CN103539472A - 轻质隔热耐火浇注料 - Google Patents

轻质隔热耐火浇注料 Download PDF

Info

Publication number
CN103539472A
CN103539472A CN201310550990.1A CN201310550990A CN103539472A CN 103539472 A CN103539472 A CN 103539472A CN 201310550990 A CN201310550990 A CN 201310550990A CN 103539472 A CN103539472 A CN 103539472A
Authority
CN
China
Prior art keywords
parts
alumina
gypsum
float
pearl
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310550990.1A
Other languages
English (en)
Inventor
穆祥
王西来
董伟胜
刘文艳
解仁
刘朝晖
苏新国
王淑娟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NINGXIA TIANZONG HONGGUANG COGENERATION TECHNOLOGY Co Ltd
Original Assignee
NINGXIA TIANZONG HONGGUANG COGENERATION TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NINGXIA TIANZONG HONGGUANG COGENERATION TECHNOLOGY Co Ltd filed Critical NINGXIA TIANZONG HONGGUANG COGENERATION TECHNOLOGY Co Ltd
Priority to CN201310550990.1A priority Critical patent/CN103539472A/zh
Publication of CN103539472A publication Critical patent/CN103539472A/zh
Pending legal-status Critical Current

Abstract

一种轻质隔热耐火浇注料,由以下原料组成:蓝晶石、莫来石、硅灰石、石膏、铝酸盐水泥、氧化铝空心球、漂珠、氧化铝微粉、二氧化硅微粉、三聚磷酸钠;上述原料的重量份数为:蓝晶石10~25份、莫来石10~20份、硅灰石10~20份、石膏10~20份、铝酸盐水泥1~5份、氧化铝空心球5~10份、漂珠5~10份、氧化铝微粉10~15份、二氧化硅微粉1~10份、硅酸钠1~5份。

Description

轻质隔热耐火浇注料
技术领域
[0001] 本发明属于耐火材料技术领域,尤其涉及一种轻质隔热耐火浇注料。
背景技术
[0002] 与定性耐火制品相比,以耐火浇注料为代表的不定形耐火材料具有工艺流程短、生产能耗及成本低、使用方便、适用范围广、整体性及使用效果好等优势,因而在世界范围内得到了迅速发展,其在整个耐火材料中所占的比重越来越高。在一些耐火材料技术先进的国家中,不定形耐火材料的产量已经接近甚至超过了定形制品的产量。例如,目前日本不定形耐火材料产量占整个耐火材料的比例达到了 60%左右;美国的为50%左右;英、德、法等国为40%~50%。如今,耐火浇注料已经被广泛地应用于冶金、建材、电力、化工等工业领域的高温设备中,现已大量应用了各种材质的耐火浇注料。
[0003] 例如,在冶金工厂以及石油、化工行业中,各种类型的加热炉的对流室及加热炉的炉底都普遍使用轻质耐火浇注料。目前,轻质耐火浇注料主要是采用铝酸盐水泥为结合剂的水硬性轻质耐火浇注料,这种浇注料具有衬体均匀、容易施工,整体性好等优点,但也存在着常温强度低、养护时间长的缺陷、保温性能较差致使能源利用率降低的问题。
发明内容
[0004] 有鉴于此,针对现有技术的不足,本发明提供一种体积密度小、热导率低、隔热性能好、衬体成型后无需养护的轻质隔热耐火浇注料。
[0005] 一种轻质隔热耐火浇注料,由以下原料组成:蓝晶石、莫来石、硅灰石、石膏、铝酸盐水泥、氧化铝空心球、漂珠、氧化铝微粉、二氧化硅微粉、三聚磷酸钠;上述原料的重量份数为:蓝晶石10~25份、莫来石10~20份、硅灰石10~20份、石膏10~20份、铝酸盐水泥I~5份、氧化铝空心球5~10份、漂珠5~10份、氧化铝微粉10-15份、二氧化硅微粉f 10份、硅酸钠1~5份。
[0006] 综上所述,本发明与现有技术相比,骨料中的氧化铝空心球、漂珠具有特殊的表面结构且内部空心,表面凹凸不平,增大接触比表面积,使得骨料与基质中铝酸盐水泥、氧化铝微粉、二氧化硅微粉结合牢固,既提高了耐火性能,又增加了物料的强度以及保温效果,采用硅酸钠作为结合剂,充分发挥其本身就具有较好的耐高温的特点,不会带来各种低熔点气化物,提高了使用性能。
具体实施方式
[0007] 下面结合实施例对本发明作进一步详细说明。本具体实施例仅仅是对本发明的解释,其并不是对发明的限制,本领域技术人员在阅读完本说明书后可以根据需要对本实施例做出任何修改,但只要在本发明的权利要求范围内都受到专利法的保护。
[0008] 实施例1
一种轻质隔热耐火浇注料,由以下原料组成:蓝晶石、莫来石、硅灰石、石膏、铝酸盐水泥、氧化铝空心球、漂珠、氧化铝微粉、二氧化硅微粉、三聚磷酸钠;上述原料的重量份数为:蓝晶石10份、莫来石10份、硅灰石10份、石膏20份、铝酸盐水泥5份、氧化铝空心球10份、漂珠10份、氧化铝微粉15份、二氧化硅微粉5份、硅酸钠5份。莫来石、硅灰石、石膏、氧化铝空心球、漂珠混合后获得的混合物作为骨料;氧化铝微粉、二氧化硅微粉混合后获得的混合物作为基质;招酸盐水泥、娃酸钠作为复合结合剂,三聚磷酸钠作为减水剂。
[0009] 实施例2 一种轻质隔热耐火浇注料,由以下原料组成:蓝晶石、莫来石、硅灰石、石膏、铝酸盐水泥、氧化铝空心球、漂珠、氧化铝微粉、二氧化硅微粉、三聚磷酸钠;上述原料的重量份数为:蓝晶石25份、莫来石15份、硅灰石15份、石膏10份、铝酸盐水泥3份、氧化铝空心球7份、漂珠7份、氧化铝微粉10份、二氧化硅微粉6份、硅酸钠2份。莫来石、硅灰石、石膏、氧化铝空心球、漂珠混合后获得的混合物作为骨料;氧化铝微粉、二氧化硅微粉混合后获得的混合物作为基质;招酸盐水泥、娃酸钠作为复合结合剂,三聚磷酸钠作为减水剂。
[0010] 实施例3
一种轻质隔热耐火浇注料,由以下原料组成:蓝晶石、莫来石、硅灰石、石膏、铝酸盐水泥、氧化铝空心球、漂珠、氧化铝微粉、二氧化硅微粉、三聚磷酸钠;上述原料的重量份数为:蓝晶石12份、莫来石16份、硅灰石12份、石膏16份、铝酸盐水泥4份、氧化铝空心球8份、漂珠8份、氧化铝微粉14份、二氧化硅微粉6份、硅酸钠4份。莫来石、硅灰石、石膏、氧化铝空心球、漂珠混合后获得的混合物作为骨料;氧化铝微粉、二氧化硅微粉混合后获得的混合物作为基质;招酸盐水泥、娃酸钠作为复合结合剂,三聚磷酸钠作为减水剂。
[0011] 上述保温耐火浇注料的骨料中的氧化铝空心球、漂珠具有特殊的表面结构且内部空心,表面凹凸不平,增大接触比表面积,使得骨料与基质中铝酸盐水泥、氧化铝微粉、二氧化硅微粉结合牢固,既提高了耐火性能,又增加了物料的强度以及保温效果,采用硅酸钠作为结合剂,充分发挥其本身就具有较好的耐高温的特点,不会带来各种低熔点气化物,提高了使用性能。

