CN102649095A - 一种钛白粉的研磨方法 - Google Patents
一种钛白粉的研磨方法 Download PDFInfo
- Publication number
- CN102649095A CN102649095A CN2011100445317A CN201110044531A CN102649095A CN 102649095 A CN102649095 A CN 102649095A CN 2011100445317 A CN2011100445317 A CN 2011100445317A CN 201110044531 A CN201110044531 A CN 201110044531A CN 102649095 A CN102649095 A CN 102649095A
- Authority
- CN
- China
- Prior art keywords
- product
- white powder
- titanium white
- primary
- titanium dioxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明实施例公开了一种钛白粉的研磨方法，该方法包括如下步骤：一级操作：将钛白粉原料投入一级水磨设备进行研磨，得到一级产品；将所述一级产品进行分离，得到一级分离颗粒；二级操作：将所述一级分离颗粒继续投入二级水磨设备进行研磨，得到二级产品；将所述二级产品再次进行分离，得到二级分离颗粒；继续进行下一级操作，直至最终得到标准级产品。通过上述对钛白粉反复水磨分离，使得钛白粉由粗颗粒细化到细度为1.5微米以内的细颗粒，大大提高了产品的利用率，降低了生产成本，节约了钛矿资源，同时也提高了产品的应用性能。
Description
技术领域
本发明属于钛白粉生产领域，具体涉及一种钛白粉的研磨方法。
背景技术
钛白粉学名二氧化钛(TiO2)，是一种白色无机颜料，具有无毒、最佳的不透明度和光亮度，被认为是世界上性能最好的一种白色颜料，广泛应用于涂料、塑料、造纸、印刷油墨、化纤、橡胶、化妆品及食品添加剂和医疗等工业。
钛白粉细度的粒度分布是一个重要的综合性指标，严重影响着钛白粉的颜料性能和产品的应用效果。而影响钛白粉细度的粒度分布的因素也很多，其中，对原料产品的研磨便是其中重要的一条。
当前，业内对钛白粉原料的研磨都是通过水磨机等相关的研磨设备直接进行连续的研磨，其所得到的成品细度粒度分布不均匀，粗颗粒所占比例较大，这样就不利于钛白粉的利用率，增加了使用量，浪费了钛矿资源，同时，也影响了钛白粉的应用效果。
发明内容
有鉴于此，本发明提供了一种钛白粉的研磨方法，使得钛白粉由粗颗粒细化到细度为1.5微米以内的细颗粒，大大提高了产品的利用率，降低了生产成本，提高了钛白粉的应用效果，同时对钛矿资源的节约和可持续发展作出了贡献。
为实现上述技术问题，本发明提供如下技术方案：一级操作：
将钛白粉原料投入一级水磨设备进行研磨，得到一级产品；
将所述一级产品进行分离，得到一级分离颗粒；
二级操作：
将所述一级分离颗粒继续投入二级水磨设备进行研磨，得到二级产品；
将所述二级产品再次进行分离，得到二级分离颗粒；
继续进行下一级操作，直至最终得到标准级产品。
优选地，所述操作包括12级操作。
优选的，所述得到标准级产品之后还包括喷雾干燥处理、产品检验。
优选的，所述标准级产品为细度在1.5微米以内的钛白粉产品。
本发明公开了一种钛白粉的研磨方法，是通过连续进行多级的水磨和分离操作实现，使得钛白粉颗粒在多级操作下逐级地过滤掉相对较粗的颗粒，对相对的细颗粒继续进行研磨，最后得到粒度分布均匀的标准级产品。本发明所公开的研磨方法由于在其研磨过程中加入了多级的分离操作，使得产品细度能够达到1-1.5微米之内，粒度分布均匀，甚至能够达到1微米之内的细度，极大地提高了产品的利用率，使其使用量相对于现有的钛白粉产品的使用量能够减少30-40％，降低了成本，节约了钛矿资源，同时由于粒度变细，也极大地提高了产品的应用性能。
附图说明
图1为本发明实施例所公开的一种钛白粉的研磨方法的工序流程示意图；
图2为本发明实施例所公开的一种钛白粉的研磨方法的产品粒度分布曲线示意图。
具体实施方式
下面结合附图和具体实施方式对本发明作进一步详细的说明。
本发明公开的是一种钛白粉的加工方法，该方法具体描述如下：
S11、将钛白粉原料投入一级水磨设备进行研磨，得到一级产品；
S12、将所述一级产品进行分离，得到一级分离的钛白粉颗粒；
S13、将所得到的一级分离的钛白粉颗粒再次投入二级水磨设备进行研磨，并进行分离，得到二级分离的钛白粉颗粒；
S14、将所述二级分离的钛白粉颗粒再次投入下一级设备进行操作，并以此循环，共进行十二级操作，直至得到最终的标准级产品。
所说的标准级产品是指细度在1-1.5微米之内的钛白粉产品，而当前的钛白粉颗粒细度都是在大于等于2微米的范围内，不能够进一步细化。
按上述步骤，最后得到标准级产品时，本发明优选为连续进行十二级的水磨和分离操作。从第一级操作到第十二及操作中所使用的分离设备，其过滤膜都是逐级减小，以达到整个操作过程中，能够逐级过滤掉每一级中的相对大颗粒，对留下的相对细颗粒继续操作，直至最后得到粒度均匀的标准级产品。
S15、对所述标准级产品进行喷雾干燥；
S16、将干燥后的钛白粉投入改性设备进行表面处理，并进行产品检验，最终得到合格的钛白粉产品。如图2所示是使用本发明所公开的方法所加工的钛白粉的颗粒分布曲线示意图。
上述操作流程可通过图1所示的流程示意图进行标注。
本发明公开了一种钛白粉的粉碎方法，是通过连续进行多级的水磨和分离操作实现，使得钛白粉颗粒在多级操作下逐级地过滤掉相对较粗的颗粒，对相对的细颗粒继续进行研磨，最后得到粒度分布均匀的标准产品。本发明所公开的研磨方法由于在其研磨过程中加入了多级的分离操作，使得产品粒度分布均匀，能够达到1-1.5微米之内，甚至能够达到1微米之内的细度，极大地提高了产品的利用率，使其使用量相对于现有的钛白粉产品的使用量能够减少30-40％，降低了成本，节约了钛矿资源，同时由于粒度变细，也极大地提高了产品的应用性能。
以上为对本发明所公开的一种钛白粉的加工方法的说明。对所公开的实施例的上述说明，使本领域专业技术人员能够实现或使用本发明。对这些实施例的多种修改对本领域的专业技术人员来说将是显而易见的，本文中所定义的一般原理可以在不脱离本发明的精神或范围的情况下，在其它实施例中实现。因此，本发明将不会被限制于本文所示的这些实施例，而是要符合与本文所公开的原理和新颖特点相一致的最宽的范围。
Claims (4)
1.一种钛白粉的研磨方法，其特征在于，包括如下步骤：
一级操作：
将钛白粉原料投入一级水磨设备进行研磨，得到一级产品；
将所述一级产品进行分离，得到一级分离颗粒；
二级操作：
将所述一级分离颗粒继续投入二级水磨设备进行研磨，得到二级产品；
将所述二级产品再次进行分离，得到二级分离颗粒；
继续进行下一级操作，直至最终得到标准级产品。
2.根据权利要求1所述的方法，其特征在于，所述操作包括12级操作。
3.根据权利要求1所述的方法，其特征在于，在所述得到标准级产品之后还包括喷雾干燥处理、产品检验。
4.根据权利要求1-3任一项所述的方法，其特征在于，所述标准级产品为细度在1.5微米以内的钛白粉产品。