CN109052983A - A kind of production method of imitation wood line, marble glass brick - Google Patents
A kind of production method of imitation wood line, marble glass brick Download PDFInfo
- Publication number
- CN109052983A CN109052983A CN201811173513.7A CN201811173513A CN109052983A CN 109052983 A CN109052983 A CN 109052983A CN 201811173513 A CN201811173513 A CN 201811173513A CN 109052983 A CN109052983 A CN 109052983A
- Authority
- CN
- China
- Prior art keywords
- glass
- brick
- coating
- production method
- imitation wood
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to ornament materials preparation technical field, the production method of especially a kind of imitation wood line, marble glass brick specifically includes following procedure: (1) pretreatment of glass, the preparation of (2) glass coating；(3) glass coating；(4) preparation of heat transfer；(5) thermal transfer；(6) stopping off paints.The present invention is handled glass using ultrasonic wave during glass coating, the absorption property of glass surface can be improved, the surface of glass block is set preferably to bond with figure layer, to make glass block surface more closely be combined with heat transfer, sublimable ink on heat-transferring printing paper can preferably be adsorbed on glass block surface, be beneficial to improve the three-dimensional sense of image；The back side that heat transfer is smeared using the hydrophobic coating being mixed by organic siliconresin and acetone can prevent image color caused by sublimable ink is reversely spread during thermal transfer light since hydrophobic coating has heat resistance, hydrophobicity, increases oiliness.
Description
Technical field
The invention belongs to ornament materials preparation technical field, especially a kind of production of imitation wood line, marble glass brick
Method.
Background technique
Glass block is the bulk being pressed into transparent or coloured glass material or hollow box-like, the biggish glassware of body,
Have many advantages, such as daylighting, high intensity, antistatic, environmental protection, corrosion-resistant, acid and alkali-resistance, be not afraid of water logging knife cut, it is easy to clean health, it is wide
It is general to be used for ornament materials.Currently, glass block in the market is broadly divided into two kinds: sand is cut glass brick, stained glass bricks, and work is produced
Skill is all first to stick at dedicated gummed paper on glass block face, profile is carved out further according to patterning requirement, then according to actual production need
It asks, figure needed for being sprayed with dry powder sand-blasting machine finally uses color spray rifle paint color on the pattern of glass block.This production work
The glass block that skill obtains there are dim pattern, it is out of shape, opaque, three-dimensional sense is bad the disadvantages of, and automation degree is low, labour is strong
Degree is big, production efficiency is low.
In order to solve problem above, relevant report proposes a kind of caloric transfer printing technology, it is first that design is good, then make
Ink is uniformly coated to form pattern on thermal transfer film by the targeted graphical with coating machine according to setting, then passes through thermal transfer
Machinery is transferred to pattern on glass.File if number of patent application is CN201110410452.3 discloses a kind of hollow glass
Brick thermal transfer coating and caloric transfer printing technology, manufacture craft include: to carry out high-light transparent coating and white on hollow glass surface
The coating of coating utilizes aluminium foil bag, silicon with heat sublimation ink in paper substrates or polymeric membrane substrate or press figure image
Adhesive tape vacuumize encapsulation need the hollow glass block of thermal transfer in conjunction with print or printed substrate with heated baking equipment come
Carry out the transfer of image；By to hollow brick glass carry out high adhesion, good weatherability, low energy consumption thermal transfer coating painting
Dress, then with the technology mode of thermal transfer by full-color digital image transfer to hollow glass block, it can be by the pattern on transfer paper
It improves and is transferred on glass block；But during thermal transfer, the ink of pattern is by natural sublimation transfer to hollow glass
On brick, it cannot be fully adsorbed on glass surface, three-dimensional sense is poor, and is easy to happen colour fading.
