CN102616752A - 一种过碳酸钠防结块剂组合物及其应用 - Google Patents
一种过碳酸钠防结块剂组合物及其应用 Download PDFInfo
- Publication number
- CN102616752A CN102616752A CN2012100544872A CN201210054487A CN102616752A CN 102616752 A CN102616752 A CN 102616752A CN 2012100544872 A CN2012100544872 A CN 2012100544872A CN 201210054487 A CN201210054487 A CN 201210054487A CN 102616752 A CN102616752 A CN 102616752A
- Authority
- CN
- China
- Prior art keywords
- agent
- spc
- caking agent
- hard caking
- sodium percarbonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种过碳酸钠防结块剂组合物,其特征在于:所述过碳酸钠防结块剂组合物由分散剂、渗透剂和憎水剂组成,分散剂、渗透剂和憎水剂的质量百分比为:45~70:20~40:5~15。本发明还提供该防结块在制备防结块过碳酸钠中的应用。本发明的过碳酸钠防结块剂组合物用量少,生产成本低,防结块效果优良。防结块剂的添加不影响过碳酸钠的稳定性及各种使用要求,还具有助洗功能,而且对环境无毒害,适合于工业化生产使用。
Description
技术领域
本发明属于无机盐的技术领域,具体涉及一种用于过碳酸钠的防结块剂组合物及其应用技术。
背景技术
过碳酸钠又名过氧化碳酸钠,是碳酸钠和过氧化氢的加成复合物,为白色松散流动性好的颗粒状固体。作为新型高效洗涤漂白剂,它具有无臭、无毒、无污染的特点。由于在水中分解产生的活性氧具有漂白作用,过碳酸钠表现出很强的去污能力,因此同传统磷系、硼系洗涤助剂相比,不仅去污力强,而且不会破坏生态环境,目前已成为世界上广泛应用的主要洗涤助剂之一。
目前,过碳酸钠的生产方法主要有干法和湿法两种:干法生产是将过氧化氢的水溶液直接喷雾到无水碳酸钠固体上而制得过碳酸钠晶体;湿法生产是用饱和的碳酸钠溶液跟一定浓度的双氧水在添加适量的稳定剂及一定的温度条件下进行反应,然后经结晶、过滤、干燥得到产品。但无论采用上述哪种方法生产的过碳酸钠晶体,都存在结块问题,给工业使用过程中连续给料和精确计量带来不便。引起过碳酸钠结块的因素很多,主要原因是过碳酸钠中含有一定量水分,由于过碳酸钠储运期间的温度、湿度、压力等因素的变化,在过碳酸钠晶体表面易反复产生溶解—结晶—再溶解—再结晶的情况,使晶体间产生“晶桥”现象,引起结块。
在实际工业生产中,为了控制过碳酸钠产品的结块,一般可通过成品分级筛分、干燥方式选择、包装环境控制、贮存环境选择等手段来解决。专利CN1729282公开了一种具有改进的贮存稳定性的过碳酸钠颗粒,通过混合过碳酸钠颗粒与其表面疏水化的细碎元素硅、铝或钛的氧化物而制备,具有高贮存稳定性,无颗粒的结块,但是防结块效果不够理想。另外对过碳酸钠涂覆外用稳定剂在提高产品热稳定性和湿稳定性的同时,对其抗结块性能也有一定的提升。而向过碳酸钠晶体中加入防结块剂是解决其结块的重要手段。
