CN101125736A - Method for manufacturing wood grain and marble glass - Google Patents
Method for manufacturing wood grain and marble glass Download PDFInfo
- Publication number
- CN101125736A CN101125736A CNA2006100621498A CN200610062149A CN101125736A CN 101125736 A CN101125736 A CN 101125736A CN A2006100621498 A CNA2006100621498 A CN A2006100621498A CN 200610062149 A CN200610062149 A CN 200610062149A CN 101125736 A CN101125736 A CN 101125736A
- Authority
- CN
- China
- Prior art keywords
- glass
- transfer printing
- water
- wood grain
- picture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a manufacturing method for glass with wood grain or marble grain and is divided into the steps, a. undercoating, wherein, the glass is coated with an amount of polishing oil specially used by the transparent class to increase adhesive of a transfer printing layer to the glass, after coating, the glass is dried in a drier for 20-50 minutes in a temperature ranging from 70-80 DEG C and then cooled to ambient temperature; b. activating transfer printing film, wherein, water-carrying transfer printing film is laid on the water surface in a transfer printing water tank with an image layer upside and the surface of the image is evenly coated with activator; c. water-carrying transfer printing; d. arranging; e. drying; f. printing colored paint, wherein, color paint is coated on the transfer printing surface and then is oven dried or dried naturally and last sides and uncoated surface of the glass are cleaned. The method for manufacturing glass with wood grain and marble grain has low cost and simple technique.
Description
Technical field
The present invention relates to decorate, furniture is with the processing of glass, especially relates to the manufacture method of a kind of wood grain, marbled glass.
Background technology
At present, it is very general that decoration, furniture use marble, but marble costs an arm and a leg, resource-constrained, for this reason, Scagliola occurred.As October 3 nineteen ninety disclosed publication number be that CN1045760A, the patent No. are 89105259.3 Chinese invention patent parian board fabrication method and purposes, disclose a kind of manufacture method of Scagliola, this method flows it and forms marble grain for be coated with the paint with distinct colors between two blocks of glass.But this method cost height is difficult to produce in batches.
Summary of the invention
Technical problem to be solved by this invention is to provide the manufacture method of a kind of wood grain, marbled glass, produces Scagliola, wood grain glass low price with this method, produces simple.
For solving the problems of the technologies described above, the technical solution adopted in the present invention is:
The manufacture method of a kind of wood grain, marbled glass is provided, and this method may further comprise the steps:
A, spray base:
(1) at an amount of transparent glass special-use polish oil of spraying on glass;
(2) the spraying back was baking oven baking 20-50 minute, and storing temperature is 70-80 degree centigrade;
(3) take out glass and reduce to room temperature;
B, film activation:
Water coating transfer film is tiled on the transfer printing tank water surface, places on the picture and text course, in the evenly spraying of picture and text surface, make the activation of picture and text layer, be easy to separate with carrier thin film with activator.
C, water coating transfer printing:
To need the glass of water coating transfer printing, press close to water coating transfer film gradually along its profile, the picture and text layer under the effect of hydraulic pressure attached to the glass light oil coating on;
D, arrangement:
Glass is taken out from the transfer printing tank, remove residual film, do not have the floating layer of set with the clear water flush away;
E, drying:
Remove glass surface moisture, carry out drying with blower or baking oven;
F, coloured enamel:
Be coated with colored paint on the transfer printing layer surface, dry or seasoning, with the limit of glass and not the spraying surface-conditioning totally get final product.
Further improvement in the technical proposal is:
Described glass special-use polish oil, quantity for spray are every square metre of 20-100 gram.
Described water temperature 20-40 degree centigrade.
Described coloured enamel quantity for spray is every square metre of a 50-200 gram.
Described activator is the organic solvent based on aromatic hydrocarbon.
The invention has the beneficial effects as follows: owing to the present invention is an attachment film and be coated with colored paint and form Wood-grain-imitating, marble grain on sheet glass, so low price, produce simple.The wood grain of being produced, marbled glass have beautiful lines, and environmental protection more.
Compare with marble, this glass has following advantage:
1, more brief.Marble generally more than 20 millimeters, seems heavy in furniture applications, marbling glass generally just can provide enough intensity at the 8-12 millimeter.
2, low price.Price with marbled glass of beautiful decorative pattern has only 1/5th or 1/10th of natural marble.
3, in all parians, the physicals of this product is near marble.At present, the parian on the market is many, and its hardness, scratch resistance and anti-staining property are more far short of what is expected than marble with resin main body not, but because the front of parian glass is a glass, so its hardness scratch resistance and anti-staining property are better than marble.
4, more environmental protection, marble contains radioactive substance, and people healthyly also are on the hazard when enjoying marble and bringing aesthetic feeling.Parian glass does not have radioactivity, and employed coating also is environmental protection coating material, through high bake VOC content far below national standard.In addition, coating is at the back side of glass, and human body is directly contact not.
And wood grain glass is fused to the advantage of traditional grain board and glass together, compares with pasting wood grain furniture, and this glass has following advantage:
1, the glittering and translucent sensation of giving people U.S. of wood grain glass;
2, gloss, wear-resisting, damage resistant;
3, water-tolerant can be done outdoor furniture and finishing is used;
4, more environmental protection.
