CN102720069B - 一种纺织品用隔热保温涂料 - Google Patents

一种纺织品用隔热保温涂料 Download PDF

Info

Publication number
CN102720069B
CN102720069B CN2012101378225A CN201210137822A CN102720069B CN 102720069 B CN102720069 B CN 102720069B CN 2012101378225 A CN2012101378225 A CN 2012101378225A CN 201210137822 A CN201210137822 A CN 201210137822A CN 102720069 B CN102720069 B CN 102720069B
Authority
CN
China
Prior art keywords
heat insulation
weight portions
parts
textiles
insulation coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2012101378225A
Other languages
English (en)
Other versions
CN102720069A (zh
Inventor
刘昆虎
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
KAIPING CITY PAINT CO Ltd ON SOLID EDGE
Original Assignee
KAIPING CITY PAINT CO Ltd ON SOLID EDGE
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by KAIPING CITY PAINT CO Ltd ON SOLID EDGE filed Critical KAIPING CITY PAINT CO Ltd ON SOLID EDGE
Priority to CN2012101378225A priority Critical patent/CN102720069B/zh
Publication of CN102720069A publication Critical patent/CN102720069A/zh
Application granted granted Critical
Publication of CN102720069B publication Critical patent/CN102720069B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种纺织品用隔热保温涂料，该纺织品用隔热保温涂料含有天然橡胶、水性环氧树脂、水性酚醛树脂、成膜助剂、分散剂、颜填料、水等组分，本涂料隔热保温效果优秀、柔韧性好、对织物的附着力强，可用于各类纺织品，如篷布、帘布之上。

Description

一种纺织品用隔热保温涂料
技术领域
本发明涉及一种涂料，具体涉及一种纺织品用隔热保温涂料。
背景技术
现有的隔热涂料产品大多数应用在混凝土或金属结构表面起到隔热效果，这类隔热涂料的柔韧性、致密性及附着性一般比较差，不宜涂刷于纺织品上，进行隔热保温。但随着帐篷、遮阳伞、遮阳蓬等户外纺织品及遮阳布帘的广泛应用，人们对纺织品的隔热保温性能的要求也越来越高。因此，开发一种隔热保温效果优秀、具有良好柔韧性与致密性、附着力强、便于操作的纺织品用隔热保温涂料，具有重要的实践意义。
发明内容
本发明提供了一种隔热保温效果优秀、柔韧性好、对织物的附着力强的纺织品用隔热保温涂料。
本发明所采用的技术方案如下：
一种纺织品用隔热保温涂料，含有天然橡胶30～50重量份、水性环氧树脂2～8重量份、水性酚醛树脂1～8重量份、成膜助剂4.5～12.5重量份、分散剂1～4重量份、颜填料30～55重量份、水20～25重量份。
优选的，所述成膜助剂为邻苯二甲酸二丁酯、苯甲醇和正丁醛苯胺缩合物中的任意一种或一种以上的组合。
优选的，所述分散剂为三乙醇胺、六偏磷酸钠、聚丙烯酸钠盐中的任意一种或一种以上的组合。
优选的，所述颜填料为金红石钛白粉、沉淀硫酸钡、硅石灰粉和白炭黑中的任意一种或一种以上的组合。
优选的，所述成膜助剂由邻苯二甲酸二丁酯2～6重量份、苯甲醇2～6重量份、正丁醛苯胺缩合物0.1～0.5重量份组成。
优选的，所述颜填料由金红石钛白粉15～25重量份、沉淀硫酸钡10～20重量份、白炭黑3～10重量份组成。
优选的，所述白炭黑为纳米级气相白炭黑。
本发明具有以下有益效果：
（1）本发明的隔热保温涂料柔韧性好、对织物的附着力强，可以直接涂敷在各类纺织品上，如各类篷布、帘布之上，不易开裂、脱落、使用寿命长；
（2）本发明的隔热保温效果优秀，当气温高、日照强烈时，它可以反射绝大部分来自太阳的热能，同时加速自身热量散发，使帐篷内部保持较低的温度，在夏季阳光强烈时内外温差最高可达20度以上；在气候寒冷、需要保温的场合使用时，只需将该涂料涂刷在帐篷的内侧表面（有些帐篷设计为正反面可以互换），就可以使内部热源（取暖设备、人体、仪器设备等等）产生的热量反射回内部空间，减少热量损失，使帐篷内部相对温暖舒适。
具体实施方式
一种纺织品用隔热保温涂料，含有天然橡胶30～50重量份、水性环氧树脂2～8重量份、水性酚醛树脂1～8重量份、成膜助剂4.5～12.5重量份、分散剂1～4重量份、颜填料30～55重量份、水20～25重量份。
优选的，所述成膜助剂为邻苯二甲酸二丁酯、苯甲醇和正丁醛苯胺缩合物中的任意一种或一种以上的组合。
优选的，所述分散剂为三乙醇胺、六偏磷酸钠、聚丙烯酸钠盐中的任意一种或一种以上的组合。
优选的，所述颜填料为金红石钛白粉、沉淀硫酸钡、硅石灰粉和白炭黑中的任意一种或一种以上的组合。
优选的，所述成膜助剂由邻苯二甲酸二丁酯2～6重量份、苯甲醇2～6重量份、正丁醛苯胺缩合物0.1～0.5重量份组成。
优选的，所述颜填料由金红石钛白粉15～25重量份、沉淀硫酸钡10～20重量份、白炭黑3～10重量份组成。
优选的，所述白炭黑为纳米级气相白炭黑。
以下结合实例对本发明作进一步具体描述，但并不局限于此。
实施例1
本发明的纺织品用隔热保温涂料的一个优选方案，含有以下重量份比的组分：天然橡胶30份、 水性环氧树脂3份、水性酚醛树脂3份、邻苯二甲酸二丁酯6份、苯甲醇6份、正丁醛苯胺缩合物0.5份、三乙醇胺2份、六偏磷酸钠2份、金红石钛白粉15份、沉淀硫酸钡15份、纳米级气相白炭黑5份、去离子水23份。
实施例2
本发明的纺织品用隔热保温涂料的一个优选方案，含有以下重量份比的组分：天然橡胶35份、水性环氧树脂5份、水性酚醛树脂3份、邻苯二甲酸二丁酯4份、苯甲醇4份、正丁醛苯胺缩合物0.3份、三乙醇胺2份、聚丙烯酸钠盐2份、金红石钛白粉20份、沉淀硫酸钡20份、纳米级气相白炭黑3份、去离子水20份。
实施例3
本发明的纺织品用隔热保温涂料的一个优选方案，含有以下重量份比的组分：天然橡胶40份、水性环氧树脂2份、水性酚醛树脂5份、邻苯二甲酸二丁酯4份、苯甲醇4份、正丁醛苯胺缩合物0.1份、六偏磷酸钠3份、金红石钛白粉17份、硅灰石粉12份、纳米级气相白炭黑6份、去离子水20份。
实施例4
本发明的纺织品用隔热保温涂料的一个优选方案，含有以下重量份比的组分：天然橡胶50份、水性环氧树脂8份、水性酚醛树脂1份、邻苯二甲酸二丁酯2份、苯甲醇2份、正丁醛苯胺缩合物0.5份、三乙醇胺1份、金红石钛白粉25份、沉淀硫酸钡10份、硅灰石粉10份、纳米级气相白炭黑10份、去离子水25份。
实施例5
本发明的纺织品用隔热保温涂料的一个优选方案，含有以下重量份比的组分：天然橡胶30份、水性环氧树脂8份、水性酚醛树脂8份、邻苯二甲酸二丁酯4.5份、三乙醇胺1份、聚丙烯酸钠盐1份、六偏磷酸钠1份、金红石钛白粉20份、纳米级气相白炭黑10份、去离子水25份。
将上述1-5实施例的隔热保温涂料各组分经溶解、混合、改性、研磨、过滤后，得到本发明的纺织品用隔热保温涂料。
性能测试实验：对实施例1-5制备的纺织品用隔热保温涂料进行性能测试，测试结果见下表
Figure 2012101378225100002DEST_PATH_IMAGE002
利用实施例1-5制备的涂料300g制成的涂层分别进行以下功能试验：
耐人工老化试验：（参照标准GB/T1865-1997）在人工耐老化仓内进行耐老化性能测试，以购得性能较好的水性乳胶涂料作为对照，对照样品耐老化处理600h有褪色现象，而本发明的测试样品耐老化处理1000h漆膜无变化。
隔热温差测试：把涂料涂在0.5×0.5×0.5m的帐篷外表面上，漆膜厚度为100μm。把涂刷的测试帐篷和参考帐篷（涂刷普通隔热涂料）分别放在碘钨灯灯泡下垂直照射30min，调节灯泡与帐篷顶部的距离，使帐篷顶部表面温度30min内达到60℃。测试完毕后，分别记录测试帐篷和参考帐篷内部的温度。结果显示，测试帐篷的内部温度比参考帐篷的内部温度低（15±2）℃，说明本发明的纺织品用隔热保温涂料具有显著的隔热效果 。