发明内容
为了克服现有技术中的上述缺陷,本发明提供了一种过碳酸钠防结块剂组合物,该防结块剂用量少,生产成本低,添加工艺简单,防结块效果优良,防结块剂的添加不影响过碳酸钠的稳定性及各种使用要求,还具有助洗功能,而且对环境无毒害。
一种过碳酸钠防结块剂组合物,其特征在于:所述过碳酸钠防结块剂组合物由分散剂、渗透剂和憎水剂组成,分散剂、渗透剂和憎水剂的质量百分比为:45~70 : 20~40 : 5~15。
所述的分散剂为马来酸—丙烯酸共聚物和聚丙烯酸及其盐中的一种或两种。
所述的渗透剂为烷基苯磺酸及其盐、仲烷基磺酸及其盐和脂肪醇聚氧乙烯醚中的一种或多种。
所述的憎水剂为硬脂酸或硬脂酸钠。
在本发明中,马来酸―丙烯酸共聚物和聚丙烯酸及其盐均具有分散作用,将其用于包裹过碳酸钠晶粒时,在其表面形成致密双电层,使晶粒间相互排斥,晶桥难以产生,起到防结块效果。但是这两种成分都具有一个弱点,就是扩散能力差。通过添加渗透剂,可明显降低上述水溶液的表面能,增加扩散力和速度,使该水溶液雾滴接触到过碳酸钠颗粒的瞬间迅速扩散,使附着在晶粒上的液膜更薄、更匀,所布展的角落更彻底、更充分,从而使防结块剂用量更少、效果更好。憎水剂主要起防潮作用,阻止环境水分进入。
本发明的防结块剂组合物可制成粉剂或水溶液剂型。
本发明的另一个目的在于提供该防结块在制备防结块过碳酸钠中的应用,能够保证防结块剂分布均匀,从而更好地达到防结块效果。
防结块剂组合物在制备防结块过碳酸钠中的应用,其特征在于:将防结块剂用水溶解后均匀涂覆到过碳酸钠颗粒表面,或将防结块剂制成粉剂与过碳酸钠混合。
进一步地,将防结块剂用水配制成质量分数为1~40%的溶液,均匀涂覆到过碳酸钠颗粒表面。
在上述应用中,所述防结块剂与过碳酸钠颗粒质量比优选为0.05~0.5%。
所述过碳酸钠颗粒度为0.15~1.5毫米,优选为0.3~1.2毫米,水分含量为0~2%。
本发明提供的过碳酸钠防结块剂用量少,生产成本低,添加工艺简单,防结块效果优良。防结块剂的添加不影响过碳酸钠的稳定性及各种使用要求,还具有助洗功能,而且对环境无毒害,适合于工业化生产使用。
具体实施方式
下面结合实施例对本发明作进一步的描述。
实施例1
过碳酸钠防结块剂各组分质量百分比为:
70% 分散剂:45%马来酸—丙烯酸共聚物,25%聚丙烯酸钠;
25% 渗透剂:15%烷基苯磺酸钠,10%脂肪醇聚氧乙烯醚;
5% 憎水剂:硬脂酸钠。
将各组分按上述配比量配备后,混合均匀得防结块剂。按过碳酸钠总质量的0.5%加入防结块剂,具体添加方式为:将上述防结块剂溶解于水配成溶液,经流化床喷涂装置将防结块剂溶液均匀涂覆于过碳酸钠颗粒表面,制得防结块过碳酸钠。另将上述配比的防结块剂粉碎制成粉剂后,与过碳酸钠颗粒均匀混合,制得防结块过碳酸钠。
所得防结块过碳酸钠用吨袋包装,压包进行储存6个月后,产品均无结块。
实施例2
过碳酸钠防结块剂各组分质量百分比为:
60% 分散剂:马来酸—丙烯酸共聚物;
35% 渗透剂:15%烷基苯磺酸钠,10%仲烷基磺酸钠,10%脂肪醇聚氧乙烯醚;
5% 憎水剂:硬脂酸钠。
将各组分按上述配比量配备后,混合均匀得防结块剂。按过碳酸钠总质量的0.05%加入防结块剂,其他操作同实例1。
所得防结块过碳酸钠用吨袋包装,压包进行储存6个月后,产品均无结块。
实施例3