Summary of the invention
In order to solve the above technical problems existing in the prior art, the present invention provides a kind of imitation wood lines, marble grain
The manufacturing method of brick is realized particular by following technical scheme:
A kind of production method of imitation wood line, marble grain brick, specifically includes the following steps:
(1) pretreatment of glass: taking glass, is cut, edging, cleaning, drying, obtains plate glass brick；It will put down again
Glass sheet brick carries out tempering and obtains tempered glass brick；
(2) glass coating is prepared: transparent glass priming paint, curing agent, diluent being mixed and made into clear dope, by white glass
Glass priming paint, curing agent, diluent are mixed and made into white coating；
(3) glass coating: transparent on silk-screen after the resulting tempered glass brick ultrasonication 10-15min of step (1)
Coating, it is dry, form clear coat；Then dry in clear coat surface silk-screen white coating, form white coating；
(4) preparation of heat transfer: design wood grain, marble grain image, with heat sublimation ink by image printing or printing
One layer of hydrophobic coating is coated onto paper substrate, then at the back side of paper substrate, 10-15min is stood, obtains heat transfer；
(5) thermal transfer: turning heat figure and be closely attached on the white coating of tempered glass brick, after keeping smooth with heatproof without
Trace adhesive tape fixes glass and thermal transfer drawing；Then start thermal transfer furnace, according to the thickness of glass block set thermal transfer temperature,
After the thermal transfer time, glass block is placed on siege, furnace center is sent into and starts hot pressing；
(6) stopping off: protection is coated at normal temperature after examining product qualified to glass, cooling is taken out to hot pressing time
Layer paint is to get imitation wood line, marble glass brick.
Preferably, the tempering of the plate glass brick is that plate glass brick is placed in heating furnace to be heated to 650 DEG C or so,
Then glass is taken out, then high pressure cold air is blowed to the two sides of glass with bull nozzle, be cooled to it rapidly and uniformly
Room temperature.
Preferably, the step (3), the frequency of ultrasonic wave are 80-100kHz.
Preferably, the step (2), the transparent glass priming paint is epoxy gloss oil, white glass priming paint is ring
Oxygen paint, curing agent are paint curing agent, diluent is dilution slow curing water.
Preferably, the clear dope is mixed by transparent glass paint, curing agent, diluent by the mass ratio of 2:1:1.2
It is made.Transparent glass paint, curing agent, diluent three proportion are improper, will lead to that adsorption capacity of the pattern on glass be strong, hardness
It is not high with finish.The present invention by related experiment find, transparent glass paint, curing agent, diluent ratio be 2:1:1.2
For optimal selection.
Preferably, the white coating is mixed by white glass paint, curing agent, diluent by the mass ratio of 3:1:1.3
It is made.White glass paint, curing agent, diluent three proportion are improper, will lead to that coloring effect of the pattern on glass be poor, figure line
Unintelligible distinct, lines are not fine, three-dimensional sense is not strong etc..The present invention by related experiment find, white glass paint, curing agent,
The ratio of diluent is that 3:1:1.3 is optimal selection.
Preferably, the step (4), the hydrophobic coating are to form organic siliconresin and acetone high-speed stirred,
Wherein the mass ratio of organic siliconresin and acetone is 1:5-6.
Preferably, the step (5), glass block with a thickness of 5-15mm, thermal transfer temperature is 155-240 DEG C, and heat turns
The print time is 220-960s, pressure 0.3-0.8Mpa.The present invention is found through experiments that the thickness of glass is different, and heat turns temperature
Degree, print time, pressure are also different, 155-240 DEG C of the architectural grade glass required temperature of general 5-15mm thickness, hot pressing time
220-960s, pressure 0.3-0.8Mpa.
Preferably, protective layer paint is common neutral paint.
Preferably, the imitation wood line, marble glass brick can use decorative floor tiles and wall brick.
The beneficial effects of the present invention are: tempering processing is carried out to glass block, its intensity can not only be enhanced, moreover it is possible to eliminate it
The defect on surface makes its surface have better absorption property；The glass block of tempering is ultrasonically treated, can be further improved
The absorption property on its surface；Therefore, after by tempering, ultrasonic treatment, glass block can preferably be glued with clear coat, white coating
It closes, and then glass block and heat-transferring printing paper are closer in combination, the sublimable ink on heat-transferring printing paper can preferably be adsorbed on glass block
Surface is beneficial to improve the three-dimensional sense of image.The hydrophobic coating that organic siliconresin and acetone are mixed has heat resistance, hates
Aqueous, increasing oiliness, the back side of heat transfer is smeared using it, can prevent sublimable ink during thermal transfer from reversely spreading and causing
Image color it is light.During thermal transfer, thermal transfer time, temperature are arranged according to the thickness of glass block, glass has been taken into account and has added
The uniformity and the validity of time of heat, it is ensured that the coloring effect of thermal transfer glass.Imitation wood line, the marble grain that the present invention makes
Glass ceramic tile, figure line is clear, the lines flow smoothly finely, three-dimensional sense is strong, and texture is felt rich in sense of movement and variation, and anti-oxidant effect
Fruit, not fugitive color.
