CN102534175A - 一种钢丝回火工艺 - Google Patents

一种钢丝回火工艺 Download PDF

Info

Publication number
CN102534175A
CN102534175A CN2012100332525A CN201210033252A CN102534175A CN 102534175 A CN102534175 A CN 102534175A CN 2012100332525 A CN2012100332525 A CN 2012100332525A CN 201210033252 A CN201210033252 A CN 201210033252A CN 102534175 A CN102534175 A CN 102534175A
Authority
CN
China
Prior art keywords
temperature
steel wire
meters
length
warm area
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012100332525A
Other languages
English (en)
Inventor
玛琳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzuki Garphyttan Wire Suzhou Co Ltd
Original Assignee
Suzuki Garphyttan Wire Suzhou Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzuki Garphyttan Wire Suzhou Co Ltd filed Critical Suzuki Garphyttan Wire Suzhou Co Ltd
Priority to CN2012100332525A priority Critical patent/CN102534175A/zh
Publication of CN102534175A publication Critical patent/CN102534175A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种钢丝回火工艺,其特征在于:该工艺依次包括以下步骤:首先,将多根不同规格的钢丝间隔排列后以3米/分钟至30米/分钟的速度从回火炉的进口穿入;其次,使进入所述回火炉内的钢丝依次通过第一温区、第二温区和第三温区;所述第一温区内的温度为600℃-500℃,所述第二温区内的温度为500℃-400℃,所述第三温区内的温度为400℃-300℃;所述第一温区的长度为2米-2.5米,所述第二温区的长度为1.6米-2.2米,所述第三温区的长度为2米-2.5米。本发明能够在三个温区构成的同一温度曲线下同时对多种不同规格的钢丝进行回火处理,并且制得的钢丝品质较好。

