CN102501509A - 真空包装米类物料的材料 - Google Patents
真空包装米类物料的材料 Download PDFInfo
- Publication number
- CN102501509A CN102501509A CN2011103513725A CN201110351372A CN102501509A CN 102501509 A CN102501509 A CN 102501509A CN 2011103513725 A CN2011103513725 A CN 2011103513725A CN 201110351372 A CN201110351372 A CN 201110351372A CN 102501509 A CN102501509 A CN 102501509A
- Authority
- CN
- China
- Prior art keywords
- layer
- evoh
- ldpe
- bonding resin
- resin layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种真空包装米类物料的材料,是由EVOH基材膜和尼龙膜通过干法复合形成的;EVOH基材膜为层状结构,中间层的原料为EVOH,在中间层的两面有粘合树脂层,粘合树脂层的外侧有PE层,各层的质量配比依次为:PE层:粘合树脂层:EVOH层:粘合树脂层:PE层=3:0.8~1.2:0.5~1:0.8~1.2:3;EVOH基材膜是利用内冷风循环式多层共挤设备挤出成型的;PE层为LDPE与LLDPE按30:70的质量比例混合、LDPE与LLDPE按25:75的质量比例混合、LDPE与MLLDPE按40:60的质量比例混合后利用多层共挤方式形成的三层膜或其中任意两种混合料形成的二层膜。该材料具有阻隔性好、保香性强、耐油及有机溶剂、作为废品处理时无有害物质产生的优点。
Description
技术领域
本发明涉及一种包装材料,特别是一种真空包装米类物料的材料。
背景技术
目前用于包装米类物料材料是尼龙膜和低密度聚乙烯膜复合形成的,这种材料的阻隔性较差,特别是阻潮能力差;保香性不理想,被包装的米类物料会出现香味消失现象;耐油和耐有机溶剂性不好;作为废品处理时,会产生有害物质;真空包装时易出现静电现象。
发明内容
本发明的目的是提供一种阻隔性好、保香性强、耐油及有机溶剂、作为废品处理时无有害物质产生的真空包装米类物料的材料,克服现有技述的不足。
本发明的真空包装米类物料的材料,由EVOH基材膜和尼龙膜通过干法复合形成的;
所述的EVOH基材膜为层状结构,中间层的原料为EVOH,在中间层的两面有粘合树脂层,粘合树脂层的外侧有PE层,各层的质量配比依次为:
PE层:粘合树脂层:EVOH层:粘合树脂层:PE层=3:0.8~1.2:0.5~1:0.8~1.2:3;
所述的EVOH基材膜是利用内冷风循环式多层共挤设备挤出成型的;
所述的PE层为LDPE与LLDPE按30:70的质量比例混合、LDPE与LLDPE按25:75的质量比例混合、LDPE与MLLDPE按40:60的质量比例混合后利用多层共挤方式形成的三层膜或其中任意两种混合料形成的二层膜。
本发明的真空包装米类物料的材料,其中所述的各层的质量配比依次为:
PE层:粘合树脂层:EVOH层:粘合树脂层:PE层=3:1:0.75:1:3。
本发明的真空包装米类物料的材料,与现有技术相比具有阻隔性好、保香性强、耐油及有机溶剂、作为废品处理时无有害物质产生的优点。
具体实施方式
本发明的真空包装米类物料的材料,是由EVOH基材膜和尼龙膜通过干法复合形成的。其中尼龙膜为现有的材料,干法复合工艺为现有技术,均不再详述。
本发明中的EVOH基材膜为层状结构,中间层的原料为EVOH,在中间层的两面有粘合树脂层,粘合树脂层的外侧有PE层,各层的质量配比依次为:
PE层:粘合树脂层:EVOH层:粘合树脂层:PE层=3:0.8~1.2:0.5~1:0.8~1.2:3,即粘合树脂层的质量在0.8、0.9、1.0、1.1、1.2中选择;EVOH层的质量在0.5、0.6、0.7、0.75、0.8、0.9、1中选择。
EVOH基材膜是利用内冷风循环式多层共挤设备挤出成型的。
其中PE层为LDPE与LLDPE按30:70的质量比例混合、LDPE与LLDPE按25:75的质量比例混合、LDPE与MLLDPE按40:60的质量比例混合后利用多层共挤方式形成的三层膜或其中任意两种混合料形成的二层膜。
PE中各原料混合的比例可在上述给出的数值基础上有所浮动,浮动范围为正负5,即在上述限定的区间内均可。
本发明的材料即复合膜与现有膜指标对比如下:
本发明复合膜的产品特性:
①采用尼龙膜进行里印,膜薄、透明度高,对文字、图案、色彩再现性优,能真实反应设计者的精心设计。
②热封基材膜采用多层共挤EVOH高阻隔膜,利用其特殊的高阻氧气性能,可使内包装大米保鲜性长达半年之久,不会存在变质和营养成分的流失。这是所谓的其它阻隔膜无法达到的技术指标。
③采用干法复合工艺,利用外层尼龙膜的透氧、透湿性能,将残留溶剂彻底释放出去,确保产品无异味。从而保证产品质量持续长期稳定。
④具有特殊的抗介质性能:耐油性和耐有机溶剂性。
Claims (2)
1.一种真空包装米类物料的材料,其特征在于:
所述的材料是由EVOH基材膜和尼龙膜通过干法复合形成的;
所述的EVOH基材膜为层状结构,中间层的原料为EVOH,在中间层的两面有粘合树脂层,粘合树脂层的外侧有PE层,各层的质量配比依次为:
PE层:粘合树脂层:EVOH层:粘合树脂层:PE层=3:0.8~1.2:0.5~1:0.8~1.2:3;
所述的EVOH基材膜是利用内冷风循环式多层共挤设备挤出成型的;
所述的PE层为LDPE与LLDPE按30:70的质量比例混合、LDPE与LLDPE按25:75的质量比例混合、LDPE与MLLDPE按40:60的质量比例混合后利用多层共挤方式形成的三层膜或其中任意两种混合料形成的二层膜。
2.根据权利要求1所述的真空包装米类物料的材料,其特征在于:所述的各层的质量配比依次为:
PE层:粘合树脂层:EVOH层:粘合树脂层:PE层=3:1:0.75:1:3。