CN102718966A - 一种电化学合成氧化钴/聚苯胺复合材料的制备方法 - Google Patents

一种电化学合成氧化钴/聚苯胺复合材料的制备方法 Download PDF

Info

Publication number
CN102718966A
CN102718966A CN2012102165688A CN201210216568A CN102718966A CN 102718966 A CN102718966 A CN 102718966A CN 2012102165688 A CN2012102165688 A CN 2012102165688A CN 201210216568 A CN201210216568 A CN 201210216568A CN 102718966 A CN102718966 A CN 102718966A
Authority
CN
China
Prior art keywords
mixing solutions
composite material
polyaniline composite
vitriolic
electrochemical synthesis
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012102165688A
Other languages
English (en)
Other versions
CN102718966B (zh
Inventor
郝建军
林雪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangzhou Power Surface Treatment Technology Co Ltd
Original Assignee
Shenyang Ligong University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shenyang Ligong University filed Critical Shenyang Ligong University
Priority to CN201210216568.8A priority Critical patent/CN102718966B/zh
Publication of CN102718966A publication Critical patent/CN102718966A/zh
Application granted granted Critical
Publication of CN102718966B publication Critical patent/CN102718966B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种电化学合成氧化钴/聚苯胺复合材料的制备方法，包括下述工艺步骤：分别取0.1mol/L苯胺和0.5mol/L硫酸的混合溶液与0.1mol/L硫酸钴和0.5mol/L硫酸的混合溶液按照1:2的比例混合，用硫酸调节混合溶液的pH值到1.0～2.0，添加十六烷基三甲基溴化铵0.3g/L，用磁力搅拌器进行搅拌，在恒电位为1.5～5.0V，温度为10～25℃下，电聚合3～15min，即得。本发明可在导电玻璃、不锈钢表面得到均匀、致密、耐蚀性优良的氧化钴/聚苯胺复合材料。

Description

一种电化学合成氧化钴/聚苯胺复合材料的制备方法
技术领域
本发明属于新材料制备的技术领域，涉及一种电化学合成氧化钴/聚苯胺复合材料的制备方法。
背景技术
聚苯胺是一种高分子合成材料。它具有许多优良的性能，可用作隐身材料、防腐材料，抗静电材料、电子化学品等。其作用主要体现在（1）、可提高基体材料的耐腐蚀性；（2）、提高基体材料与后续处理涂层间的附着力；（3）、具有高化学稳定性；（4）、具有较好的导电性能，可以吸收微波，还可以用来作为检测空气中氮氧化物的含量的材料以及H2S，SO2等有害气体的含量。
电化学合成聚苯胺的方法有很多优点：（1）、在常温常压下就能够进行合成，并且合成方法简单好做。（2）、聚合的时间短，能够减少更多的时间。（3）、整个实验过程短，克服了多步合成的缺点。（4）、聚苯胺的合成-掺杂-成膜可以点在工作电极上一步完成，膜厚也可以通过聚合时间、聚合电位、电流密度来决定。（5）、反应过程中容易控制。（6）、原料和产物都是无毒无害的，是环保型工艺。（7）、通过改变工艺参数和电解液种类可以制备出具有不同性能不同结构的聚苯胺膜层，来适应不同用途的要求。（8）、在反应过程中需要的苯胺单体少，并且直接基体上电沉积，避免了大量的有机溶剂挥发，从而做到无污染生产。但不适合大量生产。
发明内容
本发明的目的，是提供一种电化学合成氧化钴/聚苯胺复合材料的制备方法，能够得到耐腐蚀性能优良的复合材料。
采用的技术方案是：
一种电化学合成氧化钴/聚苯胺复合材料的制备方法，包括下述工艺步骤：
分别取0.1mol/L苯胺和0.5mol/L硫酸的混合溶液与0.1mol/L硫酸钴和0.5mol/L硫酸的混合溶液按照1:2的比例混合，向混合溶液中加入硫酸，调节混合溶液的pH值到1.0～2.0，然后向该混合溶液中添加十六烷基三甲基溴化铵0.3g/L，用磁力搅拌器进行搅拌，在温度为10～25℃下，恒电位为1.5～5.0V，将除油、除锈后的不锈钢片或导电玻璃片放入电解液中电聚合3～15min，即得。
本发明的优点在于：
本发明采用在常温下将苯胺-硫酸溶液和硫酸钴-硫酸溶液按一定比例混合作为基础液，加入添加剂，用磁力搅拌器进行搅拌，能够电化学合成得到的复合材料薄膜层均匀、细致，表面光滑，耐蚀性能优良的氧化钴/聚苯胺复合材料。
具体实施方式
实施例1
一种电化学合成氧化钴/聚苯胺复合材料的制备方法，包括下述工艺步骤：
分别取0.1mol/L苯胺和0.5mol/L硫酸的混合溶液与0.1mol/L硫酸钴和0.5mol/L硫酸的混合溶液按照1:2的比例混合，向混合溶液中加入硫酸，调节混合溶液的pH值到1.5，然后向该混合溶液中添加十六烷基三甲基溴化铵0.3g/L，用磁力搅拌器进行搅拌，在温度为25℃下，恒电位为1.5V，将除油、除锈后的不锈钢片放入电解液中电聚合6min，即得。
实施例2
一种电化学合成氧化钴/聚苯胺复合材料的制备方法，包括下述工艺步骤：
分别取0.1mol/L苯胺和0.5mol/L硫酸的混合溶液与0.1mol/L硫酸钴和0.5mol/L硫酸的混合溶液按照1:2的比例混合，向混合溶液中加入硫酸，调节混合溶液的pH值到2.0，然后向该混合溶液中添加十六烷基三甲基溴化铵0.3g/L，用磁力搅拌器进行搅拌，在温度为10℃下，恒电位为3.0V，将除油、除锈后的导电玻璃片放入电解液中电聚合15 min，即得。
实施例3
一种电化学合成氧化钴/聚苯胺复合材料的制备方法，包括下述工艺步骤：
分别取0.1mol/L苯胺和0.5mol/L硫酸的混合溶液与0.1mol/L硫酸钴和0.5mol/L硫酸的混合溶液按照1:2的比例混合，向混合溶液中加入硫酸，调节混合溶液的pH值到1.0，然后向该混合溶液中添加十六烷基三甲基溴化铵0.3g/L，用磁力搅拌器进行搅拌，在温度为20℃下，恒电位为5.0V，将除油、除锈后的不锈钢片放入电解液中电聚合3 min，即得。

