CN102432177A - 绿色液下专用防淬石英玻璃管 - Google Patents
绿色液下专用防淬石英玻璃管 Download PDFInfo
- Publication number
- CN102432177A CN102432177A CN2011102746183A CN201110274618A CN102432177A CN 102432177 A CN102432177 A CN 102432177A CN 2011102746183 A CN2011102746183 A CN 2011102746183A CN 201110274618 A CN201110274618 A CN 201110274618A CN 102432177 A CN102432177 A CN 102432177A
- Authority
- CN
- China
- Prior art keywords
- quartz glass
- glass tube
- quenching
- oxide
- liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种绿色液下专用防淬石英玻璃管,在生产石英玻璃管的高纯石英砂中,以高纯石英砂的重量为基本重量份,添加有下述重量份的原料:氧化铜0.1~0.8‰、氯化钠0.001~0.01‰、三氧化二铁0.001~0.03‰、硝酸钾0.001~0.03‰、氧化铕0.01~0.05‰、氧化铝0.001~0.05‰、三氧化二铬或重铬酸钾0.1~0.8‰,将以上原料与高纯石英砂充分混合后,进炉熔炼,再拉制成所需的石英玻璃管。采用管壁整体着色制备工艺拉制成型的绿色液下专用防淬石英玻璃管,管壁整体着色均匀、不炸管、强度高。是水下或液下照明电器专用的超强度防淬石英玻璃管。
Description
技术领域
本发明涉及一种石英管的制备技术,特别是一种绿色液下专用防淬石英玻璃管。
背景技术
石英玻璃的热膨胀系数小,并具有耐高温、透紫外、透红外等特点,市场需求量大,现在已越来越广泛地应用于工业及民用加热产品的外包管上。目前还没有专门用于水下或液下照明电器专用的石英玻璃管。
发明内容
本发明要解决的技术问题是针对现有技术的不足,提出了一种管壁整体着色均匀、不炸管、高强度的绿色液下专用防淬石英玻璃管。
本发明要解决的技术问题是通过以下技术方案来实现的,一种绿色液下专用防淬石英玻璃管,其特点是:在生产石英玻璃管的高纯石英砂中,以高纯石英砂的重量为基本重量份,添加有下述重量份的原料:
氧化铜0.1~0.8‰、 氯化钠0.001~0.01‰、
三氧化二铁0.001~0.03‰、 硝酸钾0.001~0.03‰、
氧化铕0.01~0.05‰、 氧化铝0.001~0.05‰、
三氧化二铬或重铬酸钾0.1~0.8‰,
将以上原料与高纯石英砂充分混合后,进炉熔炼,再拉制成所需的石英玻璃管。
本发明与现有技术相比,采用管壁整体着色制备工艺拉制成型的绿色液下专用防淬石英玻璃管,管壁整体着色均匀、不炸管、强度高。是水下或液下照明电器专用的超强度防淬石英玻璃管。
具体实施方式
一种绿色液下专用防淬石英玻璃管,在生产石英玻璃管的高纯石英砂中,以高纯石英砂的重量为基本重量份,添加有下述重量份的原料:
氧化铜0.1~0.8‰、 氯化钠0.001~0.01‰、
三氧化二铁0.001~0.03‰、 硝酸钾0.001~0.03‰、
氧化铕0.01~0.05‰、 氧化铝0.001~0.05‰、
三氧化二铬或重铬酸钾0.1~0.8‰,
将以上原料与高纯石英砂充分混合,添加时,先将与高纯石英砂在常温下无反应的氯化钠、三氧化二铁、硝酸钾、氧化铝、三氧化二铬或重铬酸钾分添加到高纯石英砂中进行搅拌混合;再将氧化铜、氧化铕添加到高纯石英砂中,并进行尾气回收处理,然后进行烤砂,冷却至常温后,入连熔炉进炉熔炼,拉制成所需的石英玻璃管。
Claims (1)
1.一种绿色液下专用防淬石英玻璃管,其特征在于:
在生产石英玻璃管的高纯石英砂中,以高纯石英砂的重量为基本重量份,添加有下述重量份的原料:
氧化铜0.1~0.8‰、 氯化钠0.001~0.01‰、
三氧化二铁0.001~0.03‰、 硝酸钾0.001~0.03‰、
氧化铕0.01~0.05‰、 氧化铝0.001~0.05‰、
三氧化二铬或重铬酸钾0.1~0.8‰,
将以上原料与高纯石英砂充分混合后,进炉熔炼,再拉制成所需的石英玻璃管。