CN102732047A - 一种3162立索尔宝红a6b的制备方法 - Google Patents
一种3162立索尔宝红a6b的制备方法 Download PDFInfo
- Publication number
- CN102732047A CN102732047A CN2012101688895A CN201210168889A CN102732047A CN 102732047 A CN102732047 A CN 102732047A CN 2012101688895 A CN2012101688895 A CN 2012101688895A CN 201210168889 A CN201210168889 A CN 201210168889A CN 102732047 A CN102732047 A CN 102732047A
- Authority
- CN
- China
- Prior art keywords
- coupling
- add
- preparation
- temperature
- acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种3162立索尔宝红A6B的制备方法,该方法包括以下步骤:将4B酸、液碱在溶解釜中溶解至透明,加冰降温,加盐酸酸析,加入亚硝酸钠溶液,搅拌1小时,留作备用,将2,3酸、液碱、水在溶解釜溶解透明放入偶合釜中,调整温度和体积,加入重氮液溶液进行偶合,偶合完毕,加入溶解好的松香皂。按照工艺时间加入氯化钙进行色淀,进入压滤机洗涤,将滤饼烘干磨粉包装得到产品,该种产品满足了塑料、油墨的着色要求,而且在纤维喷丝使用中可耐230℃高温,同时降低了生产成本。
Description
技术领域
本发明涉及一种颜料的制备方法,具体地说,涉及一种3162立索尔宝红A6B的制备方法。
背景技术
随着人民生活需求的提高,许多地方如油墨,有色塑料都用到颜料,且颜料的性能要求也越来越高,3162立索尔宝红A6B主要用于塑料,油墨等的着色,因而需要其要有高的着色率。
发明内容
本发明所要解决的技术问题是提供一种制备着色率高的3162立索尔宝红A6B的方法。
本发明解决其技术问题所采取的方案是:一种3162立索尔宝红A6B的制备方法,该方法包括以下步骤:
a.将4B酸、液碱用水在溶解釜中溶解至透明,并加冰降温至工艺温度;
b.加入盐酸进行酸析,酸析至PH=6-7.5;
c.加入亚硝酸钠溶液和冰块,搅拌1小时,留作备用;
d.在溶解釜加入2,3酸,然后加入液碱和水使温度升至60℃,将其溶解至透明后放入偶合釜中,调整偶合温度为10℃,偶合体积为偶合组份的20倍,再加入上述步骤c中留作备用的重氮液溶液进行偶合,偶合完毕,搅拌30分钟,然后调整PH值为9.5;
e.加入溶解好的松香皂,调整PH值至10-10.5,调整色淀工艺温度为25℃;
f.按照工艺时间加入氯化钙进行色淀,搅拌至工艺时间,再将温度升至工艺温度,按照工艺要求保温;
g.保温完毕后进入压滤机压滤、洗涤,将滤饼烘干再将其磨成粉装进行包装得到最终产品。
作为优选,所述步骤a的工艺温度为0℃-5℃。
作为优选,所述步骤f中的工艺温度为60℃-95℃,工艺时间为40min-70min。
作为优选,所述步骤g中压滤的压强为0.3MPa-0.6MPa,压滤时间为3h-6h。
本发明的有益效果是:本发明提供的3162立索尔宝红A6B的制备方法所生产的3162立索尔宝红A6B满足了塑料、油墨的着色要求,而且在纤维喷丝使用中可耐230度高温,同时该种制备方法降低了成本。
附图说明:
下面结合附图对本发明进一步说明。
图1是本发明3162立索尔宝红A6B的制备方法工艺流程图。
具体实施方式
下面结合附图及具体实施方式对本发明进行详细描述:如图1所示的
一种3162立索尔宝红A6B的制备方法,该方法包括以下步骤:将4B酸、液碱用水在溶解釜中溶解至透明,并加冰降温至工艺温度(0℃-5℃);加入盐酸进行酸析,酸析至PH=0.5-1;加入亚硝酸钠溶液和冰块,搅拌1小时,留作备用;在溶解釜加入2,3酸然后加入液碱和水使温度升至60℃,将其溶解至透明后放入偶合釜中,调整偶合温度为10℃,偶合体积为偶合组份的20倍,再加入留作备用的重氮液溶液进行偶合,偶合完毕,搅拌30分钟,然后调整PH值为9.5;加入溶解好的松香皂,调整PH值至10-10.5,调整色淀工艺温度为25℃;按照工艺时间加入氯化钙进行色淀,搅拌至工艺时间(40min-70min),再将温度升至工艺温度(60℃-95℃),按照工艺要求保温;保温完毕后进入压滤机压滤(压强为0.3MPa-0.6MPa、压滤时间为3h-6h)、洗涤,将滤饼烘干再将其磨成粉装进行包装得到最终产品。本发明提供的3162立索尔宝红A6B的制备方法所生产的3162立索尔宝红A6B满足了塑料、油墨的着色要求,而且在纤维喷丝使用中可耐230℃高温,同时降低了生产成本。
需要强调的是:以上仅是本发明的较佳实施例而已,并非对本发明作任何形式上的限制,凡是依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰,均仍属于本发明技术方案的范围内。
Claims (4)
1.一种3162立索尔宝红A6B的制备方法,其特征在于:该方法包括以下步骤:
a.将4B酸、液碱用水在溶解釜中溶解至透明,并加冰降温至工艺温度;
b.加入盐酸进行酸析,酸析至PH=0.5-1;
c.加入亚硝酸钠溶液和冰块,搅拌1小时,留作备用;
d.在溶解釜加入2,3酸,然后加入液碱和水使温度升至60℃,将其溶解至透明后放入偶合釜中,调整偶合温度为10℃,偶合体积为偶合组份的20倍,再加入上述步骤c中留作备用的重氮液溶液进行偶合,偶合完毕,搅拌30分钟,然后调整PH值为9.5;
e.加入溶解好的松香皂,调整PH值至10-10.5,调整色淀工艺温度为25℃;
f.按照工艺时间加入氯化钙进行色淀,搅拌至工艺时间,再将温度升至工艺温度,按照工艺要求保温;
g.保温完毕后进入压滤机压滤、洗涤,将滤饼烘干再将其磨成粉装进行包装得到最终产品。
2.根据权利要求1所述的3162立索尔宝红A6B的制备方法,其特征在于:所述步骤a的工艺温度为0℃-5℃。
3.根据权利要求1所述的3162立索尔宝红A6B的制备方法,其特征在于:所述步骤f中的工艺温度为60℃-95℃,工艺时间为40min-70min。
4.根据权利要求1所述的3162立索尔宝红A6B的制备方法,其特征在于:所述步骤g中压滤的压强为0.3MPa-0.6MPa,压滤时间为3h-6h。