Detailed description of the invention
Fig. 1 is the structure of glass block, and 1 is glass, and 2 be clear coat, and 3 be white figure layer, and 4 be wood grain, marble grain, 5
For protective layer.
Fig. 2 is imitation wood line glass brick product prepared by the present invention.
Fig. 3 is marbling glass brick product prepared by the present invention.
Specific embodiment
It is limited below with reference to specific embodiment technical solution of the present invention is further, but claimed
Range is not only limited to made description.
1 glass coating of embodiment
Clear dope, white coating are prepared by the weight of table 1.
Table 1
2 imitation wood line glass block of embodiment
Production method:
(1) pretreatment of glass: taking glass, is cut, edging, cleaning, drying, obtains plate glass brick；It will put down again
Glass sheet brick is placed in heating furnace and is heated to 650 DEG C or so, then takes out glass, then is blowed to high pressure cold air with bull nozzle
The two sides of glass, is cooled to room temperature it rapidly and uniformly, obtains with a thickness of the tempered glass brick of 5,8,10,12,15mm；
(2) glass coating: after the resulting tempered glass brick ultrasonication 10min of step (1), silk-screen embodiment 1 is made
Standby clear dope, it is dry, form clear coat；Then the white coating prepared in clear coat surface silk-screen embodiment 1 is done
It is dry, form white coating；Wherein, the frequency of ultrasonic wave is 100kHz
(3) preparation of heat transfer: design wood grain image by image printing or prints to paper substrate with heat sublimation ink
On, then at the back side of paper substrate coat one layer of hydrophobic coating, 10min is stood, heat transfer is obtained；Wherein the hydrophobic applies
Material is formed by 100g organic siliconresin, 500g acetone high-speed stirred；
(4) thermal transfer: turning heat figure and be closely attached on the white coating of tempered glass brick, after keeping smooth with heatproof without
Trace adhesive tape fixes glass and thermal transfer drawing；Then start thermal transfer furnace, according to the thickness of glass block set thermal transfer temperature,
It is specific that glass block is placed on siege as shown in table 2 after the thermal transfer time, it is sent into the pressure of furnace center 0.3-0.8MPa
Power hot pressing；
(5) it stopping off: is coated at normal temperature after examining product qualified common to hot pressing time to glass, cooling is taken out
Neutrality paint is to get imitation wood line glass block.
2 thermal transfer temperature of table, hot pressing time table
| Thickness of glass (mm) | Thermal transfer temperature (DEG C) | Hot pressing time (s) |
| 5 | 155~165 | 220~280 |
| 8 | 165~180 | 300~350 |
| 10 | 170~185 | 430~520 |
| 12 | 175~190 | 480~600 |
| 15 | 180~240 | 630~960 |
3 marbling glass block of embodiment
Production method:
(1) pretreatment of glass: taking glass, is cut, edging, cleaning, drying, is obtained with a thickness of plate glass brick；
Plate glass brick is placed in heating furnace again and is heated to 650 DEG C or so, then takes out glass, then with bull nozzle by the cold sky of high pressure
Air-blowing is cooled to room temperature it rapidly and uniformly to the two sides of glass, obtains the tempered glass brick of 5,8,10,12,15mm；
(2) glass coating: after the resulting tempered glass brick ultrasonication 15min of step (1), silk-screen embodiment 1 is made
Standby clear dope, it is dry, form clear coat；Then the white coating prepared in clear coat surface silk-screen embodiment 1 is done
It is dry, form white coating；Wherein, the frequency of ultrasonic wave is 80kHz；
(3) preparation of heat transfer: design wood grain image by image printing or prints to paper substrate with heat sublimation ink
On, then at the back side of paper substrate coat one layer of hydrophobic coating, 15min is stood, heat transfer is obtained；Wherein the hydrophobic applies
Material is formed by 100g organic siliconresin, 600g acetone high-speed stirred；
(4) thermal transfer: turning heat figure and be closely attached on the white coating of tempered glass brick, after keeping smooth with heatproof without
Trace adhesive tape fixes glass and thermal transfer drawing；Then start thermal transfer furnace, according to the thickness of glass block set thermal transfer temperature,
It is specific that glass block is placed on siege as shown in table 2 after the thermal transfer time, it is sent into the pressure of furnace center 0.3-0.8MPa
Power hot pressing；
(5) it stopping off: is coated at normal temperature after examining product qualified common to hot pressing time to glass, cooling is taken out
The glass block that neutrality is painted to get marbling.
