CN102702732A - 一种pa/pc/ppo三元合金及其制备方法 - Google Patents

一种pa/pc/ppo三元合金及其制备方法 Download PDF

Info

Publication number
CN102702732A
CN102702732A CN2012101968608A CN201210196860A CN102702732A CN 102702732 A CN102702732 A CN 102702732A CN 2012101968608 A CN2012101968608 A CN 2012101968608A CN 201210196860 A CN201210196860 A CN 201210196860A CN 102702732 A CN102702732 A CN 102702732A
Authority
CN
China
Prior art keywords
ppo
ternary alloy
parts
compatilizer
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012101968608A
Other languages
English (en)
Inventor
王晶
王凯
张天荣
王健
张陆旻
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
KUNSHAN JUWEI ENGINEERING PLASTIC CO LTD
Original Assignee
KUNSHAN JUWEI ENGINEERING PLASTIC CO LTD
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by KUNSHAN JUWEI ENGINEERING PLASTIC CO LTD filed Critical KUNSHAN JUWEI ENGINEERING PLASTIC CO LTD
Priority to CN2012101968608A priority Critical patent/CN102702732A/zh
Publication of CN102702732A publication Critical patent/CN102702732A/zh
Pending legal-status Critical Current

Abstract

本发明属于复合材料领域,具体涉及一种PA/PC/PPO三元合金,其组成为:PA 40~65份;PC 15~20份;PPO 15~30份;相容剂0.5~1份,其他加工助剂0.5~1份。制备采用双螺杆挤出工艺。本发明中在采用相容剂的基础上,主要利用了PPO对PA和PC的反应增容原理,得到了性能优异的PA/PC/PPO三元合金。

Description

一种PA/PC/PPO三元合金及其制备方法
技术领域
本发明属于复合材料领域,具体涉及一种PA/PC/PPO三元合金及其制备方法。 
背景技术
尼龙(PA)是一种性能优异的工程塑料,使得其具有耐溶剂性好,力学强度高,易加工等优点。但其存在冲击强度低、耐热性较差、因高吸水性造成的制品尺寸稳定性差等缺点使其在很多领域的应用受到限制; 
聚碳酸酯( PC)具有突出的抗冲性能和抗蠕变性能,耐寒、耐热性好,吸水率低,制品尺寸稳定。但也存在着加工流动性差、耐溶剂性能差、易应力开裂以及对缺口敏感等缺陷。  
聚苯醚(PPO)具有良好的热力学能,它可在160℃~190℃的范围内连续工作,高温下的耐蠕变性在工程塑料中较为优异。
 PA/PC/PPO共混得到的合金材料既有良好的加工性能,耐溶剂性,冲击性能,尺寸稳定性和较高的耐热性。但PA与另外两种材料的相容性差,严重影响了合金的力学性能,限制了其使用。PC的溶解度参数为9.8,PA的溶解度参数为12.7~13.6,PPO的溶解度参数为9.0,PC、PPO溶解度参数较为接近,可以达到部分相容。PA6与PC、PPO共混体系是热力学不相容体系,之间因界面张力大,界面粘结力弱,导致分散状况不好,共混物力学性能差。 
发明内容
本发明的目的是解决PA/PC/PPO之间相容性的问题,提高复合材料的力学性能。 
为实现上述目的,本发明利用PPO对PA和PC的反应增容,同时使用相容剂对三元合金材料增容改性,降低了材料的界面张力,增加了相容性,提高了合金材料的力学性能,使材料有更高的实用性。 
本发明采取的具体技术方案如下: 
一种PA/PC/PPO三元合金,以重量份计,其组成为:
PA                  40~65份
PC                  15~20份
PPO                 15~30份            
相容剂               0.5~1份
加工助剂             0.5~1份
其中,所述PA为PA6;所述PC,其分子量为30000~45000;所述PPO,其特性粘度为0.2~0.5dl/g;所述相容剂由SEBS-g-MA 、PPO-g-MA、SMA中的一种或几种组成,所述加工助剂为润滑剂和抗氧剂。
上述PA/PC/PPO三元合金的制备方法的技术方案包括以下步骤: 
本发明的制备工艺为:首先将各组分按照配方含量充分混合均匀,经双螺杆挤出机挤出造粒,其中双螺杆挤出机温度区间为230-260℃,注塑温度270-285℃,模具温度80-100℃,压力30-60MPa,速度10-15%。
本发明中在采用相容剂的基础上,主要利用了PPO对PA和PC的反应增容原理,得到了性能优异的PA/PC/PPO三元合金,主要有益效果如下: 
1、本发明材料,保持了PA和PC原有的优异性能,同时又加入了PPO,得到合金材料耐热性能好、耐溶剂性优异,尺寸稳定、又保持了原有的力学性能等优点; 
2、PPO在挤出过程中,分子中的氧原子与PA6及PC上的氢原子作用形成氢键而增容PA和PC,对PA、PC、PPO三者之间的增容起到了协同作用。
具体实施方式
下面结合实施例,对本发明作进一步的描述。 
实施例1~5 
  PA  PC PPO 相容剂 加工助剂
实施例1 73.7 15 10 0.5 0.8
实施例2 68.7 15 15 0.5 0.8
实施例3 68.4 20 10 0.8 0.8
实施例4 63.4 20 15 0.8 0.8
实施例5 63.2 20 15 1 0.8
将上述实施例,各组分物料加入到双螺杆挤出机的料斗中,经熔融共混,挤出造粒成复合材料,其中双螺杆挤出机温度区间为230-260℃,注塑温度270-285℃,模具温度80-100℃,压力30-60MPa,速度10-15%。
实施例1~5的材料性能见下表所示: 
Figure 759854DEST_PATH_IMAGE001

Claims (1)

1.一种PA/PC/PPO三元合金,以重量份计,其组成为:
PA                  40~65份
PC                  15~20份
PPO                 15~30份            
相容剂               0.5~1份
加工助剂             0.5~1份
所述PA为PA6;所述PC,其分子量为30000~45000;所述PPO,其特性粘度为0.2~0.5dl/g;所述相容剂由SEBS-g-MA 、PPO-g-MA、SMA中的一种或几种组成,所述加工助剂为润滑剂和抗氧剂。
CN2012101968608A 2012-06-15 2012-06-15 一种pa/pc/ppo三元合金及其制备方法 Pending CN102702732A (zh)