CN102533212A - 一种能低温固化的低粘性粘胶剂 - Google Patents
一种能低温固化的低粘性粘胶剂 Download PDFInfo
- Publication number
- CN102533212A CN102533212A CN2012100121365A CN201210012136A CN102533212A CN 102533212 A CN102533212 A CN 102533212A CN 2012100121365 A CN2012100121365 A CN 2012100121365A CN 201210012136 A CN201210012136 A CN 201210012136A CN 102533212 A CN102533212 A CN 102533212A
- Authority
- CN
- China
- Prior art keywords
- adhesive
- parts
- low
- product
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种能低温固化的低粘性粘胶剂,涉及粘胶剂。其组成按重量计为:有机硅树脂10-20份,硅橡胶40-60份,聚氨酯弹性体10-20份,稀释剂50-100份,铂金催化剂3-5份,硅烷偶联剂0.1-1份,聚硅氧烷流平剂0.1-0.2份。同现有技术相比,具有以下有益效果:使用此粘胶剂制作相应的胶粘制品,可以长期粘贴在乳胶漆墙面并保持制品的重复粘贴性,扩大了胶粘制品的适用范围和可操作性、便捷性,满足了人们对室内个性化装饰的需求;可以实现低温(100-120℃)固化,增加了涂布基材的可选种类,如PP及PVC等塑料薄膜和纸张均可进行涂布。同时降低了产品生产设备的使用能耗,减少了二氧化碳排放。
Description
技术领域
本发明涉及粘胶剂,尤指一种有机硅压敏型的能低温固化的低粘性粘胶剂。
背景技术
有机硅压敏粘胶剂是一种新型的具有广阔发展前景的粘胶剂,它不仅具有压敏胶所需的良好的粘胶性能,还有许多独特性能:对高能低能表面材料具有良好的粘结性;具有突出的耐高低温性能;具有良好的化学惰性和耐湿性;具有一定的液体可渗透性和生物惰性。
低粘性有机硅压敏粘胶剂由于粘性低、易于粘贴、剥离时不留残胶,主要应用于玻璃屏幕保护膜、不锈钢保护膜、烤漆保护膜等制品。目前市场上的低粘性有机硅压敏胶均为国外公司生产,价格昂贵,同时也存在不足:此类低粘性产品无法长期粘贴在乳胶漆墙面;如果采用高粘性产品贴合乳胶漆墙,长时间粘贴后剥离时会破坏墙体。既能用于乳胶漆墙又可用于玻璃、不锈钢、木板等材料表面粘贴、可以长期并反复粘贴的低粘性有机硅压敏胶还没有出现。
此外,普通有机硅压敏粘胶剂需要较高温度(160℃左右)固化,这也对涂布基材和设备提出了更高的要求,增加了涂布过程中的能耗,造成了更多的二氧化碳排放。
发明内容
本发明的目的在于克服现有技术的上述不足,提供一种能低温固化的低粘性粘胶剂。其为一种有机硅压敏粘胶剂,它能够广泛应用于乳胶漆墙、玻璃及木板等光滑致密表面的粘接,可以长期粘贴并同时具有重复粘贴性,剥离时不会破坏被贴物表面且无残胶,扩大了不干胶带、背胶相纸和塑料贴膜等产品的使用范围,减少了胶粘制品粘贴时的人工成本,增加了移摘时的便捷性和再利用性。
本发明的另一目的在于提供一种实现低温固化的有机硅压敏粘胶剂,它可以在100-120℃条件下实现完全固化,从而扩大了涂布基材的可选种类,如PP及PVC等塑料薄膜和纸张均可进行涂布。同时降低了设备的使用能耗,减少了二氧化碳排放。
