脂424,上海长宁松香公司)
缓蚀剂(磷钼酸锌钙ZAP,德国Heubach公司)
白碳黑(无锡市大鑫环保材料有限公司)
立德粉(常州丰硕化工有限公司)
重钙粉(山东临沂雷德重钙滑石粉厂)
重晶石粉(灵寿县安达矿物粉体厂)
滑石粉(山东雷德重钙滑石粉厂)
环己酮(杭州宏达化工有限责任公司)
二甲苯(天津市辰光化工有限公司)
醋酸丁酯(成都市龙恒化工有限公司)
二辛酯(济南东郡化工有限公司)
清油(Y00-7,天津市华新化工有限公司)
实施例1~实施例5
各组分重量如表1所示:
表1实施例1~实施例5的带锈腻子灰的组分重量
Figure BDA00001917568300031
制备方法是:
1、在溶剂(环己酮、二甲苯、醋酸乙酯的混合物)中加入松香树脂和过氯乙烯树脂,搅拌溶解,测试其细度为10微米以内;
2、再将缓蚀剂加入上述溶解好的过氯乙烯及松香树脂中,充分搅拌均匀,作为树脂溶液;
3、往树脂溶液中添加白碳黑、立德粉、重钙粉、重晶石粉、滑石粉,充分搅拌均匀;
4、采用S260型三辊机进行研磨,一般情况下过一遍三辊机即可直接包装。
使用方法是:
分别将测试小样直接刮涂于带锈的冷轧板底漆上,对其性能进行检测,检测方法采用国标法;配套性的测试方法是使用本实施例中的带锈腻子灰分别配套丙烯酸灰中涂和纯白丙烯酸聚氨酸面漆;
表2实施例1~实施例5的带锈腻子灰的性能测试数据
Figure BDA00001917568300032
实施例6~实施例10
备制各组分原料:
各组分重量配比如表3所示。
表3实施例6~实施例10的带锈腻子灰的组分重量
Figure BDA00001917568300042
制备方法是:
1、将过氯乙烯树脂、松香树脂加入溶剂(环己酮、二甲苯、醋酸乙酯的混合物)完全溶解,测试其细度为10微米以内;
2、再将缓蚀剂加入上述溶解好的过氯乙烯及松香树脂中,充分搅拌均匀,作为树脂溶液;
3、往树脂溶液中添加白碳黑、立德粉、重钙粉、重晶石粉、滑石粉,充分搅拌均匀;
4、在步骤3所得的混合物中加入清油、二辛酯,搅拌均匀;
5、采用S260型三辊机进行研磨,一般情况下过一遍三辊机即可直接包装。
分别将测试小样直接刮涂于带锈的冷轧板底漆上,对其性能进行检测,测试方法同实施例1~实施例5:
表4实施例6~实施例10的带锈腻子灰的性能测试数据
Figure BDA00001917568300051
此组实施例中添加了清油和二辛酯,提高了表面光洁度,不易出现开裂现象,收缩率低。

Claims (6)

1.一种带锈腻子灰,包括有如下按重量百分比计的组分:过氯乙烯树脂4~6%、松香树脂0.85~1.64%、缓蚀剂0.5~3%、白碳黑0.2~0.5%、立德粉7~12%、重钙粉15~25%、重晶石粉:25~45%、滑石粉:5~10%、溶剂6~25%。
2.根据权利要求1所述的带锈腻子灰,其特征在于:还包括有按重量百分比计的清油2~6%、二辛酯0.2~0.5%。
3.根据权利要求1所述的带锈腻子灰,其特征在于:所述的溶剂为二甲苯、醋酸丁酯、环己酮的任意比例混合物。
4.根据权利要求1所述的带锈腻子灰,其特征在于:各组分的重量百分比含量是:过氯乙烯树脂5%、松香树脂1%、缓蚀剂2%、白碳黑0.5%、立德粉10%、重钙粉20%、重晶石粉30%、滑石粉6.5%、溶剂25%。
5.权利要求1所述的带锈腻子灰的制备方法,包括以下步骤:
(a)在溶剂中加入松香树脂和过氯乙烯树脂,搅拌溶解;
(b)再加入缓蚀剂,搅拌;边搅拌边加入白碳黑、立德粉、重晶石粉、滑石粉、重钙粉,搅拌均匀;
(c)进行研磨。
6.权利要求2所述的带锈腻子灰的制备方法,包括以下步骤:
(a)在溶剂中加入松香树脂和过氯乙烯树脂,搅拌溶解;
(b)再加入缓蚀剂,搅拌;边搅拌边加入白碳黑、立德粉、重晶石粉、滑石粉、重钙粉,搅拌均匀;
(c)再加入清油和二辛酯,搅拌均匀;
(d)进行研磨。
CN201210254167.1A 2012-07-23 2012-07-23 一种带锈腻子灰 Active CN102746726B (zh)