CN102641832B - Paint-baking process for surfaces of far-infrared heating plates - Google Patents
Paint-baking process for surfaces of far-infrared heating plates Download PDFInfo
- Publication number
- CN102641832B CN102641832B CN201210139160.5A CN201210139160A CN102641832B CN 102641832 B CN102641832 B CN 102641832B CN 201210139160 A CN201210139160 A CN 201210139160A CN 102641832 B CN102641832 B CN 102641832B
- Authority
- CN
- China
- Prior art keywords
- infrared heating
- far
- far infrared
- heating plates
- minutes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a paint-baking process for the surfaces of far-infrared heating plates. The process is carried out in a dustless environment, a layer of epoxy resin is sprayed on the surface of each far-infrared heating plate to enhance the roughness of the surface of the far-infrared heating plate, primer is brushed on the processed surfaces of the far-infrared heating plates for one time, finish is brushed on the treated surfaces of the far-infrared heating plates for two times, the far-infrared heating plates are put into a high-temperature drying tunnel and baked each time after brushing, and finally, needed patterns are screen-printed on the surfaces of the dried far-infrared heating plates. The color of the far-infrared heating plates processed by the process is vivid, the surfaces of the far-infrared heating plates are smooth, the decoration effect is good, meanwhile, the far-infrared heating plates are easy to scrub, dampproofness and fireproofness are good, and the service lives are long.
Description
Technical field
The present invention relates to a kind of baking finish process of far infrared heating piece surface, belong to baking finish process technical field.
Background technology
The brilliant wall of carbon warms up and adopts the brilliant plate of carbon as exothermic material, and by energising, the brilliant one's share of expenses for a joint undertaking group of carbon does Brownian movement, produces a large amount of people's energy, and the brilliant plate of carbon sends the heat radiation of far infrared simultaneously, thus reaches the object of heating.Due to its economic environmental protection, the features such as quick heating, are just progressively widely used in the indoor environments such as family, office, public place of entertainment.In order to pursue aesthetic, can indoor environment be incorporated, therefore needing to process the brilliant plate surface of carbon.What the brilliant plate surface treatment of common carbon adopted is fabric decoration, and process is convenient, and effect is attractive in appearance, but for comparatively moist environment, bunting is easily mouldy owing to making moist, and produce peculiar smell, not only unsightly, the mould simultaneously produced can cause healthy hidden danger to child.And adopt face glass to decorate, although the problem of not making moist, glass easily damages, and comes off after the ornament materials of glass surface is easily subject to high-temperature baking for a long time.The mode of traditional decoration carbon brilliant plate is all shorter for service life, is not suitable for living environment.
Summary of the invention
The object of this invention is to provide a kind of baking finish process of far infrared heating piece surface, poor in order to solve traditional far infrared heating piece incrustation persistence, the problem that service life is short.
For realizing this purpose, the method applied in the present invention is: a kind of baking finish process of far infrared heating piece surface, is characterized in that, carries out following steps by former for far infrared heating under dustfree environment:
To far infrared heating former surface uniform spraying agent, increase far infrared heating former surface roughness, described Alevaire is epoxy resin inorganic agent;
At surperficial primer spray, in the drying tunnel of 100 ~ 200 DEG C, then toast the step of 15 ~ 45 minutes;
Spray second layer finish paint, then toasts the step of 15 ~ 45 minutes in the drying tunnel of 120 ~ 200 DEG C;
Spray third layer finish paint, then toasts the step of 10 ~ 80 minutes in the drying tunnel of 130 ~ 200 DEG C.
The baking finish process on far infrared heating piece surface, its selection process is, carries out following steps by former for far infrared heating under dustfree environment:
To far infrared heating former surface uniform atomization machine, increase far infrared heating former surface roughness;
Toast 30 minutes in the drying tunnel of 150 DEG C after surperficial primer spray;
Toast 30 minutes in the drying tunnel of 160 DEG C after spray second layer finish paint;
Toast 45 minutes in the drying tunnel of 165 DEG C after spray third layer finish paint.
Spray third layer finish paint also, after drying, carries out the step of screen printed pattern.
Its beneficial effect is: by the process of infrared heating sheet surface roughening, can make that coating is better must be attached to its surface, after multistep baking vanish, lovely luster, surface smoothness is good, easily cleans, damp-proof and fireproof performance is good, by screen printed pattern, increases its aesthetic property.
