CN104249051A - Processing method of surface coating for metal E-cigarette pipe - Google Patents
Processing method of surface coating for metal E-cigarette pipe Download PDFInfo
- Publication number
- CN104249051A CN104249051A CN201410475637.6A CN201410475637A CN104249051A CN 104249051 A CN104249051 A CN 104249051A CN 201410475637 A CN201410475637 A CN 201410475637A CN 104249051 A CN104249051 A CN 104249051A
- Authority
- CN
- China
- Prior art keywords
- baking
- metals
- smoke pipe
- baking vanish
- gloss oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a processing method of surface coating for a metal E-cigarette pipe. The processing method includes: a, diluting hardware white paint; b, spaying dilute solution of the hardware white paint to the outer surface of the metal E-cigarette pipe; c, baking the metal E-cigarette pipe, and cooling the metal E-cigarette pipe to room temperature; d, preparing mixed solution of luminous powder and hardware baking varnish; e, spaying the mixed solution of luminous powder and hardware baking varnish to the outer surface of the metal E-cigarette pipe three times; f, baking the metal E-cigarette pipe, and cooling the metal E-cigarette pipe to room temperature; g, spaying the mixed solution of luminous powder and hardware baking varnish to the outer surface the metal E-cigarette pipe three times again; h, baking the metal E-cigarette pipe again, and cooling the metal E-cigarette pipe to room temperature; i, spaying hardware baking varnish to the outer surface of the metal E-cigarette pipe three times, and baking the metal E-cigarette pipe to allow thorough dryness. By the processing method, the surface coating high in quality and good in appearance can be made on the surface of the metal E-cigarette pipe.
Description
Technical field
The present invention relates to electronic cigarette technical field, particularly relate to a kind of processing method of metal electron smoke pipe face coat.
Background technology
Along with people constantly improve healthy degree of concern, increasing smoker selects to give up smoking to reduce the injury of smoking to health, wherein, electronic cigarette as a kind of instrument slowing down smoker's craving for tobacco, by increasing ES's choice for use.
Wherein, for electronic cigarette, its smoke pipe generally adopts metal material to be prepared from, and the surface of metal electron smoke pipe is generally coated with face coat, and this face coat can strengthen the aesthetics of metal electron smoke pipe effectively.
Summary of the invention
The object of the present invention is to provide a kind of processing method of metal electron smoke pipe face coat, the processing method of this metal electron smoke pipe face coat can at Surface Machining one high-quality of metal electron smoke pipe and the good face coat of aesthetics.
For achieving the above object, the present invention is achieved through the following technical solutions.
A processing method for metal electron smoke pipe face coat, includes following processing step, is specially:
A, in five metals white baking vanish, add five metals baking vanish diluent, mix and blend five metals white baking vanish and five metals baking vanish diluent, until evenly;
B, the five metals white baking vanish after dilution is sprayed at the outer surface of metal electron smoke pipe equably;
C, by spray five metals white baking vanish metal electron smoke pipe put into baking box carry out baking process, baking temperature is 90 degree, and baking time is 10 minutes; After end to be baked, metal electron smoke pipe is shifted out from baking box and is cooled to room temperature;
D, be added in five metals baking vanish gloss oil by luminescent powder, mix and blend luminescent powder and five metals baking vanish gloss oil, until evenly;
E, luminescent powder and five metals baking vanish gloss oil mixed liquor are sprayed at equably the five metals white baking vanish layer outer surface of metal electron smoke pipe, repeat spraying three times;
F, the metal electron smoke pipe spraying luminescent powder and five metals baking vanish gloss oil mixed liquor put into baking box and carry out baking and process, baking temperature is 90 degree, and baking time is 10 minutes; After end to be baked, metal electron smoke pipe is shifted out from baking box and is cooled to room temperature;
G, luminescent powder luminescent powder and five metals baking vanish gloss oil mixed liquor being sprayed at equably metal electron smoke pipe and five metals baking vanish gloss oil mixed layer outer surface, repeat spraying three times;
H, the metal electron smoke pipe again spraying luminescent powder and five metals baking vanish gloss oil mixed liquor put into baking box and carry out baking and process, baking temperature is 135 degree, and baking time is 35 minutes; After end to be baked, metal electron smoke pipe is shifted out from baking box and is cooled to room temperature;
I, luminescent powder five metals baking vanish gloss oil being sprayed at equably metal electron smoke pipe and five metals baking vanish gloss oil mixed layer outer surface, repeat spraying three times, and then baking parches.
Wherein, described luminescent powder and five metals baking vanish gloss oil mixed liquor are that 30% luminescent powder and 70% five metals baking vanish gloss oil form by weight portion.
Beneficial effect of the present invention is: the processing method of a kind of metal electron smoke pipe face coat of the present invention, and it includes following processing step: a, dilution five metals white baking vanish; B, by the five metals white baking vanish even application after dilution in metal electron smoke pipe outer surface; C, baking five metals white baking vanish layer, and be cooled to room temperature after baking; D, prepare luminescent powder and five metals baking vanish gloss oil mixed liquor; E, by luminescent powder and five metals baking vanish gloss oil mixed liquor even application in five metals white baking vanish layer outer surface, repeat spraying three times; F, baking luminescent powder and five metals baking vanish gloss oil mixed layer, and be cooled to room temperature after baking; G, again by luminescent powder and five metals baking vanish gloss oil mixed liquor even application in luminescent powder and five metals baking vanish gloss oil mixed layer outer surface, repeat spraying three times; H, again baking luminescent powder and five metals baking vanish gloss oil mixed layer, and be cooled to room temperature after baking; I, by five metals baking vanish gloss oil even application luminescent powder and five metals baking vanish gloss oil mixed layer outer surface, repeat spraying three times, then baking parches.By above-mentioned processing step, the present invention can at Surface Machining one high-quality of metal electron smoke pipe and the good face coat of aesthetics.