过碳酸钠防结块剂各组分质量百分比为:
60% 分散剂:马来酸—丙烯酸共聚物;
35% 渗透剂:仲烷基磺酸钠;
5% 憎水剂:硬脂酸钠。
将各组分按上述配比量配备后,混合均匀得防结块剂。按过碳酸钠总质量的0.2%加入防结块剂,其他操作同实例1。所得防结块过碳酸钠用吨袋包装,压包进行储存6个月后,产品均无结块。
实施例4
过碳酸钠防结块剂各组分质量百分比为:
50% 分散剂:30%马来酸—丙烯酸共聚物,20%聚丙烯酸钠;
40% 渗透剂:20%烷基苯磺酸钠,10%仲烷基磺酸钠,10%脂肪醇聚氧乙烯醚;
10% 憎水剂:硬脂酸。
将各组分按上述配比量配备后,混合均匀得防结块剂。按过碳酸钠总质量的0.2%加入防结块剂,其他操作同实例1。
所得防结块过碳酸钠用吨袋包装,压包进行储存6个月后,产品均无结块。
实施例5
过碳酸钠防结块剂各组分质量百分比为:
65% 分散剂:35%马来酸—丙烯酸共聚物,30%聚丙烯酸钠;
20% 渗透剂:10%仲烷基磺酸钠,10%脂肪醇聚氧乙烯醚;
15% 憎水剂:硬脂酸。
将各组分按上述配比量配备后,混合均匀得防结块剂。按过碳酸钠总质量的0.2%加入防结块剂,其他操作同实例1。
所得防结块过碳酸钠用吨袋包装,压包进行储存6个月后,产品均无结块。
实施例6
过碳酸钠防结块剂各组分质量百分比为:
50% 分散剂:25%马来酸—丙烯酸共聚物,25%聚丙烯酸钠;
40% 渗透剂:15%烷基苯磺酸钠,15%仲烷基磺酸钠,10%脂肪醇聚氧乙烯醚;
10% 憎水剂:硬脂酸。
将各组分按上述配比量配备后,混合均匀得防结块剂。按过碳酸钠总质量的0.15%加入防结块剂,其他操作同实例1。
所得防结块过碳酸钠用吨袋包装,压包进行储存6个月后,产品均无结块。
以上各试验所选过碳酸钠颗粒度为0.3~1.2毫米,水分2.0%,储存环境温度变化幅度5~35℃,不论采用涂覆和外混合添加方式,均可保证过碳酸钠产品6个月不结块。用本发明制备的过碳酸钠防结块剂是一种用量少,成本低,效率高,易使用,无污染的好产品,该防结块剂的应用还增强了过碳酸钠的助洗功能。
Claims (9)
1.一种过碳酸钠防结块剂组合物,其特征在于:所述过碳酸钠防结块剂组合物由分散剂、渗透剂和憎水剂组成,分散剂、渗透剂和憎水剂的质量百分比为:45~70 : 20~40 : 5~15。
2.如权利要求1所述的过碳酸钠防结块剂组合物,其特征在于:所述的分散剂为马来酸—丙烯酸共聚物和聚丙烯酸及其盐中的一种或两种。
3.如权利要求1所述的过碳酸钠防结块剂组合物,其特征在于:所述的渗透剂为烷基苯磺酸及其盐、仲烷基磺酸及其盐和脂肪醇聚氧乙烯醚中的一种或多种。
4.如权利要求1所述的过碳酸钠防结块剂组合物,其特征在于:所述的憎水剂为硬脂酸或硬脂酸钠。
5.权利要求1-4中任一项所述防结块剂组合物在制备防结块过碳酸钠中的应用,其特征在于:将防结块剂用水溶解后均匀涂覆到过碳酸钠颗粒表面,或将防结块剂制成粉剂与过碳酸钠混合。
6.如权利要求5所述的应用,其特征在于,将防结块剂用水配制成质量分数为1~40%的溶液,均匀涂覆到过碳酸钠颗粒表面。
7.如权利要求5所述的应用,其特征在于,防结块剂与过碳酸钠颗粒质量比为0.05~0.5%。
8.如权利要求5所述的应用,其特征在于,所述过碳酸钠颗粒度为0.15~1.5毫米,水分含量为0~2%。
9.如权利要求8所述的应用,其特征在于,所述过碳酸钠颗粒度为0.3~1.2毫米。