为实现以上目的,本发明提供以下的技术方案:
一种能低温固化的低粘性粘胶剂,其组成按重量计为:有机硅树脂10-20份,硅橡胶40-60份,聚氨酯弹性体10-20份,稀释剂50-100份,铂金催化剂3-5份,硅烷偶联剂0.1-1份,聚硅氧烷流平剂0.1-0.2份。
以上成分中,有机硅树脂用来产生压敏粘胶剂所需的粘性,硅橡胶用来形成质软的胶层并降低固化温度,聚氨酯弹性体用来增加胶层的弹性和柔韧性,铂金催化剂用来实现硅树脂和硅橡胶的聚合反应,硅烷偶联剂用来促进各组分之间的交联固化,聚硅氧烷流平剂用来改善涂层的流平性,稀释剂用来调整压敏胶的粘度和干燥速度。
本发明同现有技术相比,具有以下有益效果:使用此粘胶剂制作相应的胶粘制品,可以长期粘贴在乳胶漆墙面并保持制品的重复粘贴性,扩大了胶粘制品的适用范围和可操作性、便捷性,满足了人们对室内个性化装饰的需求;可以实现低温(100-120℃)固化,增加了涂布基材的可选种类,如PP及PVC等塑料薄膜和纸张均可进行涂布。同时降低了产品生产设备的使用能耗,减少了二氧化碳排放。
具体实施方式
实施例一:
一种能低温固化的低粘性粘胶剂,其组成按重量计为:有机硅树脂10份,硅橡胶40份,聚氨酯弹性体10份,稀释剂50份,铂金催化剂3份,硅烷偶联剂0.1份,聚硅氧烷流平剂0.1份。
实施例二:
一种能低温固化的低粘性粘胶剂,其组成按重量计为:有机硅树脂15份,硅橡胶50份,聚氨酯弹性体15份,稀释剂75份,铂金催化剂4份,硅烷偶联剂0.5份,聚硅氧烷流平剂0.1份。
实施例三:
一种能低温固化的低粘性粘胶剂,其组成按重量计为:有机硅树脂20份,硅橡胶60份,聚氨酯弹性体20份,稀释剂100份,铂金催化剂5份,硅烷偶联剂1份,聚硅氧烷流平剂0.2份。
实施例四:
一种能低温固化的低粘性粘胶剂,其组成按重量计为:有机硅树脂10份,硅橡胶60份,聚氨酯弹性体20份,稀释剂100份,铂金催化剂5份,硅烷偶联剂1份,聚硅氧烷流平剂0.1份。
实施例五:
一种能低温固化的低粘性粘胶剂,其组成按重量计为:有机硅树脂20份,硅橡胶40份,聚氨酯弹性体10份,稀释剂50份,铂金催化剂3份,硅烷偶联剂0.1份,聚硅氧烷流平剂0.1份。
本发明主要用于将膜片等贴于乳胶漆墙、玻璃、不锈钢、或木板等材料的表面,粘贴运用真空吸附和胶粘原理。将本发明涂布在膜片等的背面,形成粘胶涂层,且该粘胶涂层具有低粘性及弹性好的特点,粘贴时,粘胶涂层快速与被粘接体(如乳胶漆墙、玻璃、不锈钢或木板等平整致密表面)贴合,使膜片在被贴表面的粘合力迅速达到最大值,容易形成密闭的大气负压接触面,被粘接体表面通过密闭的大气负压接触面对膜片产生足够的吸附力,在足够的吸附力与低强度粘接力的共同作用下,使膜片与被粘接体表面紧紧贴接。由于这种贴接不是仅仅依赖于粘接力,而是主要靠粘胶涂层与被粘接体表面形成的大气负压接触面的吸附力作用,所以既不会脱落,同时又具有重复粘贴性,再贴便捷,移摘时不会伤膜片,也不会伤及被粘接体,不留残胶。
上述实施例并非对本发明的技术范围作任何限制。本行业的技术人员,在本技术方案的启迪下,可做出一些变形与修改,凡是依据本发明的技术实质对以上的实施例所作的任何修改、等同变化与修饰,均仍属于本发明技术方案的范围内。
Claims (1)
1. 一种能低温固化的低粘性粘胶剂,特征在于,其组成按重量计为:有机硅树脂10-20份,硅橡胶40-60份,聚氨酯弹性体10-20份,稀释剂50-100份,铂金催化剂3-5份,硅烷偶联剂0.1-1份,聚硅氧烷流平剂0.1-0.2份。