CN1123432C - 秸秆纤维浆板及其制造方法 - Google Patents

秸秆纤维浆板及其制造方法 Download PDF

Info

Publication number
CN1123432C
CN1123432C CN 01100009 CN01100009A CN1123432C CN 1123432 C CN1123432 C CN 1123432C CN 01100009 CN01100009 CN 01100009 CN 01100009 A CN01100009 A CN 01100009A CN 1123432 C CN1123432 C CN 1123432C
Authority
CN
China
Prior art keywords
straw
straw fiber
fiber board
weight
manufacture method
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 01100009
Other languages
English (en)
Other versions
CN1362317A (zh
Inventor
马富生
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 01100009 priority Critical patent/CN1123432C/zh
Publication of CN1362317A publication Critical patent/CN1362317A/zh
Application granted granted Critical
Publication of CN1123432C publication Critical patent/CN1123432C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明涉及一种秸秆纤维浆板的制造方法,①精选植物秸秆;②清洗;③蒸煮;④粉碎,烘干;⑤加入填充料;⑥加水;⑦搅拌;⑧脱水热压成型。用上述方法制得的秸秆纤维浆板板材厚度为5cm。本发明由于利用了农业秸秆类废弃物作为原材料,解决了秸秆焚烧和堆放造成的环境污染问题,并且由于原料经过精选,不含植物粉末,制成品作为秸秆餐盒的半成品可以满足餐盒制造工业的需要。

Description

秸秆纤维浆板及其制造方法
技术领域
本发明涉及一种植物纤维浆板及其制造方法,特别是一种秸秆纤维浆板及其制造方法。
背景技术
目前,采用植物纤维制造餐盒或其他工业产品是新兴的产业,我国农村秸秆的焚烧和堆放造成的环境污染问题也毋待解决。由于秸秆的获得具有时间性,在秋季如果不能及时将秸秆进行处理,就会影响可降解餐盒或其他工业产品的生产,秸秆的堆放也会造成各种费用的增加。
发明内容
本发明的目的在于:提供一种秸秆纤维浆板及其制造方法,以回收的植物纤维为原料,及时制成秸秆纤维浆板,作为餐盒的半成品以利于秸秆的存放和餐盒制造工业的需要。
本发明是这样实现的:一种秸秆纤维浆板的制造方法,①精选植物秸秆;②清洗,去除植物粉末;③将秸秆在150℃下蒸煮;④将秸秆粉碎成为粒径小于3mm的颗粒,烘干后制成秸秆纤维板;⑤将占秸秆纤维板重量50%-80%的填充料与秸秆纤维板混合;⑥在上述步骤⑤所得混合物中加重量为混合物重量5000%-7000%的水;⑦充分搅拌;⑧脱水热压成型。
所述的秸秆为玉米杆、稻杆、麦秸其中的一种或几种。
所述的填充料为滑石粉,重量占秸秆纤维板重量的70%。
所述的混合物中加重量为混合物重量6000%的水。
一种秸秆纤维浆板,其特征在于:由粒径小于3mm的秸杆颗粒制成的秸杆纤维板和占秸杆纤维板重量50%-80%的填充料组成,板材厚度为5cm。
本发明由于利用了农业秸秆类废弃物作为原材料,解决了秸秆焚烧和堆放造成的环境污染问题,并且由于原料经过精选,不含植物粉末,制成品作为秸秆餐盒的半成品可以满足餐盒制造工业的需要。
具体实施方式
下面结合非限定性的实施例对本发明做进一步说明。
实施例1.选取没有污染,无霉变的玉米杆120公斤;切断后清洗干净,这样可以使产品有害物质含量符合国家卫生标准;去除植物粉末,这样可以使产品外观光洁;将秸秆段在150℃下蒸煮;将秸秆段粉碎成为粒径小于3mm的颗粒,烘干后制成秸秆纤维板;将重量为70公斤的滑石粉和秸秆纤维板混合;在所得的混合物中加12吨水;充分搅拌;用浆泵将秸秆浆抽到成型机上,真空脱水后热压成型即可,所述板材厚度为5cm。
实施例2.如实施例1所述的方法,采用120公斤稻杆;50公斤的滑石粉;和10吨水。
实施例3.如实施例1所述的方法,采用120公斤麦秸;80公斤的滑石粉;和15吨水。

Claims (5)

1.一种秸秆纤维浆板的制造方法,①精选植物秸秆;②清洗,去除植物粉末;③将秸秆在150℃下蒸煮;④将秸秆粉碎成为粒径小于3mm的颗粒,烘干后制成秸秆纤维板;⑤将占秸秆纤维板重量50%-80%的填充料与秸秆纤维板混合;⑥在上述步骤⑤所得混合物中加重量为混合物重量5000%-7000%的水;⑦充分搅拌;⑧脱水热压成型。
2.根据权利要求1所述的秸秆纤维浆板的制造方法,所述的秸秆为玉米杆、稻杆、麦秸其中的一种或几种。
3.根据权利要求1或2所述的秸秆纤维浆板的制造方法,所述的填充料为滑石粉,重量占秸秆纤维板重量的70%。
4.根据权利要求1或2所述的秸秆纤维浆板的制造方法,所述的混合物中加重量为混合物重量6000%的水。
5.一种秸秆纤维浆板,其特征在于:由粒径小于3mm的秸杆颗粒制成的秸杆纤维板和占秸杆纤维板重量50%-80%的填充料组成,板材厚度为5cm。
CN 01100009 2001-01-02 2001-01-02 秸秆纤维浆板及其制造方法 Expired - Fee Related CN1123432C (zh)