CN102604168A - 一种烟片级标准橡胶 - Google Patents
一种烟片级标准橡胶 Download PDFInfo
- Publication number
- CN102604168A CN102604168A CN2012100263347A CN201210026334A CN102604168A CN 102604168 A CN102604168 A CN 102604168A CN 2012100263347 A CN2012100263347 A CN 2012100263347A CN 201210026334 A CN201210026334 A CN 201210026334A CN 102604168 A CN102604168 A CN 102604168A
- Authority
- CN
- China
- Prior art keywords
- content
- smoked sheet
- rubber
- percent
- plasticity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及化工领域,尤其是一种烟片橡胶,其特征在于用烟片胶加工而成,其杂质含量0.05%-0.08%(m/m),灰份含量0.8%(m/m),氮含量0.6%(m/m),挥发物含量0.8%(m/m),塑性初值≥40,塑性保持率≥60,门尼粘度ML/(1′+4′)100℃为83±10,丙酮抽出物含量2.0-3.5%Wt.铜含量,8mg/kg,锰含量10mg/kg,成品每件35kg,每一托盘1.26吨的标准包装。这种烟片级标准橡胶的生产工艺不仅保留了烟片原有的特性,而且还去除了烟片里含有的大量杂质,指标均一稳定,避免了橡胶质量指标波动大导致的轮胎质量风险,可满足轮胎企业做高端产品的需求。
Description
技术领域
本发明涉及化工领域,尤其是一种烟片橡胶。
背景技术
天然橡胶按形态可以分为两大类:固态天然橡胶(胶片与标准橡胶)和浓缩胶乳。在日常使用中,固态天然橡胶占了绝大部分的比例。 固态天然橡胶按加工方式的不同又可以分为:
标准胶是按国际上统一的理化效能、指标来分级的,这些理化性能包括杂质含量、塑性初值、塑性保持率、氮含量、挥发物含量、灰分含量等六项,其中以杂质含量为主导性指标,依杂质之多少分为5、10、20、50及等外胶等共五个级别。
烟片胶是胶片胶中最具代表性的品种,一直是用量大、应用广的一个胶种,烟片胶一般按外形来分级,分为特级、一级、二级、三级、四级、五级等共六级。和标准橡胶按理化指标分级不同的是,烟片分级均采用目测分级,外观分级因人而异,指标未进行理化试验。烟片胶主要是以优异的拉伸强度、抗撕裂性能、抗老化性能、耐磨性能等被用于轮胎的关键部位,但是烟片在制作过程中本身容易受外界污染,比如泥沙,树叶树皮等,导致杂质含量较高,轮胎厂直接使用的话轮胎容易断层或爆胎。烟片在烘烤过程中可能烘烤不熟,水分会导致轮胎起泡或爆胎。多种规格,不便于使用;尤其是111.1kg规格的烟片不容易搬运和切割。市面上的烟片胶因为生产商不同,管理水平的不一致,质量指标波动也较大,会导致轮胎企业使用过程中频繁的调整配方,质量风险较大。
发明内容
本发明的目的在于提供一种烟片级标准橡胶,通过对将传统烟片胶经过标准化的工艺加工,得到杂质含量、灰分含量、挥发物含量、氮含量、塑性初值、抗氧指数,门尼粘度等理化指标良好且稳定的烟片级标准橡胶。
本发明公开了一种烟片级标准橡胶,其特征在于用烟片胶加工而成,其杂质含量0.05%-0.08%(m/m),灰份含量0.8%(m/m),氮含量0.6%(m/m),挥发物含量0.8%(m/m),塑性初值≥40,塑性保持率≥60,门尼粘度ML/(1′+4′)100℃为83±10,丙酮抽出物含量2.0-3.5% Wt. 铜含量,8mg/kg,锰含量10mg/kg,成品每件35kg,每一托盘1.26吨的标准包装。