Claims (7)

1.一种纺织品用隔热保温涂料，其特征在于：其含有天然橡胶30～50重量份、水性环氧树脂2～8重量份、水性酚醛树脂1～8重量份、成膜助剂4.5～12.5重量份、分散剂1～4重量份、颜填料30～55重量份、水20～25重量份。
2.根据权利要求1所述的一种纺织品用隔热保温涂料，其特征在于：所述成膜助剂为邻苯二甲酸二丁酯、苯甲醇和正丁醛苯胺缩合物中的任意一种或一种以上的组合。
3.根据权利要求1所述的一种纺织品用隔热保温涂料，其特征在于：所述分散剂为三乙醇胺、六偏磷酸钠、聚丙烯酸钠盐中的任意一种或一种以上的组合。
4.根据权利要求1所述的一种纺织品用隔热保温涂料，其特征在于：所述颜填料为金红石钛白粉、沉淀硫酸钡、硅灰石粉和白炭黑中的任意一种或一种以上的组合。
5.根据权利要求1所述的一种纺织品用隔热保温涂料，其特征在于：所述成膜助剂由邻苯二甲酸二丁酯2～6重量份、苯甲醇2～6重量份、正丁醛苯胺缩合物0.1～0.5重量份组成。
6.根据权利要求1所述的一种纺织品用隔热保温涂料，其特征在于：所述颜填料由金红石钛白粉15～25重量份、沉淀硫酸钡10～20重量份、白炭黑3～10重量份组成。
7.根据权利要求4或6所述的一种纺织品用隔热保温涂料，其特征在于：所述白炭黑为纳米级气相白炭黑。
CN2012101378225A 2011-05-23 2012-05-07 一种纺织品用隔热保温涂料 Expired - Fee Related CN102720069B (zh)