CN102504653A - Method of preparing coating for shell art products - Google Patents
Method of preparing coating for shell art products Download PDFInfo
- Publication number
- CN102504653A CN102504653A CN2011103111765A CN201110311176A CN102504653A CN 102504653 A CN102504653 A CN 102504653A CN 2011103111765 A CN2011103111765 A CN 2011103111765A CN 201110311176 A CN201110311176 A CN 201110311176A CN 102504653 A CN102504653 A CN 102504653A
- Authority
- CN
- China
- Prior art keywords
- weight parts
- mass parts
- shell
- art products
- stir
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method of preparing a coating for shell art products. The method comprises the following steps of: loading 30 to 34 weight parts of polyethylene wax, 5 to 7 weight parts of rosin, 3 weight parts of white wax and 30 to 40 weight parts of palmic acid into a reaction kettle, mixing, heating up to 160 DEG C, adding a mixed accelerator composed of 50 to 56 weight parts of stearic acid and 1 to 2 weight parts of oily water, heating up to 180 DEG C, adding 140 to 160 weight parts of 90 to 100 DEG C water, stirring for 1 hour, and cooling down to room temperature. The industrial test proves that the coating product made by the method can effectively protect shells from fading or being lusterless due to corrosion resulting from contact with the external environment.
Description
Technical field
The present invention relates to a kind of preparation method of shell handicraft finish, belong to the chemistry painting industry technical field.
Technical background
Shell is the shell that clams etc. has the shell animal.What wherein have has pearlescent iris gloss, thereby is used to jewellery industry, makes necklace, costume jewellery (button etc.), even is installed on the jewellery, more is used to make shell carving, pasteup more, inlays handle of a knife etc.In all kinds of shells, the Burma shellfish of the natural pearls oyster (pinctada maxina) that is produced with the northern Torres Strait of Australia one band, Filipine Manila shellfish, Burma and the geoduck in the West Indies, the big clam of queen etc. are for excellent.Especially nearly 2 years, the shell jewellery of jewelry level also began more and more to be liked natural and unrestrained natural people to dote on especially in our city.Mother pearl shellfish is a natural materials; Therefore every color and lines are all very unique; Satisfied the demand of more and more human consumers to personalized jewellery; The processing of mother pearl shellfish ornaments is very complicated, and the primary mother pearl shellfish will carry out very careful polishing, accurate cutting, inlays according to design requirements.Go through the multiple tracks art breading, just can process the shell ornaments that make us pleasing.But the staple of shell is 95% lime carbonate and a spot of chitin element.Long-time and extraneous the contact can be corroded and fade or tarnish, and the value of shell own will be lost like this, so one deck protective layer need be smeared in the top layer of shell.
Summary of the invention
The object of the invention provides a kind of preparation method of shell handicraft finish, and the finish that this method is prepared can effectively be protected shell not corrode because of the contact in the external world to fade.
In order to achieve the above object; The present invention adopts a technical scheme to be: a kind of preparation method of shell handicraft finish, and the preparation process of this method is following: in reaction kettle, add 30-34 mass parts polyethylene wax, 5-7 mass parts rosin, 3 mass parts Chinese wax and 30-40 mass parts Palmiticacid, mix and stir; Be heated to 160 ℃; Add 50-56 mass parts Triple Pressed Stearic Acid and 1-2 mass parts profit mixed accelerators, continue to be warmed up to 180 ℃, adding 90-100 ℃ of hot water of 140-160 mass parts; Continue to stir 1h, be cooled to room temperature.
The product that the inventive method is prepared proves through commerical test, can effectively protect shell not corrode because of the contact in the external world and fade or tarnish.
Embodiment
Embodiment 1
A kind of preparation method of shell handicraft finish, the preparation process of this method is following: in reaction kettle, add 30-34 mass parts polyethylene wax, 5-7 mass parts rosin, 3 mass parts Chinese wax and 30-40 mass parts Palmiticacid, mix and stir; Be heated to 160 ℃; Add 50-56 mass parts Triple Pressed Stearic Acid and 1-2 mass parts profit mixed accelerators, continue to be warmed up to 180 ℃, adding 90-100 ℃ of hot water of 140-160 mass parts; Continue to stir 1h, be cooled to room temperature.
Claims (1)
1. the preparation method of a shell handicraft finish is characterized in that the preparation process of this method is following: in reaction kettle, add 30-34 mass parts polyethylene wax, 5-7 mass parts rosin, 3 mass parts Chinese wax and 30-40 mass parts Palmiticacid, mix and stir; Be heated to 160 ℃; Add 50-56 mass parts Triple Pressed Stearic Acid and 1-2 mass parts profit mixed accelerators, continue to be warmed up to 180 ℃, adding 90-100 ℃ of hot water of 140-160 mass parts; Continue to stir 1h, be cooled to room temperature.