CN102501528A - 用于食品包装的无异味膜 - Google Patents
用于食品包装的无异味膜 Download PDFInfo
- Publication number
- CN102501528A CN102501528A CN2011103513250A CN201110351325A CN102501528A CN 102501528 A CN102501528 A CN 102501528A CN 2011103513250 A CN2011103513250 A CN 2011103513250A CN 201110351325 A CN201110351325 A CN 201110351325A CN 102501528 A CN102501528 A CN 102501528A
- Authority
- CN
- China
- Prior art keywords
- ldpe
- lldpe
- layer
- raw material
- mlldpe
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
用于食品包装的无异味膜,是利用内冷风循环式多层共挤设备共挤加工成型的三层共挤膜;中间层一侧的边层原料及质量配比为LDPE:LLDPE=30:65~75;中间层原料及质量配比为LDPE:LLDPE=25:70~80;中间层另一侧的边层原料及质量配比为LDPE:MLLDPE=40:55~65;上述各层总质量的配比为LDPE+LLDPE:LDPE+LLDPE:LDPE+MLLDPE=1:2.5~3.5:0.5~1.5;各原料的熔体指数均为1~3并无任何添加剂。由于对原料的熔体指数和添架剂的限制,并对各层原料的质量配比进行控制,利用内冷风循环方式进行多层共挤,使加工成型的包装膜不但符合食品包装的卫生要求,而且具有良好的柔软性及加工性,包装后与被包装物的贴附能力更强,占用空间小,方便了运输,包装材料的成本也有所降低。
Description
技术领域
本发明涉及一种包装膜,特别是一种用于食品包装的无异味膜。
背景技术
目前用于食品包装的塑料膜在制作加工时不注重原料的选择,大多直接选择低农密度聚乙烯原料,其原料内有一定量的多种添加剂,原料的熔体指数也大不相同,加工性差,生产出的包装膜有时带有一定的异味。
发明内容
本发明的目的是提供一种更加符合食品包装、柔软性能和加工性能好、与被包装物贴附性强、包装后占据空间小、方便运输、成本低的用于食品包装的无异味膜,克服现有技术的不足。
本发明的用于食品包装的无异味膜,是利用内冷风循环式多层共挤设备共挤加工成型的三层共挤膜;
中间层一侧的边层原料为LDPE和LLDPE,质量配比为LDPE:LLDPE=30:65~75;
中间层原料为LDPE和LLDPE,质量配比为LDPE:LLDPE=25:70~80;
中间层另一侧的边层原料为LDPE和MLLDPE,质量配比为LDPE:MLLDPE=40:55~65;
上述各层总质量的配比为
LDPE+LLDPE:LDPE+LLDPE:LDPE+MLLDPE=1:2.5~3.5:0.5~1.5;
所述的各原料的熔体指数均为1~3并无任何添加剂。
本发明的用于食品包装的无异味膜,其中所述的中间层一侧的边层原料质量配比为LDPE:LLDPE=30:70;
中间层原料质量配比为LDPE:LLDPE=25:75;
中间层另一侧的边层原料质量配比为LDPE:MLLDPE=40:60;
上述各层总质量的配比为
LDPE+LLDPE:LDPE+LLDPE:LDPE+MLLDPE=1:3:1;
所述的各原料的熔体指数均为2。
本发明的用于食品包装的无异味膜,由于对原料的熔体指数和添架剂的限制,并对各层原料的质量配比进行控制,利用内冷风循环方式进行多层共挤,使加工成型的包装膜不但符合食品包装的卫生要求,而且具有良好的柔软性及加工性,包装后与被包装物的贴附能力更强,占用空间小,方便了运输,包装材料的成本也有所降低。
具体实施方式
