CN102675987A - 一种易施工的单组分透明木器修色剂及其制备方法 - Google Patents
一种易施工的单组分透明木器修色剂及其制备方法 Download PDFInfo
- Publication number
- CN102675987A CN102675987A CN2012101660372A CN201210166037A CN102675987A CN 102675987 A CN102675987 A CN 102675987A CN 2012101660372 A CN2012101660372 A CN 2012101660372A CN 201210166037 A CN201210166037 A CN 201210166037A CN 102675987 A CN102675987 A CN 102675987A
- Authority
- CN
- China
- Prior art keywords
- dressing agent
- solution
- woodenware
- ketone resin
- monobutyl ether
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种易施工的单组分透明木器修色剂及其制备方法,该修色剂含有如下重量百分比组分:有机溶剂80~87%,醛酮树脂1.8~3%,醋酸酯类溶剂1.2~2%,色精溶液10~15%,其中,色精溶液由色精溶于有机溶剂得到,其质量浓度为0.01~49%。本发明的单组分透明木器修色剂,经检测和试用证明,其着色力好、不影响涂层附着力;施工时,气味低、易施工,施工时无需喷涂操作,仅由普通人员刷涂操作即可;尤其是施工后木材纹理清晰、立体层次感效果好、着色效果也可由施工人员轻松掌握、施工方便快捷。
Description
技术领域
本发明涉及一种木器涂料,具体涉及一种易施工的单组分透明木器修色剂及其制备方法。
背景技术
家装市场的家具、门窗等一般采用实木或胶合板制成,实木因是自然生长,表面有一事实上的色差;胶合板因为是人工合成,表面纹理生硬,颜色呆滞。为了解决上述问题,一般会对家具、门窗等木器表面进行修色。修色是一种常见的涂装形式,尤其是透明修色,在木器表面涂上透明有色修色剂后,即改变了木器颜色,又能看到木器纹理,其不仅可以通过底着色显露出木纹纹路,还可以通过底色和面色的色差体现出层次感,在对木器保护的同时,赋予了木器极大的美感,达到了极佳的装饰效果。
PU漆是所有聚酯涂料的统称,PU透明有色漆是一种美化性能优良的木器涂料,由于其突出的保护和装饰性能,目前被广泛用于木器装色,但是PU透明有色漆的施工艺要求喷涂、刷涂,技术含量高,工序烦琐,在施工时,需要有着良好的喷涂技术及对色彩敏感的判断力,稍不注意就会造成色差且不易返工修复,因施工技术限制,所以局限于专业的油漆师傅使用,不利于大面积推广,而且容易产生不均匀,凹凸部分表面无法喷涂均匀,造成色差,影响装饰效果。
发明内容
本发明的目的在于提供一种易施工的单组分透明木器修色剂。
本发明所采用的技术方案是:
一种易施工的单组分透明木器修色剂,由如下重量百分比的组分组成:
有机溶剂80~87%,
醛酮树脂1.8~3%,
醋酸酯类溶剂1.2~2%,
色精溶液10~15%,
其中,色精溶液由色精溶于有机溶剂得到,其质量浓度为0.01~49wt%。