Description of drawings
Fig. 1 is film activation synoptic diagram;
Fig. 2 is a water coating transfer printing synoptic diagram;
Fig. 3 is wood grain, marbled glass structure iron.
Below in conjunction with accompanying drawing the present invention is described further:
Embodiment
See also Fig. 1,2:
The manufacture method step of wood grain of the present invention, marbled glass is as follows:
The first step, spray base:
At an amount of transparent glass special-use polish oil of spraying on glass, quantity for spray is every square metre of a 20-100 gram; The spraying back was baking oven baking 20-50 minute, and storing temperature is 70-80 degree centigrade; It is stand-by that taking-up glass is reduced to room temperature;
Second step, film activation:
Water coating transfer film is tiled on the transfer printing tank water surface, place on the picture and text course, keep the water cleaning in the tank, and be in neutral state substantially, use activator in the evenly spraying of picture and text surface, make the activation of picture and text layer, be easy to separate with carrier thin film, activator can dissolve and destroy polyvinyl alcohol rapidly for the organic solvent based on aromatic hydrocarbon, but can not destroy the picture and text layer, make picture and text be in unbound state.
Film activation principle is seen Fig. 1, and wherein 1 is tank, and 2 is water coating transfer film, and 3 is activator.
The 3rd step, water coating transfer printing:
To need the glass of water coating transfer printing, press close to water coating transfer film gradually along its profile, the picture and text layer is slowly transferred to glass surface under the effect of hydraulic pressure, owing to the effect of sticking of ink lay and specific coatings inherent produces sticking power.In the transfer process, the speed of stock and water coating transfer film will keep evenly, avoids the film gauffer and makes picture and text not attractive in appearance.Say in principle, should guarantee the stretching that picture and text are suitable, avoid overlapping as far as possible, particularly the junction is overlapping too much, can give mixed and disorderly sensation.Fu Za product is high more to the requirement of operation.
Water temperature is the important factor that influences transfer quality, and it's the end is past water temperature, may make the decreased solubility of base material film, and water temp is too high to cause damage to picture and text again easily, causes the picture and text distortion.The scope that water temperature is suitable is 20-40 degree centigrade, can adopt automatic temperature control apparatus, and water temperature is controlled in the stable scope.Water coating transfer process is seen Fig. 2, and wherein, 1 is tank, and 2 is water coating transfer film, and 3 is activator, and 4 is the glass light oil coating, and 5 is glass.
The 4th step, arrangement:
Glass is taken out from the transfer printing tank, remove residual film, do not have the floating layer of set with the clear water flush away.Notice that hydraulic pressure can not be too big, otherwise the picture and text of transfer printing are caused damage.
The 5th step, drying:
Remove glass surface moisture, be beneficial to the finish-drying of transfer ink layer, for increasing sticking power, available blower or baking oven carry out drying.
The 6th goes on foot, is sprayed with colored paint:
Be coated with colored paint on the transfer printing layer surface, dry or seasoning, with the limit of glass and not the spraying surface-conditioning totally get final product.Coloured enamel is selected different lacquers for use according to different wood grains, marble grain, and general dark wood grain adopts the coffee colored paint, and marble is selected white paint for use.The coloured enamel quantity for spray is every square metre of a 50-200 gram.The glass surface of never spraying paint just can be seen wood grain true to nature or marble grain.Wood grain marble line glass structure is seen Fig. 3.5 is glass, and 4 is the glass light oil coating, and 2 is the water transfer printing layer, and 6 is the colored paint coating.
Claims (5)
1. the manufacture method of a wood grain, marbled glass, it is characterized in that: this method may further comprise the steps:
A, spray base:
(1) at an amount of transparent glass special-use polish oil of spraying on glass;
(2) the spraying back was baking oven baking 20-50 minute, and storing temperature is 70-80 degree centigrade;
(3) take out glass and reduce to room temperature;
B, film activation:
Water coating transfer film is tiled on the transfer printing tank water surface, places on the picture and text course, in the evenly spraying of picture and text surface, make the activation of picture and text layer, be easy to separate with carrier thin film with activator;
C, water coating transfer printing:
To need the glass of water coating transfer printing, press close to water coating transfer film gradually along its profile, the picture and text layer under the effect of hydraulic pressure attached to the glass light oil coating on;
D, arrangement:
Glass is taken out from the transfer printing tank, remove residual film, do not have the floating layer of set with the clear water flush away;
E, drying:
Remove glass surface moisture, carry out drying with blower or baking oven;
F, be sprayed with colored paint:
Be coated with colored paint on the transfer printing layer surface, dry or seasoning, with the limit of glass and not the spraying surface-conditioning totally get final product.
2. the manufacture method of wood grain as claimed in claim 1, marbled glass is characterized in that: described glass special-use polish oil, quantity for spray are every square metre of 20-100 gram.
3. the manufacture method of wood grain as claimed in claim 1, marbled glass is characterized in that: described water temperature 20-40 degree centigrade.
4. the manufacture method of wood grain as claimed in claim 1, marbled glass is characterized in that: described coloured enamel quantity for spray is every square metre of a 50-200 gram.
5. the manufacture method of wood grain as claimed in claim 1, marbled glass is characterized in that: described activator is the organic solvent based on aromatic hydrocarbon.