CN102531682A - 一种耐高温日用陶瓷釉料 - Google Patents
一种耐高温日用陶瓷釉料 Download PDFInfo
- Publication number
- CN102531682A CN102531682A CN2011104147020A CN201110414702A CN102531682A CN 102531682 A CN102531682 A CN 102531682A CN 2011104147020 A CN2011104147020 A CN 2011104147020A CN 201110414702 A CN201110414702 A CN 201110414702A CN 102531682 A CN102531682 A CN 102531682A
- Authority
- CN
- China
- Prior art keywords
- percent
- glaze
- domestic ceramics
- heat resisting
- ceramics glaze
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐高温日用陶瓷釉料,该釉料配方的化学组成为:SiO274.29~75.02wt%,Al2O311.23~11.88wt%,Fe2O30.13~0.15wt%,CaO0.93~1.04wt%,MgO3.69~3.98wt%,K2O5.26~5.78wt%,Na2O0.72~1.05wt%,TiO20.01wt%,Li2O0.44wt%,B2O30.89~1.57wt%,I.L.1.29~1.36wt%。本发明的陶瓷釉料烧制得到的产品降低了产品的热膨胀系数,减少釉面针孔、增加釉面光泽度,提高瓷器的机械强度和热稳定性,适合大规模生产。
Description
技术领域
本发明涉及一种耐高温日用陶瓷釉料。
背景技术
在制备日用陶瓷过程中,为了使陶瓷产品烧制出来后减少釉面针孔、增加釉面光泽度,或在烧制过程中降低釉的高温粘度,增加釉的高温流动性功能,会在釉料中加入大量熔剂,因而导致釉的热膨胀系数过大,最终造成日用陶瓷
的热稳定性变差,在运输、储存或使用过程中常常出现炸瓷现象,尤其是餐具如盘、碗、碟等在消毒过程中热耐受度低,产品非正常消耗过快。
发明内容
本发明的目的在于针对上述缺陷,提供一种新的釉料配方,该釉料配方采用常规方法烧制得到的陶瓷在热稳定性上高于常规陶瓷。
本发明通过以下技术方案实现上述目的:
一种耐高温日用陶瓷釉料,其配方的化学组成为:SiO2 74.29~75.02wt%,Al2O3 11.23 ~11.88 wt %,Fe2O3 0.13~0.15wt%,CaO 0.93~1.04wt%,MgO 3.69~3.98wt%,K2O 5.26~5.78 wt%,Na2O 0.72~1.05 wt%,TiO2 0.01 wt%,Li2O 0.44 wt%,B2O3 0.89~1.57 wt%,I.L.1.29~1.36 wt%。
经过多次试验优化,上述釉料配方最佳为:SiO2 74.72 wt%,Al2O3 11.43 wt%,Fe2O3 0.13 wt%,CaO 0.99 wt%,MgO 3.75 wt%,K2O 5.26 wt%,Na2O 1.04 wt%,TiO2 0.01 wt%,Li2O 0.44 wt%,B2O3 0. 91 wt%,I.L.1.32 wt%。
上述釉料配方经过粉碎、球磨、过筛、静置、陈腐、稀释成质量百分含量为60%的釉浆,喷施于素坯表面,釉料厚度为2mm,送入窑炉烧制,烧制出的产品热稳定性明显提升。
与现有技术相比,本发明的陶瓷釉料由于加入了Li2O的成分,与SiO2 和Al2O3在高温烧制过程中降低了釉的熔融温度、高温粘度和釉的膨胀系数,提高了釉的高温流动性和表面张力,从而减少釉面针孔、增加釉面光泽度,提高瓷器的机械强度、耐酸碱性和耐磨性。
具体实施方式
下面结合具体实施例进一步解释本发明。
实施例1
坯料瓷泥选择常用的日用陶瓷生产用瓷泥,修坯后进行清洗,整修,干燥素坯备用。
釉料组成配方:SiO2 74.72 wt%,Al2O3 11.43 wt%,Fe2O30.13 wt%,CaO 0.99 wt%,MgO 3.75 wt%,K2O 5.26 wt%,Na2O 1.04 wt%,TiO2 0.01 wt%,Li2O 0.44 wt%,B2O3 0. 91 wt%,I.L.1.32 wt%。
上述配方精确称量粉碎,球磨机球磨,出磨过300目筛,重复过筛5次,除铁3次,加水配制成浓度为45wt%的釉浆,在施釉前,再检查一遍素坯,合格后采用浸渍的方式施釉,然后送入窑炉,最高烧成温度为1300℃。
产品经检验,陶瓷吸水率为0.13%,釉面无龟裂,光泽度98,热稳定性240℃→20℃一次不炸,热膨胀系数5.3(α×10-6/℃)。
Claims (2)
1.一种耐高温日用陶瓷釉料,其特征在于釉料配方的化学组成为:SiO2 74.29~75.02wt%,Al2O3 11.23~11.88wt%,Fe2O3 0.13~0.15wt%,CaO 0.93~1.04wt%,MgO 3.69~3.98wt%,K2O 5.26~5.78 wt%,Na2O 0.72~1.05 wt%,TiO2 0.01 wt%,Li2O 0.44 wt%,B2O3 0.89~1.57 wt%,I.L.1.29~1.36 wt%。
2.根据权利要求1所述耐高温日用陶瓷釉料,其特征在于釉料配方的化学组成为:SiO2 74.72 wt%,Al2O3 11.43 wt%,Fe2O3 0.13 wt%,CaO 0.99 wt%,MgO 3.75 wt%,K2O 5.26 wt%,Na2O 1.04 wt%,TiO2 0.01 wt%,Li2O 0.44 wt%,B2O3 0. 91 wt%,I.L.1.32 wt%。