优选的,所述有机溶剂独立的选自乙二醇单丁醚、丁基卡必醇中的一种,或乙二醇单丁醚、丁基卡必醇中的一种与多元醇二元酯(EGDA)、DBE(高沸点酯类溶剂)中的至少一种的混合物。
优选的,所述有机溶剂均为乙二醇单丁醚。
优选的,醋酸酯类溶剂为醋酸丁酯。
上述的易施工的单组分透明木器修色剂的制备方法,包括以下步骤:
1) 将醛酮树脂溶于醋酸酯类溶剂中,搅拌均匀,得醛酮树脂溶液;
2) 将醛酮树脂溶液、色精溶液、有机溶剂混合,搅拌均匀,得易施工的透明木器修色剂。
本发明的醛酮树脂可选自 BASF A-81、岳阳科立孚合成材料有限公司生厂的CR-A81树脂。本发明的醛酮树脂也可用其它的同类型的产品替代。
本发明的有益效果是:
本发明的单组分透明木器修色剂,经检测和试用证明,其着色力好、不影响涂层附着力;施工时,气味低、易施工,施工时无需喷涂操作,仅由普通人员刷涂操作即可;尤其是施工后木材纹理清晰、立体层次感效果好、着色效果也可由施工人员轻松掌握、施工方便快捷。
本发明的透明木器修色剂降低了施工技术难度,是专门针对木器修色(上色、着色)所设计的一款较为简单快捷且施工容易的修色、着色产品,适用各种材质木料面板修色(着色、上色),使用后木材面板纹理清晰自然,层次感较强,能大幅度美化家具装修效果档次。
具体实施方式
下面结合具体的实施例对本发明作进一步的说明,但并不局限如此。
实施例中黑色精为台湾公隆化学股份有限公司生产,型号:820S色精;红色精为台湾公隆化学股份有限公司生产,型号:306S色精;黄色精为台湾公隆化学股份有限公司生产,型号:120S色精。
以下所述百分比均为重量百分比。
实施例1
一种易施工的单组分透明木器修色剂(黑胡桃色),含有如下重量百分比组分:
乙二醇单丁醚84.5 %,
醛酮树脂3 %,
醋酸丁酯2%,
黑色精溶液6.2 %,
红色精溶液0.4 %,
黄色精溶液3.9 %;
其中,红色精溶液、黑色精溶液、黄色精溶液的质量浓度均为45%。
上述单组分透明木器修色剂的制备方法,包括以下步骤:
1) 将黑色精、红色精、黄色精分别溶于乙二醇单丁醚,分别制成红色精溶液、黑色精溶液、黄色精溶液;
2) 将醛酮树脂溶于醋酸酯类溶剂中,搅拌均匀,得醛酮树脂溶液;
3) 将醛酮树脂溶液、不同颜色的色精溶液、乙二醇单丁醚按比例混合,搅拌均匀,得易施工的透明木器修色剂。
实施例2
一种易施工的单组分透明木器修色剂(黑棕色),含有如下重量百分比组分:
乙二醇单丁醚84.5 %,
醛酮树脂1.8 %,
醋酸丁酯1.2%,
黑色精溶液5.7 %,
红色精溶液4.6 %,
黄色精溶液2.2 %;
其中,黑色精溶液、红色精溶液、黄色精溶液的质量浓度均为40%。
制备方法同实施例1。
上述单组分透明木器修色剂的制备方法,包括以下步骤:
1) 将黑色精、红色精、黄色精分别溶于丁基卡必醇,分别制成红色精溶液、黑色精溶液、黄色精溶液;
2) 将醛酮树脂溶于醋酸酯类溶剂中,搅拌均匀,得醛酮树脂溶液;
3) 将醛酮树脂溶液、不同颜色的色精溶液、乙二醇单丁醚按比例混合,搅拌均匀,得易施工的透明木器修色剂。
实施例3
一种易施工的单组分透明木器修色剂(红木色),含有如下重量百分比组分:
乙二醇单丁醚67.7 %,
多元醇二元酯(EGDA)15 %,
醛酮树脂3 %,
醋酸丁酯2%
黑色精溶液1 %,
红色精溶液8 %,
黄色精溶液3.3 %;
其中,黑色精溶液、红色精溶液、黄色精溶液的质量浓度均为20%。
上述单组分透明木器修色剂的制备方法,包括以下步骤:
