CN102641832A - Paint-baking process for surfaces of far-infrared heating plates - Google Patents
Paint-baking process for surfaces of far-infrared heating plates Download PDFInfo
- Publication number
- CN102641832A CN102641832A CN2012101391605A CN201210139160A CN102641832A CN 102641832 A CN102641832 A CN 102641832A CN 2012101391605 A CN2012101391605 A CN 2012101391605A CN 201210139160 A CN201210139160 A CN 201210139160A CN 102641832 A CN102641832 A CN 102641832A
- Authority
- CN
- China
- Prior art keywords
- infrared heating
- far infrared
- far
- heating plates
- drying tunnel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a paint-baking process for the surfaces of far-infrared heating plates. The process is carried out in a dustless environment, a layer of epoxy resin is sprayed on the surface of each far-infrared heating plate to enhance the roughness of the surface of the far-infrared heating plate, primer is brushed on the processed surfaces of the far-infrared heating plates for one time, finish is brushed on the treated surfaces of the far-infrared heating plates for two times, the far-infrared heating plates are put into a high-temperature drying tunnel and baked each time after brushing, and finally, needed patterns are screen-printed on the surfaces of the dried far-infrared heating plates. The color of the far-infrared heating plates processed by the process is vivid, the surfaces of the far-infrared heating plates are smooth, the decoration effect is good, meanwhile, the far-infrared heating plates are easy to scrub, dampproofness and fireproofness are good, and the service lives are long.
Description
Technical field
The present invention relates to the baking vanish technology on a kind of far infrared heating sheet surface, belong to baking vanish technology field.
Background technology
The warm employing far infrared heating sheet that adopts of wall generally adopts the brilliant plate of carbon as the exothermic material far infrared, and through energising, the brilliant one's share of expenses for a joint undertaking of carbon group does Brownian movement, produces a large amount of heat energy, and the brilliant plate of carbon sends the heat radiation of far infrared simultaneously, thereby reaches the purpose of heating.Because its economic environmental protection, characteristics such as quick heating just progressively are widely used in the indoor environments such as family, office, public place of entertainment.In order to pursue aesthetic, make it can incorporate indoor environment, therefore need handle the brilliant plate of carbon surface.What the brilliant plate surface treatment of common carbon was adopted is fabric decoration, convenient processing, and effect is attractive in appearance, however for comparatively moist environment, bunting is mouldy owing to making moist easily, produces peculiar smell, and not only not attractive in appearance, produced simultaneously mould can be caused healthy hidden danger to the child.And adopt face glass to decorate, and though the problem of not making moist, glass damages easily, and the explosion phenomenon appears in safety glass, and the ornament materials of glass surface comes off after receiving high-temperature baking for a long time easily.The mode of the brilliant plate of traditional decoration carbon is all shorter service life, is not suitable for living environment.
Summary of the invention
The purpose of this invention is to provide the baking vanish technology on a kind of far infrared heating sheet surface, poor in order to solve traditional far infrared heating sheet incrustation persistence, the problem that service life is short.
For realizing this purpose, the method that the present invention adopted is: the baking vanish technology on a kind of far infrared heating sheet surface, it is characterized in that, and former of far infrared heating is carried out following steps under dustfree environment:
At surperficial primer spray, in 100~200 ℃ drying tunnel, toast 15~45 minutes step then;
Spray second layer finish paint, in 120~200 ℃ drying tunnel, toast 15~45 minutes step then;
Spray the 3rd aspect lacquer, in 130~200 ℃ drying tunnel, toast 10~80 minutes step then.
The baking vanish technology on a kind of far infrared heating sheet surface, its selection process is that former of far infrared heating is carried out following steps under dustfree environment:
In 150 ℃ drying tunnel, toasting 30 minutes behind the surperficial primer spray;
In 160 ℃ drying tunnel, toasted 30 minutes behind the spray second layer finish paint;
Spraying the 3rd aspect lacquer back toasted 45 minutes in 165 ℃ drying tunnel.
Before surperficial primer spray, also comprise the step that increases former surface roughness of far infrared heating, the method that increases roughness is: to former surperficial even spraying agent of far infrared heating.Said Alevaire is the epoxy resin inorganic agent.
After spraying the 3rd aspect lacquer and oven dry, carry out the step of screen printed pattern.
Its beneficial effect is: through infrared heating sheet surface roughening is handled, can make that coating is better must be attached to its surface, behind the multistep baking vanish; Lovely luster, surface smoothness is good, is prone to clean; The damp-proof and fireproof performance is good, through screen printed pattern, increases its aesthetic property.
