CN103102613A - 一种pvc弹性体复合物专用料 - Google Patents

一种pvc弹性体复合物专用料 Download PDF

Info

Publication number
CN103102613A
CN103102613A CN 201110358695 CN201110358695A CN103102613A CN 103102613 A CN103102613 A CN 103102613A CN 201110358695 CN201110358695 CN 201110358695 CN 201110358695 A CN201110358695 A CN 201110358695A CN 103102613 A CN103102613 A CN 103102613A
Authority
CN
China
Prior art keywords
resistant
rubber
pvc
polyvinyl chloride
resistance
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201110358695
Other languages
English (en)
Inventor
王月朗
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DEHAO SUPERMICRO NEW MATERIALS Co Ltd TIANJIN
Original Assignee
DEHAO SUPERMICRO NEW MATERIALS Co Ltd TIANJIN
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DEHAO SUPERMICRO NEW MATERIALS Co Ltd TIANJIN filed Critical DEHAO SUPERMICRO NEW MATERIALS Co Ltd TIANJIN
Priority to CN 201110358695 priority Critical patent/CN103102613A/zh
Publication of CN103102613A publication Critical patent/CN103102613A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种PVC弹性体复合物专用料。其特征在于,采用先进的生产技术,以聚氯乙烯为基料,掺入一定比例的丁腈橡胶,并添加耐寒增塑剂、稳定剂、防老化剂等助剂,经特殊加工制成的粒料。经此工艺制得的聚氯乙烯-丁腈复合物塑料,由于有丁腈橡胶的掺入使用,产品具有橡胶的柔软性(热塑性弹性体)。由于橡胶具有优良的耐油性能,且具大分子增塑剂的作用,因此本产品具有优良的耐油、耐寒、耐溶剂和耐迁移性。用于如电机引接线及各类的耐油电线、耐迁移电线等,尤其适用于耐低温环境。

Description

一种PVC弹性体复合物专用料
技术领域
本发明涉及高分子材料改性技术,尤其是橡塑共混复合物合金材料。
背景技术
聚氯乙烯(PVC)原材料来源广泛,制品成本低、质量轻、施工和维护保养方便,是位居第二的通用塑料。但PVC材料具有韧性差、耐热性差等缺点,制约了其在性能要求较高领域的发展。多年来, 人们在PVC共混增韧改性等方面取得了较大的进展。其中NBR (丁二烯-丙烯腈无规共聚物,也称丁腈橡胶) 因与PVC相容性好, 得到的材料韧性、耐油性优异而倍受青睐,因此如何寻求一种经济高效的橡塑共混配方实为必要。
发明内容
本发明提供一种橡塑共混复合物专用料,它是以聚氯乙烯为基料,掺入一定比例的丁腈橡胶,并添加耐寒增塑剂、稳定剂、防老化剂等助剂,经特殊加工制成的粒料。首先将计量好的聚氯乙烯与丁晴橡胶加入高速混合机中高速混合,至温度升至145℃时停止混合;待温度降至125℃时再将计量好的增塑剂、稳定剂、防老化剂等助剂放入高速混合机中高速混合均匀后,经双螺杆挤出机挤出造粒。本产品由于有丁腈橡胶的掺入使用,产品具有橡胶的柔软性(热塑性弹性体)。由于橡胶具有优良的耐油性能,且具大分子增塑剂的作用,因此本产品具有优良的耐油、耐寒、耐溶剂和耐迁移性。用于如电机引接线及各类的耐油电线、耐迁移电线等,尤其适用于耐低温环境。 
具体实施方式
以下通过实施例进一步说明本发明:
实施例1:
聚氯乙烯-丁腈橡胶合金配方:(质量份)
PVC 100
NBR 25
耐寒剂 15
增塑剂 5
增容剂 2.5
稳定剂 3
防老化剂 4.5
    首先将计量好的聚氯乙烯与丁晴橡胶加入高速混合机中高速混合,至温度升至145℃时停止混合;待温度降至125℃时再将计量好的增塑剂、稳定剂、防老化剂等助剂放入高速混合机中高速混合均匀后,经双螺杆挤出机挤出造粒。制得高性能的聚氯乙烯-丁腈橡胶共混物。
其挤出成型工艺(温度℃)参数:
  1段 2段 3段 4段 5段 6段 模头
温度,℃ 130 140 145 150 155 170 170
实施例2:
聚氯乙烯-丁腈橡胶合金配方:(质量份)
PVC 100
NBR 35
耐寒剂 20
增塑剂 10
增容剂 3
稳定剂 6.5
防老化剂 3.5
首先将计量好的聚氯乙烯与丁晴橡胶加入高速混合机中高速混合,至温度升至145℃时停止混合;待温度降至125℃时再将计量好的增塑剂、稳定剂、防老化剂等助剂放入高速混合机中高速混合均匀后,经双螺杆挤出机挤出造粒。制得高性能的聚氯乙烯-丁腈橡胶共混物。
其挤出成型工艺(温度℃)参数:     
  1段 2段 3段 4段 5段 6段 模头
温度,℃ 130 135 140 150 155 170 170
本发明方法制成的聚氯乙烯-丁腈橡胶合金具有优异的性能,其性能指标如下:(1)缺口冲击强度/KJ/m2≥25;(2)断裂伸长率/%≥50;(3)弯曲强度/MPa≥60;(4)弯曲模量/GPa
≥2.5;(5)拉伸强度/MPa≥65。
以上所述,仅是本发明的较佳实施例而已,并非对本发明作任何形式上的限制,凡是依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰,均仍属于本发明技术方案的范围内。

Claims (2)

1.聚氯乙烯-丁腈复合物塑料是以聚氯乙烯为基料,掺入一定比例的丁腈橡胶,并添加耐寒增塑剂、稳定剂、防老化剂等助剂,经特殊加工制成的粒料,其特征在于,经过丁腈橡胶增韧后的复合物塑料,同时具备了塑料的强度与橡胶的韧度,具备极其优良的力学性能,可以用于工业生产,日常生活的众多领域。
2.根据权利要求1所述的一种PVC弹性体复合物专用料,其特征在于,由于有丁腈橡胶的掺入使用,产品具有橡胶的柔软性(热塑性弹性体)由于橡胶具有优良的耐油性能,且具大分子增塑剂的作用,因此本产品具有优良的耐油、耐寒、耐溶剂和耐迁移性,用于如电机引接线及各类的耐油电线、耐迁移电线等,尤其适用于耐低温环境。
CN 201110358695 2011-11-14 2011-11-14 一种pvc弹性体复合物专用料 Pending CN103102613A (zh)