CN102558725A - 一种橡塑共混复合专用料 - Google Patents

一种橡塑共混复合专用料 Download PDF

Info

Publication number
CN102558725A
CN102558725A CN2010105991002A CN201010599100A CN102558725A CN 102558725 A CN102558725 A CN 102558725A CN 2010105991002 A CN2010105991002 A CN 2010105991002A CN 201010599100 A CN201010599100 A CN 201010599100A CN 102558725 A CN102558725 A CN 102558725A
Authority
CN
China
Prior art keywords
cpvc
compound
nbr
rubber
nbr rubber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2010105991002A
Other languages
English (en)
Inventor
揣成智
郑力行
任秀龙
王月朗
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DEHAO SUPERMICRO NEW MATERIALS Co Ltd TIANJIN
Original Assignee
DEHAO SUPERMICRO NEW MATERIALS Co Ltd TIANJIN
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DEHAO SUPERMICRO NEW MATERIALS Co Ltd TIANJIN filed Critical DEHAO SUPERMICRO NEW MATERIALS Co Ltd TIANJIN
Priority to CN2010105991002A priority Critical patent/CN102558725A/zh
Publication of CN102558725A publication Critical patent/CN102558725A/zh
Pending legal-status Critical Current

Abstract

本发明涉及高分子材料改性技术，尤其是丁腈橡胶改性CPVC的复合共混料。本发明CPVC-NBR橡塑复合专用料由CPVC树脂、NBR、增塑剂、稳定剂、填充物、润滑剂经过高速混合、双螺杆挤出、造粒、冷却等工序制得。本CPVC-NBR橡塑复合专用料.具有良好的柔韧性，可以作为护套料和绝缘料广泛使用；稳定剂使用的稀土稳定剂，大大降低了使用一般稳定剂所带来的环境污染，其具有环保意义；相比于其它的同类材料具有优异的综合性能。

Description

一种橡塑共混复合专用料
技术领域 本发明涉及高分子材料改性技术，尤其是丁腈橡胶改性CPVC的复合共混料。
背景技术 CPVC的含氯量高于PVC，较高的氯含量赋予了CPVC优异的物理机械性、耐老化性、耐腐蚀性、耐高温能力、变形性、可溶性及阻燃自熄性等，因而CPVC是性能优良的新型材料，被广泛用于建筑行业、化工、冶金、造船、电器、纺织等领域，应用前景十分广阔。但是，CPVC的抗冲击及加工性能较差使得其在一些领域的应用受到了限制。
本发明使用NBR改性CPVC，由于有丁腈橡胶的掺入，产品具有橡胶的柔软性(热塑性弹性体)，而且橡胶具有优良的耐油性能和大分子增塑剂的作用，对CPVC的加工性能又有所帮助，因此CPVC-NBR橡塑共混复合材料可以拓宽CPVC的应用范围，是一种综合性能优异的复合材料。
发明内容 本发明的目的在于克服现有技术的不足，提供一种既具有CPVC的优良性能，同时有具有比较好的柔韧性的CPVC-NBR橡塑复合专用料，这种复合料特别适用于护套料和绝缘料。
本发明是通过以下技术方案来实现的：
本发明CPVC-NBR橡塑复合专用料，包括：CPVC树脂、NBR、增塑剂、稳定剂、填充物、润滑剂。其特征在于，复合材料的质量份数配比为：
CPVC树脂                              100
NBR                                   25～40
增塑剂                                20～30
主稳定剂                              4～6
辅助稳定剂                            0.5～1
填充物                                20～25
润滑剂                                0.5～1
本发明CPVC-NBR橡塑复合专用料，其特征在于：所述的CPVC聚氯乙烯树脂，含氯量大于等于62％，可从市场购得。
而且，所述NBR丁腈橡胶中丙烯腈含量为18％～24％，可从市场购得。
而且，其特征在于：所述增塑剂为TOTM和DIDP；TOTM为偏苯三酸三辛酯，DIDP为邻苯二甲酸二异癸酯。
而且，其特征在于：所述主稳定剂为稀土稳定剂，辅助稳定剂为Ca/Zn稳定剂。
而且，其特征在于：所述填充物选自碳酸钙和煅烧高岭土。
而且，其特征在于：所述润滑剂选自硬脂酸钡和硬脂酸。
本发明的特点是：
1.具有良好的柔韧性，可以作为护套料和绝缘料广泛使用。
2.稳定剂使用的稀土稳定剂，大大降低了使用一般稳定剂所带来的环境污染，其具有环保意义。
3.由于CPVC的使用，相比于其它的同类材料具有优异的综合性能。
具体实施方式
本发明通过以下实施例进一步详述，下述实施例是说明性的，不是限定性的，不能以下述实施例来限定本发明的保护范围。
实施例：CPVC-NBR橡塑复合专用料
  CPVC   100
  NBR   25
  增塑剂，TOTM   20
  增塑剂，DIDP   10
  主稳定剂   5
  辅助稳定剂   0.6
  填充物   25
  润滑剂   0.6
将计量好的CPVC、增塑剂、稳定剂、填充物、润滑剂加入高速混合机中高速混合，混合5～10分钟后加入计量好的NBR继续高速混合5～10分钟，将混合好的料经双螺杆挤出机挤出造粒，然后冷却、包装。
其挤出成型工艺(温度℃)参数：
  1段   2段   3段   4段   5段   6段   模头
  温度，℃   130   150   155   160   165   170   170
其中挤出机L/D≥24
以上所述，仅是本发明的较佳实施例而已，并非对本发明作任何形式上的限制，凡是依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰，均仍属于本发明技术方案的范围内。

Claims (7)

1.一种CPVC-NBR橡塑复合专用料，包括：包括：CPVC树脂、NBR、增塑剂、稳定剂、填充物、润滑剂。其特征在于，复合材料的质量份数配比为：
CPVC树脂                        100份；
NBR                             25～40份；
增塑剂                          20～30份；
主稳定剂                        4～6份；
辅助稳定剂                      0.5～1份；
填充物                          20～25份；
润滑剂                          0.5～1份。
2.根据权利要求1所述的一种CPVC-NBR橡塑复合专用料，其特征在于：所述的CPVC聚氯乙烯树脂，含氯量大于等于62％，可从市场购得。
3.根据权利要求1所述的一种CPVC-NBR橡塑复合专用料，其特征在于：所述NBR丁腈橡胶中丙烯腈含量为18％～24％，可从市场购得。
4.根据权利要求1所述的一种CPVC-NBR橡塑复合专用料，其特征在于：所述增塑剂为TOTM和DIDP；TOTM为偏苯三酸三辛酯，DIDP为邻苯二甲酸二异癸酯。
5.根据权利要求1所述的一种CPVC-NBR橡塑复合专用料，其特征在于：所述主稳定剂为稀土稳定剂，辅助稳定剂为Ca/Zn稳定剂。
6.根据权利要求1所述的一种CPVC-NBR橡塑复合专用料，其特征在于：所述填充物选自碳酸钙和煅烧高岭土。
7.根据权利要求1所述的一种CPVC-NBR橡塑复合专用料，其特征在于：所述润滑剂选自硬脂酸钡和硬脂酸。
CN2010105991002A 2010-12-21 2010-12-21 一种橡塑共混复合专用料 Pending CN102558725A (zh)