1) 将黑色精、红色精、黄色精分别溶于乙二醇单丁醚,分别制成红色精溶液、黑色精溶液、黄色精溶液;
2) 将醛酮树脂溶于醋酸酯类溶剂中,搅拌均匀,得醛酮树脂溶液;
3) 将醛酮树脂溶液、不同颜色的色精溶液、乙二醇单丁醚按比例混合,搅拌均匀,得易施工的透明木器修色剂。
实施例4
一种易施工的单组分透明木器修色剂,含有如下重量百分比组分:
乙二醇单丁醚87 %,
醛酮树脂1.8 %,
醋酸丁酯1.2%
黑色精溶液2 %,
红色精溶液5 %,
黄色精溶液3 %;
其中,黑色精溶液、红色精溶液、黄色精溶液的质量浓度均为49%。
制备方法同实施例1。
实施例5
一种易施工的单组分透明木器修色剂,含有如下重量百分比组分:
乙二醇单丁醚80 %,
醛酮树脂3 %,
醋酸丁酯2%
红色精溶液15%;
其中,红色精溶液的质量浓度均为0.01%。
上述单组分透明木器修色剂的制备方法,包括以下步骤:
1) 将红色精溶于乙二醇单丁醚,制成红色精溶液;
2) 将醛酮树脂溶于醋酸酯类溶剂中,搅拌均匀,得醛酮树脂溶液;
3) 将醛酮树脂溶液、红色精溶液、乙二醇单丁醚按比例混合,搅拌均匀,即可。
实施例6
一种易施工的单组分透明木器修色剂,含有如下重量百分比组分:
乙二醇单丁醚85 %,
醛酮树脂2.4 %,
醋酸丁酯1.6%
红色精溶液5 %,
黄色精溶液6 %;
其中,红色精溶液、黄色精溶液的质量浓度均为20%。
上述单组分透明木器修色剂的制备方法,包括以下步骤:
1) 将红色精、黄色精分别溶于乙二醇单丁醚,分别制成红色精溶液、黄色精溶液;
2) 将醛酮树脂溶于醋酸酯类溶剂中,搅拌均匀,得醛酮树脂溶液;
3) 将醛酮树脂溶液、红色精溶液、黄色精溶液、乙二醇单丁醚按比例混合,搅拌均匀,即可。
采用本发明的单组分透明木器修色剂进行施工:按木器透明底漆正常施工流程,将木器表面涂刷打磨后清理漆面灰尘,均匀涂一遍底漆,无须打磨,待表面实干后均匀连续性涂刷相关色系的本发明的单组分透明木器修色剂,3~5分钟后,使用棉布按涂刷修色剂时的涂刷顺序,均匀连续性擦拭至干燥,然后进行木器透明面漆涂刷。本发明的透明木器修色剂施工时无需喷涂施工,可由普通人员刷涂操作施工。
将实施例1的修色剂按上述方法施工后的效果和市售的两种修色剂(样品A、样品B)施工后的效果见表1,其中的附着力检测参照GB/T23997-2009,由表可知,本发明的单组分透明木器修色剂施工后漆膜无脱层、跑油现象,且附着力为一级,优于市售产品。
Claims (5)
1.一种易施工的单组分透明木器修色剂,由如下重量百分比的组分组成:
有机溶剂80~87%,
醛酮树脂1.8~3%,
醋酸酯类溶剂1.2~2%,
色精溶液10~15%,
其中,色精溶液由色精溶于有机溶剂得到,其质量浓度为0.01~49%。
2.根据权利要求1所述的易施工的单组分透明木器修色剂,其特征在于:所述有机溶剂独立的选自乙二醇单丁醚、丁基卡必醇中的一种,或乙二醇单丁醚、丁基卡必醇中的一种与多元醇二元酯(EGDA)、DBE中的至少一种的混合物。
3.根据权利要求2所述的易施工的单组分透明木器修色剂,其特征在于:所述有机溶剂均为乙二醇单丁醚。
4.根据权利要求1所述的易施工的单组分透明木器修色剂,其特征在于:醋酸酯类溶剂为醋酸丁酯。
5.权利要求1所述的易施工的单组分透明木器修色剂的制备方法,包括以下步骤:
1)将醛酮树脂溶于醋酸酯类溶剂中,搅拌均匀,得醛酮树脂溶液;
2)将醛酮树脂溶液、色精溶液、有机溶剂混合,搅拌均匀,得易施工的透明木器修色剂。