CN102504121A - 含氟水性聚氨酯成膜交联剂的制备方法 - Google Patents
含氟水性聚氨酯成膜交联剂的制备方法 Download PDFInfo
- Publication number
- CN102504121A CN102504121A CN2011103376446A CN201110337644A CN102504121A CN 102504121 A CN102504121 A CN 102504121A CN 2011103376446 A CN2011103376446 A CN 2011103376446A CN 201110337644 A CN201110337644 A CN 201110337644A CN 102504121 A CN102504121 A CN 102504121A
- Authority
- CN
- China
- Prior art keywords
- crosslinking agent
- preparation
- polyurethane film
- based polyurethane
- liquor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种含氟水性聚氨酯成膜交联剂的制备方法,包括以下步骤:a、在充满惰性气体的干燥清洁的反应釜中依次加入有机溶剂N,N-二甲基甲酰胺、催化剂量的二月桂酸二丁基锡、MDI以及HDI,加热溶解后得到a液;b、将计量的PEG-800、1,4-丁二醇混溶,得到b液;c、将b液缓慢滴加到a液中,控温反应1~5h得到预聚产物;d、在步骤c获得的预聚产物经过封端处理后,滴加计量的由丙烯酸、全氟醇、链引发剂和N,N-二甲基甲酰胺的混合液,保温反应1~15h后,经中和处理即可。本发明所获得含氟水性聚氨酯成膜交联剂使织物具有优良交联固着和表面活性性能,拒水拒油性能,手感丰满柔顺,透气性好。
Description
技术领域:
本发明涉及一种含氟水性聚氨酯成膜交联剂,特别涉及含氟水性聚氨酯成膜交联剂的制备方法。
背景技术:
随着服装、家纺、旅游、运输等行业的发展,对纺织特种材料的要求也越来越高,目前,国产纺织助剂在品种和质量以及在合成和应用技术方面与国际先进水平相比还有较大差距,专用和高档纺织助剂尚不得不依赖进口。
水性聚氨酯PU以水为分散介质,有溶剂型PU的耐低温、柔韧性好、粘结强度高等优良性能,又有气味小、不污染环境、节约能源等优点,可广泛用于轻纺、印染、皮革加工、涂料和造纸等行业。然而,水性聚氨酯的亲水链段由于具有较高的表面自由能,在提高聚氨酯水溶性的同时也降低了它的耐水、拒油性能.为了弥补这一缺陷,通常在聚氨酯结构中嵌入强疏水性链段,众所周知,氟碳烷烃具有极低的表面自由能,在各种基体低表面能改性中已得到广泛应用.有机氟热稳定性和化学稳定性好,可使织物表面能降低至油、水和污渍不能浸润的程度,且不影响织物手感、透气性、透湿性、色牢度、色光和进行其它后整理。
发明内容:
发明目的:针对现有技术存在的缺陷,本发明提供了一种含氟水性聚氨酯成膜交联剂的制备方法。
技术方案:为实现上述发明目的,本发明采用以下技术方案:
一种含氟水性聚氨酯成膜交联剂的制备方法,包括以下步骤:a、在充满惰性气体的干燥、清洁的反应釜中依次加入有机溶剂N,N-二甲基甲酰胺、催化剂量的二月桂酸二丁基锡、4,4’-二苯甲烷二异氰酸酯MDI以及六亚甲基二异氰酸酯HDI,加热溶解后,得到a液;b、将计量的聚乙二醇PEG-800与1,4-丁二醇按照6-7:1的质量比混溶后,得到b液;c、将b液缓慢滴加到a液中,在90~100℃下控温反应1~5h,得到预聚产物;d、在步骤c获得的预聚产物中加入由乙二醇乙醚和N-甲基二乙醇胺按照6-7:1的质量比复配的复合封端剂,在在90~100℃下继续保温反应1~5h,得到封端的聚氨酯乳液;e、将步骤d所获得的封端的聚氨酯乳液降温至70℃后,滴加计量的由丙烯酸、全氟醇、链引发剂和N,N-二甲基甲酰胺组成的混合液,在60~80℃下保温反应1~15h;f、加入乙醇酸中和剂,调节PH=7~9,加入去离子水,高速搅拌至匀,降温,封装产品。
所述全氟醇为全氟辛醇。
所述链引发剂为偶氮二异丁腈
根据以上的技术方案,可以实现以下的有益效果:与现有技术相比,本发明具有以下优点:本发明所获得含氟水性聚氨酯成膜交联剂使织物具有优良交联固着和表面活性性能,拒水拒油性能,手感丰满柔顺,透气性好。
具体实施方式:
下面结合实施例对本发明做进一步地详细说明,但是本发明要求保护的范围并不局限于实施例表示的范围。
实施例1:
在充满氮气或惰性气体的干燥,清洁的反应釜中加入有机溶剂N,N-二甲基甲酰胺(135.0kg)和4,4’-二苯甲烷二异氰酸酯(300.0kg),六亚甲基二异氰酸酯(100.0kg),催化剂二月桂酸二丁基锡(1.8kg),搅拌下加热至60℃溶解,待用;
称取PEG-800 (300.0kg),1,4-丁二醇(45.0kg)混合后,滴加入上述反应器中,控制温度在90~100℃,反应1~5h,反应毕,向反应产物中加入乙二醇乙醚(115.2kg)和N—甲基二乙醇胺(17.5kg),反应1~5h,得到封端的聚氨酯乳液;
向上述反应液中滴加丙烯酸(70.0kg),全氟辛醇(170.0kg),链引发剂偶氮二异丁腈(1.0kg),N,N-二甲基甲酰胺(50.0kg)的混合液,保持温度在60~80℃,反应1~15h;
向上述反应液中加入中和剂乙醇酸(12.5kg), 调节PH=7.8,加入去离子水,高速搅拌至匀,降温,封装产品。
Claims (3)
1.一种含氟水性聚氨酯成膜交联剂的制备方法,其特征在于,包括以下步骤:a、在充满惰性气体的干燥、清洁的反应釜中依次加入有机溶剂N,N-二甲基甲酰胺、催化剂量的二月桂酸二丁基锡、4,4’-二苯甲烷二异氰酸酯MDI以及六亚甲基二异氰酸酯HDI,加热溶解后,得到a液;b、将计量的聚乙二醇PEG-800与1,4-丁二醇按照6~7:1的质量比混溶后,得到b液;c、将b液缓慢滴加到a液中,在90~100℃下控温反应1~5h,得到预聚产物;d、在步骤c获得的预聚产物中加入由乙二醇乙醚和N-甲基二乙醇胺按照6-7:1的质量比复配的复合封端剂,并在90~100℃下继续保温反应1~5h,得到封端的聚氨酯乳液;e、将步骤d所获得的封端的聚氨酯乳液降温至70℃后,滴加计量的由丙烯酸、全氟醇、链引发剂和N,N-二甲基甲酰胺组成的混合液,在60~80℃下保温反应1~15h;f、加入乙醇酸中和剂,调节PH=7~9,加入去离子水,高速搅拌至匀,降温,封装产品。
2.根据权利要求1所述一种含氟水性聚氨酯成膜交联剂的制备方法,其特征在于:所述全氟醇为全氟辛醇。
3.根据权利要求1所述一种含氟水性聚氨酯成膜交联剂的制备方法,其特征在于:所述链引发剂为偶氮二异丁腈。