实施例1:本发明的用于食品包装的无异味膜,是利用内冷风循环式多层共挤设备共挤加工成型的三层共挤膜。
原料包括低密度聚乙烯(LDPE)、线性低密度聚乙烯(LLDPE)、茂金属线性低密度聚乙烯(MLLDPE)。
中间层一侧的边层原料质量配比为LDPE:LLDPE=30:70;
中间层原料质量配比为LDPE:LLDPE=25:75;
中间层另一侧的边层原料质量配比为LDPE:MLLDPE=40:60;
上述各层总质量的配比依次为:
LDPE+LLDPE:LDPE+LLDPE:LDPE+MLLDPE=1:3:1;
上述的各原料的熔体指数均为2并无任何添加剂。
实施例2:本发明的用于食品包装的无异味膜,是利用内冷风循环式多层共挤设备共挤加工成型的三层共挤膜。
原料包括低密度聚乙烯(LDPE)、线性低密度聚乙烯(LLDPE)、茂金属线性低密度聚乙烯(MLLDPE)。
中间层一侧的边层原料为LDPE和LLDPE,质量配比为LDPE:LLDPE=30:65。
中间层原料为LDPE和LLDPE,质量配比为LDPE:LLDPE=25:70。
中间层另一侧的边层原料为LDPE和MLLDPE,质量配比为LDPE:MLLDPE=40:55。
上述各层总质量的配比低次为:
LDPE+LLDPE:LDPE+LLDPE:LDPE+MLLDPE=1:2.5:0.5
上述各原料的熔体指数均为1并无任何添加剂。
实施例3:本发明的用于食品包装的无异味膜,是利用内冷风循环式多层共挤设备共挤加工成型的三层共挤膜。
原料包括低密度聚乙烯(LDPE)、线性低密度聚乙烯(LLDPE)、茂金属线性低密度聚乙烯(MLLDPE)。
中间层一侧的边层原料为LDPE和LLDPE,质量配比为LDPE:LLDPE=30:75。
中间层原料为LDPE和LLDPE,质量配比为LDPE:LLDPE=25:80。
中间层另一侧的边层原料为LDPE和MLLDPE,质量配比为LDPE:MLLDPE=40:65。
上述各层总质量的配比低次为:
LDPE+LLDPE:LDPE+LLDPE:LDPE+MLLDPE=1:3.5:1.5
上述各原料的熔体指数均为3并无任何添加剂。
实施例4:本发明的用于食品包装的无异味膜,是利用内冷风循环式多层共挤设备共挤加工成型的三层共挤膜。
原料包括低密度聚乙烯(LDPE)、线性低密度聚乙烯(LLDPE)、茂金属线性低密度聚乙烯(MLLDPE)。
中间层一侧的边层原料为LDPE和LLDPE,质量配比为LDPE:LLDPE=30:72。
中间层原料为LDPE和LLDPE,质量配比为LDPE:LLDPE=25:73。
中间层另一侧的边层原料为LDPE和MLLDPE,质量配比为LDPE:MLLDPE=40:62。
上述各层总质量的配比低次为:
LDPE+LLDPE:LDPE+LLDPE:LDPE+MLLDPE=1:2.8:1.2
上述各原料的熔体指数均为2.1并无任何添加剂。
Claims (2)
1.一种用于食品包装的无异味膜,其特征在于:
所述的无异味膜是利用内冷风循环式多层共挤设备共挤加工成型的三层共挤膜;
中间层一侧的边层原料为LDPE和LLDPE,质量配比为LDPE:LLDPE=30:65~75;
中间层原料为LDPE和LLDPE,质量配比为LDPE:LLDPE=25:70~80;
中间层另一侧的边层原料为LDPE和MLLDPE,质量配比为LDPE:MLLDPE=40:55~65;
上述各层总质量的配比为
LDPE+LLDPE:LDPE+LLDPE:LDPE+MLLDPE=1:2.5~3.5:0.5~1.5;
所述的各原料的熔体指数均为1~3并无任何添加剂。
2.根据权利要求1所述的用于食品包装的无异味膜,其特征在于:
所述的中间层一侧的边层原料质量配比为LDPE:LLDPE=30:70;
中间层原料质量配比为LDPE:LLDPE=25:75;
中间层另一侧的边层原料质量配比为LDPE:MLLDPE=40:60;
上述各层总质量的配比为
LDPE+LLDPE:LDPE+LLDPE:LDPE+MLLDPE=1:3:1;
所述的各原料的熔体指数均为2。