CN102675659A - 工件防锈乳液的制备方法 - Google Patents

工件防锈乳液的制备方法 Download PDF

Info

Publication number
CN102675659A
CN102675659A CN2011100640593A CN201110064059A CN102675659A CN 102675659 A CN102675659 A CN 102675659A CN 2011100640593 A CN2011100640593 A CN 2011100640593A CN 201110064059 A CN201110064059 A CN 201110064059A CN 102675659 A CN102675659 A CN 102675659A
Authority
CN
China
Prior art keywords
workpiece
emulsion
weight parts
preparation
kilograms
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011100640593A
Other languages
English (en)
Inventor
陈云红
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2011100640593A priority Critical patent/CN102675659A/zh
Publication of CN102675659A publication Critical patent/CN102675659A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种工件防锈乳液的制备方法，由油酸15-20份、聚乙烯醇5-8份、石油磺酸钡4-6份、石蜡3-5份、三乙醇胺2.5-4份、烷基酚聚氧乙烯醚1.2-1.5份、纯水55-65份配制而成，本发明制备的工件防锈液无毒、无味，能使浸液的工件由于水分的蒸发快速干燥，无油渍渗出现象。

Description

工件防锈乳液的制备方法
技术领域
本发明属于精细化工领域，涉及一种防锈乳液，具体涉及一种工件防锈乳液的制备方法。
背景技术
工件磷化处理后一般都需要除油漆、浸油，但浸油处理后，表面附着的油膜很易吸附尘埃，形成不均匀的污点，影响表观质量。此外，油墨不易干燥，即便用手工清除多余的油珠，以后还会有油渗出。机动车用的离合器零件经磷化浸油处理，虽用手工擦去表面的污迹，但装配后，铆钉周围仍会有油迹，油如渗到石棉摩擦片上，使用时，会发生打滑现象。
发明内容
发明目的：本发明的目的是为解决现有技术的不足，提供一种工件防锈乳液的制备方法。
本发明采用的技术方案：一种工件防锈乳液的制备方法，所述工件防锈乳液的具体制备步骤为：
(1)将石蜡3-5份、油酸15-20份及石油磺酸钡4-6份物料置于容器中，在70-75℃温度下不断搅拌使其充分互溶；
(2)再加入三乙醇胺2.5-4份和烷基酚聚氧乙烯醚1.2-1.5份，继续搅拌至形成均匀粘稠物；
(3)再将聚乙烯醇5-8份加入55-65份纯水中于90-95℃度下不断搅拌使其溶解成透明溶液，至冷却到40-45℃后将此溶液在不断搅拌下加入到步骤(2)所述的物料中，所得乳白色乳液即为工件防锈乳液。
在本发明中，三乙醇胺、烷基酚聚氧乙烯醚用作乳化剂，聚乙烯醇用作粘合剂，石蜡用作油酸和石油磺酸钡的助溶剂。
有益效果：本发明制备的工件防锈液无毒、无味，能使浸液的工件由于水分的蒸发快速干燥，无油渍渗出现象。
具体实施方式：
实施例1
一种工件防锈乳化液的制备方法：
(1)将石蜡3千克、油酸15千克及石油磺酸钡4千克物料置于容器中，在70℃温度下不断搅拌使其充分互溶；
(2)再加入三乙醇胺2.5千克和烷基酚聚氧乙烯醚1.2千克，继续搅拌至形成均匀粘稠物；
(3)再将聚乙烯醇5千克加入55千克纯水中于90℃度下不断搅拌使其溶解成透明溶液，至冷却到40℃后将此溶液在不断搅拌下加入到步骤(2)所述的物料中，所得乳白色乳液即为工件防锈乳液。
实施例2
(1)将石蜡4千克、油酸18千克及石油磺酸钡5千克物料置于容器中，在75℃温度下不断搅拌使其充分互溶；
(2)再加入三乙醇胺3千克和烷基酚聚氧乙烯醚1.5千克，继续搅拌至形成均匀粘稠物；
(3)再将聚乙烯醇6千克加入60千克纯水中于95℃度下不断搅拌使其溶解成透明溶液，至冷却到45℃后将此溶液在不断搅拌下加入到步骤(2)所述的物料中，所得乳白色乳液即为工件防锈乳液。
实施例3
(1)将石蜡5千克、油酸20千克及石油磺酸钡6千克物料置于容器中，在75℃温度下不断搅拌使其充分互溶；
(2)再加入三乙醇胺4千克和烷基酚聚氧乙烯醚1.5千克，继续搅拌至形成均匀粘稠物；
(3)再将聚乙烯醇8千克加入65千克纯水中于95℃度下不断搅拌使其溶解成透明溶液，至冷却到45℃后将此溶液在不断搅拌下加入到步骤(2)所述的物料中，所得乳白色乳液即为工件防锈乳液。

Claims (1)

1.一种工件防锈乳液的制备方法，其特征在于：所述工件防锈乳液的具体制备步骤包括：
(1)将石蜡3-5份、油酸15-20份及石油磺酸钡4-6份物料置于容器中，在70-75℃温度下不断搅拌使其充分互溶；
(2)再加入三乙醇胺2.5-4份和烷基酚聚氧乙烯醚1.2-1.5份，继续搅拌至形成均匀粘稠物；
(3)再将聚乙烯醇5-8份加入55-65份纯水中于90-95℃度下不断搅拌使其溶解成透明溶液，至冷却到40-45℃后将此溶液在不断搅拌下加入到步骤(2)所述的物料中，所得乳白色乳液即为工件防锈乳液。
CN2011100640593A 2011-03-16 2011-03-16 工件防锈乳液的制备方法 Pending CN102675659A (zh)