Description

一种钢丝回火工艺
技术领域
本发明涉及一种钢丝生产工艺,尤其涉及一种钢丝回火工艺。
背景技术
钢丝是钢材的板、管、型、丝四大品种之一,是用热轧盘条经冷拉制成的再加工产品 ,在钢丝的生产过程中为提高钢丝的机械性能,通常会对钢丝进行硬化处理,以大幅提升钢丝的强度、硬度、耐磨性、疲劳强度以及韧性等,从而满足各种机械零件和工具的不同使用需求。上述硬化处理通常包括有对钢丝的淬火处理和回火处理,目前,采用传统的钢丝回火工艺对钢丝进行回火处理时,一次仅能够对同一种规格的钢丝进行回火处理,而无法同时对多种不同规格的钢丝进行回火处理,此外,传统的钢丝回火工艺制得的钢丝其强度、硬度、耐磨性、疲劳强度以及韧性等较差,所以很难满足各种机械零件和工具的不同使用需求。
发明内容
本发明所要解决的技术问题是提供一种能够同时对多种不同规格的钢丝进行回火处理,并且制得的钢丝品质较好的钢丝回火工艺。
为解决上述技术问题,本发明提供一种钢丝回火工艺,该工艺依次包括以下步骤:首先,将多根不同规格的钢丝间隔排列后以3米/分钟至30米/分钟的速度从回火炉的进口穿入;
其次,使进入所述回火炉内的钢丝依次通过第一温区、第二温区和第三温区;所述第一温区内的温度为600℃-500℃,所述第二温区内的温度为500℃-400℃,所述第三温区内的温度为400℃-300℃;所述第一温区的长度为2米-2.5米,所述第二温区的长度为1.6米-2.2米,所述第三温区的长度为2米-2.5米。
钢丝穿入回火炉内的速度为15米/分钟。
所述第一温区内的温度为550℃,长度为2.3米;所述第二温区内的温度为450℃,长度为2米;所述第三温区内的温度为350℃,长度为2.3米。
与现有技术相比,本发明的有益效果为:
由于本发明的钢丝回火工艺依次包括有将多根不同规格的钢丝以3米/分钟至30米/分钟穿入回火炉,并在炉内依次通过三个不同的温区,从而保证了在较高的生产效率下不同规格的钢丝均能在回火炉内进行回火处理,使钢丝组织发生改变,从而大幅提升钢丝的强度、硬度、耐磨性、疲劳强度以及韧性等,因此本发明能够在三个温区构成的同一温度曲线下同时对多种不同规格的钢丝进行回火处理,并且制得的钢丝品质较好。
具体实施方式
以下结合具体实施方式对本发明做进一步详细说明
一种钢丝回火工艺,该工艺依次包括以下步骤:
首先,使间隔排列的多根不同规格的钢丝以3米/分钟至30米/分钟的速度从回火炉的进口穿入;优选钢丝穿入回火炉内的速度为15米/分钟;
其次,使进入回火炉内的钢丝依次通过相邻设置的第一温区、第二温区和第三温区;其中第一温区内的温度为600℃-500℃,长度为2米-2.5米;第二温区内的温度为500℃-400℃,长度为1.6米-2.2米;第三温区内的温度为400℃-300℃,长度为2米-2.5米。
上述步骤中使钢丝以3米/分钟至30米/分钟的速度穿入回火炉,并在回火炉内设置三个温区是为了使不同规格的钢丝均能够在回火炉内进行回火处理,使钢丝组织发生改变,以提高钢丝的机械性能。
实施例1:
一种钢丝回火工艺,该工艺依次包括以下步骤:
首先,使间隔排列的多根不同规格的钢丝以15米/分钟的速度从回火炉的进口穿入;并保持以15米/分钟的速度在回火炉内行走;
其次,使进入回火炉内的钢丝依次通过相邻设置的第一温区、第二温区和第三温区;其中,第一温区内的温度为550℃,长度为2.3米;第二温区内的温度为450℃,长度为2米;第三温区内的温度为350℃,长度为2.3米。
实施例2:
一种钢丝回火工艺,该工艺依次包括以下步骤:
首先,使间隔排列的多根不同规格的钢丝以3米/分钟的速度从回火炉的进口穿入;并保持以3米/分钟的速度在回火炉内行走;
其次,使进入回火炉内的钢丝依次通过相邻设置的第一温区、第二温区和第三温区;其中,第一温区内的温度为600℃,长度为2米;第二温区内的温度为500℃,长度为1.6米;第三温区内的温度为400℃,长度为2米。
实施例3:
一种钢丝回火工艺,该工艺依次包括以下步骤:
首先,使间隔排列的多根不同规格的钢丝以30米/分钟的速度从回火炉的进口穿入;并保持以30米/分钟的速度在回火炉内行走;
其次,使进入回火炉内的钢丝依次通过相邻设置的第一温区、第二温区和第三温区;其中,第一温区内的温度为500℃,长度为2.5米;第二温区内的温度为400℃,长度为2.2米;第三温区内的温度为300℃,长度为2.5米。
以上所述仅为本发明的较佳实施方式,本发明的保护范围并不以上述实施方式为限,但凡本领域普通技术人员根据本发明所揭示内容所作的等效修饰或变化,皆应纳入权利要求书中记载的保护范围内。

Claims (3)

1.一种钢丝回火工艺,其特征在于:该工艺依次包括以下步骤:
首先,将多根不同规格的钢丝间隔排列后以3米/分钟至30米/分钟的速度从回火炉的进口穿入;
其次,使进入所述回火炉内的钢丝依次通过第一温区、第二温区和第三温区;
所述第一温区内的温度为600℃-500℃,所述第二温区内的温度为500℃-400℃,所述第三温区内的温度为400℃-300℃;
所述第一温区的长度为2米-2.5米,所述第二温区的长度为1.6米-2.2米,所述第三温区的长度为2米-2.5米。
2.根据权利要求1所述的钢丝回火工艺,其特征在于:钢丝穿入回火炉内的速度为15米/分钟。
3.根据权利要求1所述的钢丝回火工艺,其特征在于:所述第一温区内的温度为550℃,长度为2.3米;所述第二温区内的温度为450℃,长度为2米;所述第三温区内的温度为350℃,长度为2.3米。
CN2012100332525A 2012-02-15 2012-02-15 一种钢丝回火工艺 Pending CN102534175A (zh)