CN102432951A - 一种改性三元乙丙胶 - Google Patents

一种改性三元乙丙胶 Download PDF

Info

Publication number
CN102432951A
CN102432951A CN2011103243285A CN201110324328A CN102432951A CN 102432951 A CN102432951 A CN 102432951A CN 2011103243285 A CN2011103243285 A CN 2011103243285A CN 201110324328 A CN201110324328 A CN 201110324328A CN 102432951 A CN102432951 A CN 102432951A
Authority
CN
China
Prior art keywords
propylene diene
parts
nano
agent
ethylene
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011103243285A
Other languages
English (en)
Inventor
张明宇
沈雯
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhongte Haxon Cable Co Ltd
Original Assignee
Zhongte Haxon Cable Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhongte Haxon Cable Co Ltd filed Critical Zhongte Haxon Cable Co Ltd
Priority to CN2011103243285A priority Critical patent/CN102432951A/zh
Publication of CN102432951A publication Critical patent/CN102432951A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种成本低而性能良好的改性三元乙丙胶。该改性三元乙丙胶，其由下列重量份原料制成：三元乙丙胶100、防老剂RD1-3、氧化锌2-4、增塑剂8-12、润滑剂4-6、偶联剂1-3、硫化剂2-4、纳米蒙脱土18-22、纳米氧化铝28-32、纳米氧化镁18-22。本发明的改性三元乙丙胶具备优良的抗阻燃性能和良好的拉伸强度，很好的耐高低温性能，可以广泛用于矿用电缆领域。

