CN102643580A - 一种硅胶喷涂油墨配方及其制作工艺 - Google Patents

一种硅胶喷涂油墨配方及其制作工艺 Download PDF

Info

Publication number
CN102643580A
CN102643580A CN2012101594690A CN201210159469A CN102643580A CN 102643580 A CN102643580 A CN 102643580A CN 2012101594690 A CN2012101594690 A CN 2012101594690A CN 201210159469 A CN201210159469 A CN 201210159469A CN 102643580 A CN102643580 A CN 102643580A
Authority
CN
China
Prior art keywords
silica gel
printing ink
gel spraying
resin
manufacturing technique
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012101594690A
Other languages
English (en)
Inventor
莫小静
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
KUNSHAN WEMORE ELECTRONIC TECHNOLOGY Co Ltd
Original Assignee
KUNSHAN WEMORE ELECTRONIC TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by KUNSHAN WEMORE ELECTRONIC TECHNOLOGY Co Ltd filed Critical KUNSHAN WEMORE ELECTRONIC TECHNOLOGY Co Ltd
Priority to CN2012101594690A priority Critical patent/CN102643580A/zh
Publication of CN102643580A publication Critical patent/CN102643580A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种硅胶喷涂油墨配方及其制作工艺，包括甲基乙烯基聚硅氧烷40%～72%；二氧化硅15%～45%；铂催化剂0.01%～0.7%；抑制剂0.001%～1%；树脂10%～30%；芳香烃25%～40%。按照配方，使用精密电子秤称重后，投入到高速分散机内；利用高速分散机将各组分打磨，转速为3000r/m，时间5分钟；打磨完成后的原料，放置于碾磨机进行碾磨，碾磨结束得到硅胶喷涂油墨。本发明解决了现有技术中油墨产品没有进行充分的混合，颜料色粉粒子颗粒较大，不够细腻，喷涂使用起来，品质较差，不能满足使用者需要的问题，提供了一种能够把颜料色粉粒子打磨细腻，并且多种色粉充分混合均匀的硅胶喷涂油墨配方及其制作工艺。

Description

一种硅胶喷涂油墨配方及其制作工艺
技术领域
本发明涉及一种油墨的配方及其制作工艺，特别是涉及一种硅胶喷涂油墨配方及其制作工艺。
背景技术
油墨是用于包装材料印刷的重要材料，它通过印刷将图案、文字表现在承印物上油墨中包括主要成分和辅助成分，它们均匀地混合并经反复轧制而成一种粘性胶状流体。由颜料、连结料和助剂等组成。用于书刊、包装装潢、建筑装饰等各种印刷。随着社会需求增大，油墨品种和产量也相应扩展和增长。
目前的油墨产品没有进行充分的混合，颜料色粉粒子颗粒较大，不够细腻，喷涂使用起来，品质较差，不能满足使用者的需要。
发明内容
为了解决现有技术中油墨产品没有进行充分的混合，颜料色粉粒子颗粒较大，不够细腻，喷涂使用起来，品质较差，不能满足使用者需要的问题，本发明提供了一种能够把颜料色粉粒子打磨细腻，并且多种色粉充分混合均匀的硅胶喷涂油墨配方及其制作工艺。
为了解决上述问题，本发明所采取的技术方案是：
一种硅胶喷涂油墨的配方，其特征在于：包括甲基乙烯基聚硅氧烷、二氧化硅、铂催化剂、抑制剂、树脂和芳香烃，所述各组分的重量百分比为：
甲基乙烯基聚硅氧烷40%～72%； 
二氧化硅15%～45%； 
铂催化剂0.01%～0.7%；               
抑制剂 0.001%～1%； 
树脂10%～30%； 
芳香烃25%～40%。
前述的一种硅胶喷涂油墨的配方，其特征在于：所述树脂采用颜料树脂。
一种硅胶喷涂油墨的制作工艺，其特征在于：包括以下步骤：
（1）、通过精密电子秤称重后，将重量百分比为40%～72%的甲基乙烯基聚硅氧烷、15%～45%的二氧化硅、0.01%～0.7%铂催化剂、0.001%～1%的抑制剂、10%～30%的颜料树脂、25%～40%的芳香烃投入到高速分散机内；
（2）、利用高速分散机将各组分打磨，转速为3000r/m，时间5分钟；
（3）、打磨完成后的原料，放置于碾磨机进行碾磨，将颜料色粉粒子打磨细腻，碾磨结束，得到硅胶喷涂油墨。
前述的一种硅胶喷涂油墨的制作工艺，其特征在于：所述碾磨机采用三辊碾磨机。
本发明的有益效果是：通过本发明的配方制得油墨混合十分均匀，颗粒较小，能够将颜料色粉粒子打磨细腻，油墨品质较高，能够满足使用者的需要，适合保存于5～10℃环境中。
具体实施方式
一种硅胶喷涂油墨的配方，其特征在于：包括甲基乙烯基聚硅氧烷、二氧化硅、铂催化剂、抑制剂、树脂和芳香烃，所述各组分的重量百分比为：
甲基乙烯基聚硅氧烷40%～72%； 
二氧化硅15%～45%； 
铂催化剂0.01%～0.7%；               
抑制剂 0.001%～1%； 
颜料树脂10%～30%； 
芳香烃25%～40%。
一种硅胶喷涂油墨的制作工艺，其特征在于：包括以下步骤：
（1）、通过精密电子秤称重后，将重量百分比为40%～72%的甲基乙烯基聚硅氧烷、15%～45%的二氧化硅、0.01%～0.7%铂催化剂、0.001%～1%的抑制剂、10%～30%的颜料树脂、25%～40%的芳香烃投入到高速分散机内；
（2）、利用高速分散机将各组分打磨，转速为3000r/m，时间5分钟；
（3）、打磨完成后的原料，放置于三辊碾磨机进行碾磨，将颜料色粉粒子打磨细腻，碾磨结束，得到硅胶喷涂油墨。
以上显示和描述了本发明的基本原理、主要特征及优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (4)

1.一种硅胶喷涂油墨的配方，其特征在于：包括甲基乙烯基聚硅氧烷、二氧化硅、铂催化剂、抑制剂、树脂和芳香烃，所述各组分的重量百分比为：
甲基乙烯基聚硅氧烷40%～72%； 
二氧化硅15%～45%； 
铂催化剂0.01%～0.7%；               
抑制剂 0.001%～1%； 
树脂10%～30%； 
芳香烃25%～40%。
2.根据权利要求1所述的一种硅胶喷涂油墨的配方，其特征在于：所述树脂采用颜料树脂。
3.一种硅胶喷涂油墨的制作工艺，其特征在于：包括以下步骤：
（1）、通过精密电子秤称重后，将重量百分比为40%～72%的甲基乙烯基聚硅氧烷、15%～45%的二氧化硅、0.01%～0.7%铂催化剂、0.001%～1%的抑制剂、10%～30%的颜料树脂、25%～40%的芳香烃投入到高速分散机内；
（2）、利用高速分散机将各组分打磨，转速为3000r/m，时间5分钟；
（3）、打磨完成后的原料，放置于碾磨机进行碾磨，将颜料色粉粒子打磨细腻，碾磨结束，得到硅胶喷涂油墨。
4.根据权利要求3所述的一种硅胶喷涂油墨的制作工艺，其特征在于：所述碾磨机采用三辊碾磨机。
CN2012101594690A 2012-05-22 2012-05-22 一种硅胶喷涂油墨配方及其制作工艺 Pending CN102643580A (zh)