It is important to point out that, above embodiments and test example are only limitted to do further technical solution of the present invention herein
Elaboration and understanding, should not be understood as it is further to technical solution of the present invention limited, what those skilled in the art made
The innovation and creation of non-protruding essential characteristics and marked improvement still fall within protection category of the invention.
Claims (10)
1. the production method of a kind of imitation wood line, marble grain brick, specifically includes the following steps:
(1) pretreatment of glass: taking glass, is cut, edging, cleaning, drying, obtains plate glass brick；Again by plate glass
Glass brick carries out tempering and obtains tempered glass brick；
(2) glass coating is prepared: transparent glass priming paint, curing agent, diluent being mixed and made into clear dope, by white glass bottom
Paint, curing agent, diluent are mixed and made into white coating；
(3) glass coating: after the resulting tempered glass brick ultrasonication 10-15min of step (1), clear dope on silk-screen,
It is dry, form clear coat；Then dry in clear coat surface silk-screen white coating, form white coating；
(4) preparation of heat transfer: design wood grain, marble grain image by image printing or print to paper with heat sublimation ink
It on substrate processed, then at the back side of paper substrate coats one layer of hydrophobic coating, stands 10-15min, obtain heat transfer；
(5) thermal transfer: turning figure for heat and be closely attached on the white coating of tempered glass brick, uses the seamless glue of heatproof after keeping smooth
Band fixes glass and thermal transfer drawing；Then start thermal transfer furnace, thermal transfer temperature is set according to the thickness of glass block, heat turns
After printing the time, glass block is placed on siege, furnace center is sent into and starts hot pressing；
(6) stopping off paints: coating protection at normal temperature after examining product qualified to glass, cooling is taken out to hot pressing time
Layer paint is to get imitation wood line, marble glass brick.
2. the production method of imitation wood line as described in claim 1, marble grain brick, which is characterized in that the plate glass
The tempering of brick is that plate glass brick is placed in heating furnace to be heated to 650 DEG C or so, then takes out glass, then will with bull nozzle
High pressure cold air blows to the two sides of glass, is cooled to room temperature it rapidly and uniformly.
3. the production method of imitation wood line as described in claim 1, marble grain brick, which is characterized in that the step (3),
The frequency of ultrasonic wave is 80-100kHz.
4. the production method of imitation wood line as described in claim 1, marble grain brick, which is characterized in that the step (2),
The transparent glass priming paint is epoxy gloss oil, white glass priming paint is epoxy paint, curing agent is paint curing agent, dilute
Agent is released as dilution slow curing water.
5. the production method of imitation wood line as described in claim 1, marble grain brick, which is characterized in that the clear dope
It is mixed by transparent glass paint, curing agent, diluent by the mass ratio of 2:1:1.2.
6. the production method of imitation wood line as described in claim 1, marble grain brick, which is characterized in that the white coating
It is mixed by white glass paint, curing agent, diluent by the mass ratio of 3:1:1.3.
7. the production method of imitation wood line as described in claim 1, marble grain brick, which is characterized in that the step (4),
The hydrophobic coating is to form organic siliconresin and acetone high-speed stirred, and wherein the mass ratio of organic siliconresin and acetone is
1:5-6。
8. the production method of imitation wood line as described in claim 1, marble grain brick, which is characterized in that the step (5),
Glass block with a thickness of 5-15mm, thermal transfer temperature is 155-240 DEG C, and the thermal transfer time is 220-960s, pressure 0.3-
0.8MPa。
9. the production method of imitation wood line as described in claim 1, marble grain brick, which is characterized in that the protective layer oil
Paint is common neutral paint.
10. the production method of imitation wood line as described in claim 1, marble grain brick, which is characterized in that the imitation wood line,
Marble glass brick can be used for decorative floor tiles and wall brick.