Detailed description of the invention
Below in conjunction with concrete embodiment, the present invention will be described.
A processing method for metal electron smoke pipe face coat, includes following processing step, is specially:
A, in five metals white baking vanish, add five metals baking vanish diluent, mix and blend five metals white baking vanish and five metals baking vanish diluent, until evenly;
B, the five metals white baking vanish after dilution is sprayed at the outer surface of metal electron smoke pipe equably;
C, by spray five metals white baking vanish metal electron smoke pipe put into baking box carry out baking process, baking temperature is 90 degree, and baking time is 10 minutes; After end to be baked, metal electron smoke pipe is shifted out from baking box and is cooled to room temperature;
D, be added in five metals baking vanish gloss oil by luminescent powder, mix and blend luminescent powder and five metals baking vanish gloss oil, until evenly;
E, luminescent powder and five metals baking vanish gloss oil mixed liquor are sprayed at equably the five metals white baking vanish layer outer surface of metal electron smoke pipe, repeat spraying three times;
F, the metal electron smoke pipe spraying luminescent powder and five metals baking vanish gloss oil mixed liquor put into baking box and carry out baking and process, baking temperature is 90 degree, and baking time is 10 minutes; After end to be baked, metal electron smoke pipe is shifted out from baking box and is cooled to room temperature;
G, luminescent powder luminescent powder and five metals baking vanish gloss oil mixed liquor being sprayed at equably metal electron smoke pipe and five metals baking vanish gloss oil mixed layer outer surface, repeat spraying three times;
H, the metal electron smoke pipe again spraying luminescent powder and five metals baking vanish gloss oil mixed liquor put into baking box and carry out baking and process, baking temperature is 135 degree, and baking time is 35 minutes; After end to be baked, metal electron smoke pipe is shifted out from baking box and is cooled to room temperature;
I, luminescent powder five metals baking vanish gloss oil being sprayed at equably metal electron smoke pipe and five metals baking vanish gloss oil mixed layer outer surface, repeat spraying three times, and then baking parches.
Need point out further, preferably, luminescent powder and five metals baking vanish gloss oil mixed liquor are that 30% luminescent powder and 70% five metals baking vanish gloss oil form by weight portion; Certainly, the mass parts ratio of above-mentioned luminescent powder and five metals baking vanish gloss oil is not construed as limiting the invention, and namely luminescent powder and five metals baking vanish gloss oil can also adopt other mass parts ratio to mix.
By above-mentioned processing step, the present invention can at Surface Machining one high-quality of metal electron smoke pipe and the good face coat of aesthetics.
Above content is only preferred embodiment of the present invention, and for those of ordinary skill in the art, according to thought of the present invention, all will change in specific embodiments and applications, this description should not be construed as limitation of the present invention.
Claims (2)
1. a processing method for metal electron smoke pipe face coat, is characterized in that, includes following processing step, is specially:
A, in five metals white baking vanish, add five metals baking vanish diluent, mix and blend five metals white baking vanish and five metals baking vanish diluent, until evenly;
B, the five metals white baking vanish after dilution is sprayed at the outer surface of metal electron smoke pipe equably;
C, by spray five metals white baking vanish metal electron smoke pipe put into baking box carry out baking process, baking temperature is 90 degree, and baking time is 10 minutes; After end to be baked, metal electron smoke pipe is shifted out from baking box and is cooled to room temperature;
D, be added in five metals baking vanish gloss oil by luminescent powder, mix and blend luminescent powder and five metals baking vanish gloss oil, until evenly;
E, luminescent powder and five metals baking vanish gloss oil mixed liquor are sprayed at equably the five metals white baking vanish layer outer surface of metal electron smoke pipe, repeat spraying three times;
F, the metal electron smoke pipe spraying luminescent powder and five metals baking vanish gloss oil mixed liquor put into baking box and carry out baking and process, baking temperature is 90 degree, and baking time is 10 minutes; After end to be baked, metal electron smoke pipe is shifted out from baking box and is cooled to room temperature;
G, luminescent powder luminescent powder and five metals baking vanish gloss oil mixed liquor being sprayed at equably metal electron smoke pipe and five metals baking vanish gloss oil mixed layer outer surface, repeat spraying three times;
H, the metal electron smoke pipe again spraying luminescent powder and five metals baking vanish gloss oil mixed liquor put into baking box and carry out baking and process, baking temperature is 135 degree, and baking time is 35 minutes; After end to be baked, metal electron smoke pipe is shifted out from baking box and is cooled to room temperature;
I, luminescent powder five metals baking vanish gloss oil being sprayed at equably metal electron smoke pipe and five metals baking vanish gloss oil mixed layer outer surface, repeat spraying three times, and then baking parches.
2. the processing method of a kind of metal electron smoke pipe face coat according to claim 1, is characterized in that: described luminescent powder and five metals baking vanish gloss oil mixed liquor are that 30% luminescent powder and 70% five metals baking vanish gloss oil form by weight portion.