Description

一种改性三元乙丙胶
技术领域
本发明涉及橡胶材料加工领域，具体涉及一种改性三元乙丙胶及其制备方法。
背景技术
三元乙丙胶因其优良的电气性能、机械物理性能及优异的加工性能，在电缆行业广泛地应用。由于三元乙丙胶自身的氧指数较低(氧指数仅17)，限制了其在矿用电缆领域的推广和应用。因此提高三元乙丙胶的阻燃氧指数，对于三元乙丙胶在矿用电缆领域的运用有着现实的意义。用纳米蒙脱土、纳米氧化铝、纳米氧化镁替代三元乙丙胶配方中的碳酸钙及陶土，能充分提高三元乙丙胶的氧指数，解决其在矿用电缆领域应用的瓶颈。纳米蒙脱土是优良的补强和阻燃剂，纳米氧化铝、纳米氧化镁由于其自身含有结晶水，在燃烧过程中利用结晶水挥发吸收热量，实现三元乙丙胶的无卤素阻燃。同时纳米级材料，由于其优异的表面亲和力，对三元乙丙胶的物理机械性能不会产生破坏。
发明内容
本发明的目的在于解决现有技术中的缺陷，提供一种纳米蒙脱土、纳米氧化铝、纳米氧化镁改性的三元乙丙胶，本发明改性的三元乙丙胶具有很高的氧指数，同时具有很高的机械强度，优良的断裂伸长率、很好的体积电阻率。
为实现上述目的本发明采用的技术方案如下：
一种改性三元乙丙胶，其特征在于，其由下列重量份原料制成：
Figure BDA0000101271790000011
Figure BDA0000101271790000021
所述的改性三元乙丙胶，其特征在于，其由下列重量份原料制成：
Figure BDA0000101271790000022
所述的增塑剂为38号汽缸油；所述的润滑剂为微晶石蜡；所述的偶联剂为硅烷偶联剂YGO-1204；所述的硫化剂为硫磺。
本发明的改性三元乙丙胶的制备方法如下：
按配方比例将三元乙丙胶、纳米蒙脱土、纳米氧化铝、纳米氧化镁以及防老剂、增塑剂加入到密炼机中，启动密炼机，将几种原材料充分混合，待密炼室温度达到120℃时，将混合的胶料由密炼室放出，投入到开炼机上进行塑炼，通过滤胶机过滤后碾页，然后加入硫化剂进行二次混炼均匀后，制得改性后的三元乙丙胶。
本发明的有益效果：
本发明的改性后的三元乙丙胶与传统的三元乙丙胶相比较，本发明改性的三元乙丙胶具有很高的氧指数，同时具有很高的机械强度，优良的断裂伸长率、很好的体积电阻率。
具体实施方式
例1
一种改性三元乙丙胶，其是由下列重量份原料制成：
Figure BDA0000101271790000031
增塑剂为38号汽缸油；所述的润滑剂为微晶石蜡；所述的偶联剂为硅
烷偶联剂YGO-1204；所述的硫化剂为硫磺。
制备方法如下：
按配方比例将三元乙丙胶、纳米蒙脱土、纳米氧化铝、纳米氧化镁以及防老剂、增塑剂加入到密炼机中，启动密炼机，将几种原材料充分混合，待密炼室温度达到120℃时，将混合的胶料由密炼室放出，投入到开炼机上进行塑炼，通过滤胶机过滤后碾页，然后加入硫化剂进行二次混炼均匀后，制得改性后的三元乙丙胶。
实验数据
下表为本实施例中改性后的三元乙丙胶与传统的三元乙丙胶机械物理性能的试验对比：
Figure BDA0000101271790000032
由上表可见，本发明中用纳米蒙脱土、纳米氧化铝、纳米氧化镁与三元乙丙胶共混，得到的混炼胶，经平板硫化后，测得其拉伸强度等机械物理性能，较传统的三元乙丙胶有大幅的提高，同时阻燃氧指数有很大的提高。
例2
一种改性三元乙丙胶，由A、B两部分混炼而成，
A组分由下列重量份原料制成：
Figure BDA0000101271790000041
增塑剂为38号汽缸油；所述的润滑剂为微晶石蜡；所述的偶联剂为硅
烷偶联剂YGO-1204；所述的硫化剂为硫磺。
按配方比例将三元乙丙胶、纳米蒙脱土、纳米氧化铝、纳米氧化镁以及防老剂、增塑剂加入到密炼机中，启动密炼机，将几种原材料充分混合，待密炼室温度达到120℃时，将混合的胶料由密炼室放出，投入到开炼机上进行塑炼，通过滤胶机过滤后碾页，然后加入硫化剂进行二次混炼均匀后，制得A组分。
B组分由下列重量份原料制成：
Figure BDA0000101271790000042
Figure BDA0000101271790000051
制备方法如下：
按配方比例将除硫磺外原料组分加入到密炼机中，启动密炼机，将几种原材料充分混合，待密炼室温度达到130℃时，将混合的胶料由密炼室放出，投入到开炼机上进行塑炼，通过滤胶机过滤后碾页，然后加入硫磺进行二次混炼均匀后，制得B组分。
将制得的A、B组分进行混炼混匀，制得改性后的三元乙丙胶。
实验数据
下表为本实施例中改性后的三元乙丙胶与传统的三元乙丙胶机械物理性能的试验对比：
Figure BDA0000101271790000052

Claims (3)

1.一种改性三元乙丙胶，其特征在于，其由下列重量份原料制成 ：
三元乙丙胶     100
防老剂RD       1-3
氧化锌          2-4
增塑剂          8-12
润滑剂          4-6
偶联剂          1-3
硫化剂          2-4
纳米蒙脱土     18-22
纳米氧化铝     28-32
纳米氧化镁     18-22。
2.根据权利要求1所述的改性三元乙丙胶，其特征在于，其由下列重量份原料制成 ：
三元乙丙胶     100
防老剂RD       2
氧化锌          3
增塑剂          10
润滑剂          5
偶联剂          2
硫化剂          3
纳米蒙脱土      20
纳米氧化铝      30
纳米氧化镁      20。
3.根据权利要1或2所述的改性三元乙丙胶，其特征在于：所述的增塑剂为38号汽缸油；所述的润滑剂为微晶石蜡；所述的偶联剂为硅烷偶联剂YGO-1204；所述的硫化剂为硫磺。
CN2011103243285A 2011-10-24 2011-10-24 一种改性三元乙丙胶 Pending CN102432951A (zh)