CN102617170A - 一种用于回转窑在线快速修补料 - Google Patents
一种用于回转窑在线快速修补料 Download PDFInfo
- Publication number
- CN102617170A CN102617170A CN2012100982082A CN201210098208A CN102617170A CN 102617170 A CN102617170 A CN 102617170A CN 2012100982082 A CN2012100982082 A CN 2012100982082A CN 201210098208 A CN201210098208 A CN 201210098208A CN 102617170 A CN102617170 A CN 102617170A
- Authority
- CN
- China
- Prior art keywords
- percent
- repair material
- rotary kiln
- quick repair
- line quick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种用于回转窑在线快速修补料。其组分及重量百分比含量为:Al2O3:55~85%,SiO2:10~25%,MgO:0.1~15%,Fe:0.01~5%,Al:0.01~3%,Fe2O3:0.1~3%,硅溶胶结合剂占上述总量的8~20%。本发明能实现在线喷补,对炉衬基础无需进行清理进行喷补,修补质量稳定,不易产生脱落现象,维修费用由目前的一次需要数十万元降低至几万元,即约为十分之一,并使使用周期可提高50%及以上。
Description
技术领域
本发明涉及一种耐火材料修补料,具体属于一种用于回转窑在线快速修补料。
背景技术
回转窑的使用周期如球团回转窑目前一般只有2年左右,其破坏最严重的部位常出现在窑头、窑尾。目前窑头修补常采用将回转窑停产并冷却后进行半干法喷补,其修补料采用过水玻璃结合的高铝材料。采用半干法喷补的不足是:需要机组停止作业,并检修维护用时长,导致机组作业率降低,并且大修费用可达上千万元;过水玻璃结合的高铝材料存在的不足是:在高温下粘接不牢固,对炉衬要求严格,既要进行清理,否则炉衬基础太脏时,容易造成喷补层脱落。
经检索,有资料报道显示,也有用于回转窑的修补料,其为溶胶结合的矾土、氧化镁质材料,其存在的不足是高温下修补有一定效果,但在球团回转窑热态下修补,会导致烧结速度慢,强度比较低,因此效果不理想。中国专利申请号为申请号: CN200810226854.6的专利文献,其公开了一种工作衬用可塑修补料,该修补料的主料及重量百分比为:5~70%的高铝矾土,20~90%的刚玉,4~20%的氧化镁,主料外另加占主料重量5~20%的硅溶胶。高铝矾土的粒度不大于10mm,Al2O3含量不小于80%;刚玉包括棕刚玉、亚白刚玉、板状刚玉及电熔白刚玉等;氧化镁包括中档镁砂、高纯镁砂及电熔镁砂等,其MgO含量不小于93.0%;硅溶胶溶液,SiO2含量为20.0%~40.0%,Na2O含量不大于0.4%,pH范围为8.5~12。这种修补料只依靠溶胶结合,在热态使用可以粘接,但耐磨性差,难以快速烧结。中国专利申请号为CN200810196814.1的专利文献,其涉及并公开了一种溶胶结合耐火修补材料及修补方法,其所述溶胶结合耐火修补材料的组分及重量份为:修补料基体:55~90份,碳化硅:0~35份,氧化硅及氧化铝的微粉:3~8份,溶胶:3~20份,促进凝固剂0.02~5份。 所述修补料基体由重量百分数为50%~85%的粗骨料和15%~50%的粉料组成,所述修补料基体中的粗骨料是粒度为1~10mm的刚玉、莫来石、矾土、焦宝石、粘土或其混合物。所述修补料基体中的粉料为刚玉、莫来石、矾土、焦宝石或其混合物。CN200810196814.1的专利文献所存在的不足同CN200810226854.6的专利文献,均为只依靠溶胶结合,在热态使用可以粘接,但耐磨性差,难以快速烧结。中国专利申请号为CN201010290322.6的专利文献,其公开了一种回转窑炉衬修补料,它是由原料氧化铝、碳化硅、二氧化锆和莫来石按照下述重量百分比配制而成:氧化铝50~70%;碳化硅20~35%;二氧化锆5~7%;莫来石5~10%。所述氧化铝的粒度为1~3μm;碳化硅的粒度为1~3μm;二氧化锆的粒度为1~5μm;莫来石的粒度为1~3μm。将上述各原料粉碎研磨至粉料后,在搅拌机中混合均匀,装袋存放待用。该发明但没有结合剂,即使用水作为结合剂也不会产生强度,认为无法使用。
本发明则能够克服上述发明的缺点,通过采用硅溶胶结合,并加入一定量的金属粉末,利用快速热固化熔融反应粘接到炉衬上,形成快速修补层,对于掉砖处、凹坑处的修补效果良好。
发明内容
本发明在于克服目前存在的不足,提供一种能高温在线喷补,对炉衬基础无需进行清理,修补处不易脱落的一种用于回转窑在线快速修补料。
实现上述目的的措施:
一种用于回转窑在线快速修补料,其组分及重量百分比含量为:Al2O3: 55~85%,SiO2 :10~25%,MgO :0.1~15%,Fe:0.01~5%,Al:0.01~3%,Fe2O3 :0.1~3%,硅溶胶结合剂占上述总量的8~20%。
本发明与现有技术相比,能实现在线喷补,对炉衬基础无需进行清理进行喷补,修补质量稳定,不易产生脱落现象, 维修费用由目前的一次需要数十万元降低至几万元,即约为十分之一,并使使用周期可提高50%及以上。
具体实施方式
下面对本发明予以详细描述:
实施例1
一种用于回转窑在线快速修补料,其组分及重量百分比含量为:Al2O3: 55%,SiO2 :25%,MgO :10%,Fe:4%,Al:3%,Fe2O3 :3%,硅溶胶结合剂占上述总量的8%。
实施例2
一种用于回转窑在线快速修补料,其组分及重量百分比含量为:Al2O3: 59%,SiO2 :22%,MgO:15%,Fe:0.01%,Al:2.99%,Fe2O3:1%,硅溶胶结合剂占上述总量的12%。
实施例3
一种用于回转窑在线快速修补料,其组分及重量百分比含量为:Al2O3: 66%,SiO2 :18%,MgO:14%,Fe:0.8%,Al:1%,Fe2O3:0.2%,硅溶胶结合剂占上述总量的15%。
实施例4
一种用于回转窑在线快速修补料,其组分及重量百分比含量为:Al2O3: 76%,SiO2 :10%,MgO:8%,Fe:3%,Al:0.02%,Fe2O3:2.98%,硅溶胶结合剂占上述总量的17%。
实施例5
一种用于回转窑在线快速修补料,其组分及重量百分比含量为:Al2O3: 81%,SiO2 :13%,MgO:0.1%,Fe:5%,Al:0.2%,Fe2O3:0.7%,硅溶胶结合剂占上述总量的16%。
实施例6
一种用于回转窑在线快速修补料,其组分及重量百分比含量为:Al2O3: 85%,SiO2 :10%,MgO:0.9%,Fe:3.99%,Al:0.01%,Fe2O3:0.1%,硅溶胶结合剂占上述总量的20%。
在使用时,用水调节其粘度即可。
上述各实施例试验后,经试验检测,其结果:
Claims (1)
1.一种用于回转窑在线快速修补料,其组分及重量百分比含量为:Al2O3: 55~85%,SiO2 :10~25%,MgO :0.1~15%,Fe:0.01~5%,Al:0.01~3%,Fe2O3 :0.1~3%,硅溶胶结合剂占上述总量的8~20%。