这种烟片级标准橡胶的加工工艺:采用烟片为原材料,经过二级破碎,一级预洗,一级挤压工序,绉片八次到十次,造粒二到三次,然后经过蒸汽炉低温烘干。
本发明的烟片级标准橡胶不同于市面上不同规格(33.3kg,50kg,111.11kg)不同质量的烟片(目测分级,无指标分级),能够通过指标分级,规避了直接使用烟片的种种风险,填补了烟片胶无理化指标分级的空白,同时这种烟片级标准橡胶的生产工艺不仅保留了烟片原有的特性,而且还去除了烟片里含有的大量杂质,避免了由杂质导致的轮胎脱层或爆胎的风险;通过蒸汽烘干炉低温烘干,去除了烟片里可能带有的水分,避免了轮胎在硫化过程中高温高压下产生气泡的风险;通过低温、恒温烘干,不但保护了橡胶分子链,提升了胶料的塑性初值、抗氧指数、门尼粘度、拉伸强度等理化指标;成品每件35kg,每托盘1.26吨是国际通用的标准包装,在使用和运输上比50kg,111.11kg规格的烟片胶方便,且大大降低了工人劳动强度;通过对原料烟片的化验分析,配方的调配和工艺的加工,规模化生产可使原料科学合理的搭配生产,指标均一稳定,避免了橡胶质量指标波动大导致的轮胎质量风险,可满足轮胎企业做高端产品的需求。
具体实施方式
将电机功率为90KW的破碎机2台,电机功率为160KW的1号挤压机和电机功率200KW的2号挤压机,电机功率为55KW的绉片机8台,电机功率为132KW的造粒机2台设置于橡胶加工的流水线上:
步骤1、将大块的烟片胶依次投入两台破碎机,同时进行喷水洗涤,通过机体内动刀和定刀的组合将胶块破碎,在剪切揉搓过程中将杂质、灰分物质随流动的水滤出,大块胶料得到初步破碎;
步骤2、破碎后的胶料进入1号挤压机,同时进行喷水洗涤,机体下部配合有滤沙孔,出料口有动刀定刀组合。在剪切揉搓过程中将杂质、灰分物质随流动的水滤出,到出料口的胶料在动定刀的剪切下得到更充分地破碎、揉搓,使胶料更进一步被破碎、混合,更进一步除去胶料内的杂质、灰分,提高胶料的一致性,胶料获得了更好的软硬度;
步骤3、经过1次挤压的胶料进入2号挤压机进行第二次挤压,同时进行喷水洗涤,机体下部配合有滤沙孔,在剪切揉搓过程中将杂质、灰分物质随流动的水滤出,经2号挤压机出来的胶料得到更充分地剪切、揉搓,使胶料更进一步破碎、混合,更进一步除去胶料内的杂质、灰分,提高胶料的一致性,胶料获得了更好的软硬度,更有利于胶料压绉成品,为造粒提供了有利条件;
步骤4、将步骤3中经过二次挤压的胶料先经过4台绉片机四次绉片,然后进入造粒机进行一次造粒,将二次挤压后得到的软硬合适、混合均匀的胶料进一步打碎,进一步除去杂质、灰分,使产品的纯度、一致性得到提高,使胶粒直径减小;
步骤5、将步骤4中经过第一次造粒的胶料再次经过4台绉片机四次绉片,然后经过造粒机第二次造粒;
步骤7、将二次造粒后的胶料放入烘干炉烘干;
步骤8、称量打包。
得到的烟片级标准橡胶其杂质含量0.05%-0.08%(m/m),灰份含量0.8%(m/m),氮含量0.6%(m/m),挥发物含量0.8%(m/m),塑性初值≥40,塑性保持率≥60,门尼粘度ML/(1′+4′)100℃为83±10,丙酮抽出物含量2.0-3.5% Wt. 铜含量,8mg/kg,锰含量10mg/kg,成品每件35kg,每一托盘1.26吨的标准包装。
Claims (1)
1.一种烟片级标准橡胶,其特征在于用烟片胶加工而成,其杂质含量0.05%-0.08%(m/m),灰份含量0.8%(m/m),氮含量0.6%(m/m),挥发物含量0.8%(m/m),塑性初值≥40,塑性保持率≥60,门尼粘度ML/(1′+4′)100℃为83±10,丙酮抽出物含量2.0-3.5% Wt. 铜含量,8mg/kg,锰含量10mg/kg,成品每件35kg,每一托盘1.26吨的标准包装。