Claims (4)

1.一种电化学合成氧化钴/聚苯胺复合材料的制备方法，其特征在于包括下述工艺步骤：
分别取0.1mol/L苯胺和0.5mol/L硫酸的混合溶液与0.1mol/L硫酸钴和0.5mol/L硫酸的混合溶液按照1:2的比例混合，向混合溶液中加入硫酸，调节混合溶液的pH值到1.0～2.0，然后向该混合溶液中添加十六烷基三甲基溴化铵0.3g/L，用磁力搅拌器进行搅拌，在温度为10～25℃下，恒电位为1.5～5.0V，将除油、除锈后的不锈钢片或导电玻璃片放入电解液中电聚合3～15min，即得。
2.根据权利要求1所述的一种电化学合成氧化钴/聚苯胺复合材料的制备方法，其特征在于包括下述工艺步骤：
分别取0.1mol/L苯胺和0.5mol/L硫酸的混合溶液与0.1mol/L硫酸钴和0.5mol/L硫酸的混合溶液按照1:2的比例混合，向混合溶液中加入硫酸，调节混合溶液的pH值到1.5，然后向该混合溶液中添加十六烷基三甲基溴化铵0.3g/L，用磁力搅拌器进行搅拌，在温度为25℃下，恒电位为1.5V，将除油、除锈后的不锈钢片放入电解液中电聚合6min，即得。
3.根据权利要求1所述的一种电化学合成氧化钴/聚苯胺复合材料的制备方法，其特征在于包括下述工艺步骤：
分别取0.1mol/L苯胺和0.5mol/L硫酸的混合溶液与0.1mol/L硫酸钴和0.5mol/L硫酸的混合溶液按照1:2的比例混合，向混合溶液中加入硫酸，调节混合溶液的pH值到2.0，然后向该混合溶液中添加十六烷基三甲基溴化铵0.3g/L，用磁力搅拌器进行搅拌，在温度为10℃下，恒电位为3.0V，将除油、除锈后的导电玻璃片放入电解液中电聚合15 min，即得。
4.根据权利要求1所述的一种电化学合成氧化钴/聚苯胺复合材料的制备方法，其特征在于包括下述工艺步骤：
分别取0.1mol/L苯胺和0.5mol/L硫酸的混合溶液与0.1mol/L硫酸钴和0.5mol/L硫酸的混合溶液按照1:2的比例混合，向混合溶液中加入硫酸，调节混合溶液的pH值到1.0，然后向该混合溶液中添加十六烷基三甲基溴化铵0.3g/L，用磁力搅拌器进行搅拌，在温度为20℃下，恒电位为5.0V，将除油、除锈后的不锈钢片放入电解液中电聚合3 min，即得。
CN201210216568.8A 2012-06-28 2012-06-28 一种电化学合成氧化钴/聚苯胺复合材料的制备方法 Active CN102718966B (zh)