Claims (4)

1.一种轻质隔热耐火浇注料,其特征在于:由以下原料组成:蓝晶石、莫来石、硅灰石、石膏、铝酸盐水泥、氧化铝空心球、漂珠、氧化铝微粉、二氧化硅微粉、三聚磷酸钠;上述原料的重量份数为:蓝晶石10-25份、莫来石10-20份、硅灰石10-20份、石膏10-20份、铝酸盐水泥I飞份、氧化铝空心球5~10份、漂珠5~10份、氧化铝微粉10-15份、二氧化硅微粉I~10份、娃酸钠I~5份。
2.根据权利要求1所述的轻质隔热耐火浇注料,其特征在于:上述原料的重量份数具体为:蓝晶石10份、莫来石10份、硅灰石10份、石膏20份、铝酸盐水泥5份、氧化铝空心球10份、漂珠10份、氧化铝微粉15份、二氧化硅微粉5份、硅酸钠5份;莫来石、硅灰石、石膏、氧化铝空心球、漂珠混合后获得的混合物作为骨料;氧化铝微粉、二氧化硅微粉混合后获得的混合物作为基质;铝酸盐水泥、硅酸钠作为复合结合剂,三聚磷酸钠作为减水剂。
3.根据权利要求1所述的轻质隔热耐火浇注料,其特征在于:上述原料的重量份数具体为:蓝晶石25份、莫来石15份、硅灰石15份、石膏10份、铝酸盐水泥3份、氧化铝空心球7份、漂珠7份、氧化铝微粉10份、二氧化硅微粉6份、硅酸钠2份;莫来石、硅灰石、石膏、氧化铝空心球、漂珠混合后获得的混合物作为骨料;氧化铝微粉、二氧化硅微粉混合后获得的混合物作为基质;铝酸盐水泥、硅酸钠作为复合结合剂,三聚磷酸钠作为减水剂。
4.根据权利要求1所述的轻质隔热耐火浇注料,其特征在于:上述原料的重量份数具体为:蓝晶石12份、莫来石16份、硅灰石12份、石膏16份、铝酸盐水泥4份、氧化铝空心球8份、漂珠8份、氧化铝微粉14份、二氧化硅微粉6份、硅酸钠4份;莫来石、硅灰石、石膏、氧化铝空心球、漂珠混合后获得的混合物作为骨料;氧化铝微粉、二氧化硅微粉混合后获得的混合物作为基质;铝酸盐 水泥、硅酸钠作为复合结合剂,三聚磷酸钠作为减水剂。
CN201310550990.1A 2013-11-09 2013-11-09 轻质隔热耐火浇注料 Pending CN103539472A (zh)