Detailed description of the invention
All features disclosed in this description, or the step in disclosed all methods or process, except mutually exclusive feature and/or step, all can combine by any way.
Arbitrary feature disclosed in this description (comprising any accessory claim, summary and accompanying drawing), unless specifically stated otherwise, all can be replaced by other equivalences or the alternative features with similar object.That is, unless specifically stated otherwise, each feature is an example in a series of equivalence or similar characteristics.
Embodiment 1
Former for a far infrared heating surface wipes is clean, spray epoxy resin coating, after dry, the paint mixed up is sprayed onto far infrared heating piece surface, form one deck priming paint, put into high temperature drying tunnel 100 DEG C baking 45 minutes.The far infrared heating piece of drying is taken out, carries out the spraying of second layer finish paint, then put into high temperature drying tunnel 120 DEG C baking 45 minutes.Far infrared heating piece after drying is taken out, carries out the spraying of third layer minute surface environmental protection paint, put into high temperature drying tunnel 130 DEG C baking 80 minutes.Finally by serigraphy, required pattern is printed onto the surface of the far infrared heating piece after baking vanish.
Embodiment 2
Far infrared heating piece surface wipes is clean, spray epoxy resin coating, after dry, the paint mixed up is sprayed onto far infrared heating piece surface, form one deck priming paint, put into high temperature drying tunnel 150 DEG C baking 30 minutes.The far infrared heating piece of drying is taken out, carries out the spraying of second layer finish paint, then put into high temperature drying tunnel 160 DEG C baking 30 minutes.Far infrared heating piece after drying is taken out, carries out the spraying of third layer minute surface environmental protection paint, put into high temperature drying tunnel 165 DEG C baking 45 minutes.Finally by serigraphy, required pattern is printed onto the surface of the far infrared heating piece after baking vanish.
Embodiment 3
Former for a far infrared heating surface wipes is clean, spray epoxy resin coating, after dry, the paint mixed up is sprayed onto far infrared heating piece surface, form one deck priming paint, put into high temperature drying tunnel 200 DEG C baking 15 minutes.The far infrared heating piece of drying is taken out, carries out the spraying of second layer finish paint, then put into high temperature drying tunnel 200 DEG C baking 15 minutes.Far infrared heating piece after drying is taken out, carries out the spraying of third layer minute surface environmental protection paint, put into high temperature drying tunnel 200 DEG C baking 10 minutes.Finally by serigraphy, required pattern is printed onto the surface of the far infrared heating piece after baking vanish.
Before surperficial primer spray, also comprise the step increasing far infrared heating former surface roughness, the method increasing roughness is: to far infrared heating former surface uniform spraying agent.Described Alevaire is asphalt mixtures modified by epoxy resin inorganic agent.
The present invention is not limited to aforesaid detailed description of the invention.The present invention expands to any new feature of disclosing in this manual or any combination newly, and the step of the arbitrary new method disclosed or process or any combination newly.
Claims (3)
1. the baking finish process on far infrared heating piece surface, is characterized in that, carries out following steps by former for far infrared heating under dustfree environment:
To far infrared heating former surface uniform spraying agent, increase far infrared heating former surface roughness, described Alevaire is epoxy resin inorganic agent;
At surperficial primer spray, in the drying tunnel of 100 ~ 200 DEG C, then toast the step of 15 ~ 45 minutes;
Spray second layer finish paint, then toasts the step of 15 ~ 45 minutes in the drying tunnel of 120 ~ 200 DEG C;
Spray third layer finish paint, then toasts the step of 10 ~ 80 minutes in the drying tunnel of 130 ~ 200 DEG C.
2. the baking finish process on far infrared heating piece surface according to claim 1, is characterized in that,
Toast 30 minutes in the drying tunnel of 150 DEG C after surperficial primer spray;
Toast 30 minutes in the drying tunnel of 160 DEG C after spray second layer finish paint;
Toast 45 minutes in the drying tunnel of 165 DEG C after spray third layer finish paint.
3. the baking finish process on far infrared heating piece surface according to claim 1 and 2, is characterized in that, spray third layer finish paint also, after drying, carries out the step of screen printed pattern.