The specific embodiment
Disclosed all characteristics in this specification, or the step in disclosed all methods or the process except mutually exclusive characteristic and/or the step, all can make up by any way.
Disclosed arbitrary characteristic in this specification (comprising any accessory claim, summary) is only if special narration all can be replaced by other equivalences or the alternative features with similar purpose.That is, only if special narration, each characteristic is an example in a series of equivalences or the similar characteristics.
Embodiment 1
With former surperficial wiped clean of far infrared heating, spray epoxy resin coating, the paint that will mix up after waiting to do is sprayed onto far infrared heating sheet surface, forms one deck priming paint, puts into 100 ℃ of bakings of high temperature drying tunnel 45 minutes.The far infrared heating sheet of oven dry is taken out, carry out the spraying of second layer finish paint, put into 120 ℃ of bakings of high temperature drying tunnel 45 minutes again.Far infrared heating sheet after the oven dry is taken out, carry out the spraying of the 3rd layer of minute surface environmental protection paint, put into 130 ℃ of bakings of high temperature drying tunnel 80 minutes.At last through serigraphy, needed pattern is printed onto the far infrared heating sheet surface behind the baking vanish.
Embodiment 2
With far infrared heating sheet surface wiped clean, spray epoxy resin coating, the paint that will mix up after waiting to do is sprayed onto far infrared heating sheet surface, forms one deck priming paint, puts into 150 ℃ of bakings of high temperature drying tunnel 30 minutes.The far infrared heating sheet of oven dry is taken out, carry out the spraying of second layer finish paint, put into 160 ℃ of bakings of high temperature drying tunnel 30 minutes again.Far infrared heating sheet after the oven dry is taken out, carry out the spraying of the 3rd layer of minute surface environmental protection paint, put into 165 ℃ of bakings of high temperature drying tunnel 45 minutes.At last through serigraphy, needed pattern is printed onto the far infrared heating sheet surface behind the baking vanish.
Embodiment 3
With former surperficial wiped clean of far infrared heating, spray epoxy resin coating, the paint that will mix up after waiting to do is sprayed onto far infrared heating sheet surface, forms one deck priming paint, puts into 200 ℃ of bakings of high temperature drying tunnel 15 minutes.The far infrared heating sheet of oven dry is taken out, carry out the spraying of second layer finish paint, put into 200 ℃ of bakings of high temperature drying tunnel 15 minutes again.Far infrared heating sheet after the oven dry is taken out, carry out the spraying of the 3rd layer of minute surface environmental protection paint, put into 200 ℃ of bakings of high temperature drying tunnel 10 minutes.At last through serigraphy, needed pattern is printed onto the far infrared heating sheet surface behind the baking vanish.
Before surperficial primer spray, also comprise the step that increases former surface roughness of far infrared heating, the method that increases roughness is: to former surperficial even spraying agent of far infrared heating.Said Alevaire is the epoxy resin inorganic agent.
The present invention is not limited to the aforesaid specific embodiment.The present invention expands to any new feature or any new combination that discloses in this manual, and the arbitrary new method that discloses or step or any new combination of process.
Claims (6)
1. the baking vanish technology on a far infrared heating sheet surface is characterized in that, former of far infrared heating is carried out following steps under dustfree environment:
At surperficial primer spray, in 100~200 ℃ drying tunnel, toast 15~45 minutes step then;
Spray second layer finish paint, in 120~200 ℃ drying tunnel, toast 15~45 minutes step then;
Spray the 3rd aspect lacquer, in 130~200 ℃ drying tunnel, toast 10~80 minutes step then.
2. the baking vanish technology on far infrared heating sheet according to claim 1 surface is characterized in that,
In 150 ℃ drying tunnel, toasting 30 minutes behind the surperficial primer spray;
In 160 ℃ drying tunnel, toasted 30 minutes behind the spray second layer finish paint;
Spraying the 3rd aspect lacquer back toasted 45 minutes in 165 ℃ drying tunnel.
3. the baking vanish technology on far infrared heating sheet according to claim 1 surface is characterized in that, before surperficial primer spray, also comprises the step that increases former surface roughness of far infrared heating.
4. the baking vanish technology on far infrared heating sheet according to claim 3 surface is characterized in that the method that increases roughness is: to former surperficial even spraying agent of far infrared heating.
5. the baking vanish technology on far infrared heating sheet according to claim 4 surface is characterized in that said Alevaire is the epoxy resin inorganic agent.
6. the baking vanish technology on far infrared heating sheet according to claim 1 and 2 surface is characterized in that, after the 3rd aspect of spraying is coated with lacquer and dried, carries out the step of screen printed pattern.