CN102416732A - 一种镀膜玻璃 - Google Patents
一种镀膜玻璃 Download PDFInfo
- Publication number
- CN102416732A CN102416732A CN2011103050600A CN201110305060A CN102416732A CN 102416732 A CN102416732 A CN 102416732A CN 2011103050600 A CN2011103050600 A CN 2011103050600A CN 201110305060 A CN201110305060 A CN 201110305060A CN 102416732 A CN102416732 A CN 102416732A
- Authority
- CN
- China
- Prior art keywords
- layer
- glass
- coated glass
- radiant panel
- disposed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种镀膜玻璃,包括玻璃层和镀膜层,玻璃层与镀膜层中间设置有辐射板,辐射板上设置有若干小孔。在本发明的一个实施例中,所述的玻璃层为透明层、半透明层、或不透明层。所述的镀膜层材料为彩色印纸。进一步,所述的玻璃层的厚度为300纳米至600纳米之间。另外,所述的辐射板里边设置有金属丝。以便达到更好的防副射效果,结构简单,节能性高,达到了安全环宝的要求,而且颜色丰富,达到了良好的视觉要求,而且可以根据需要来选择透明玻璃或者半透明及不透明,使的灵活性增强。利于推广使用。
Description
技术领域
本发明涉及一种节能装饰玻璃领域,特别涉及到一种镀膜玻璃。
背景技术
目前,镀膜玻璃已经被广泛应用到人们的生产和生活中,现有的镀膜玻璃通常分为两层,即玻璃层和镀膜层,足已达到好看的视觉效果。镀膜玻璃按产品特性可分为以下几类:热反射玻璃、低辐射玻璃、Low-E、导电膜玻璃等。如申请号为200610170597.X的申请文件公开了一种镀膜玻璃,该镀膜玻璃包括玻璃基片和膜层,其中,所述膜层为金属膜,所述金属膜直接附着在玻璃基片的至少一个表面,在所述金属膜上还附着有保护层,所述保护层为紫外光固化漆涂层。而且提供的镀膜玻璃的颜色不会随着视角的不同而发生改变,可以呈现各种具有金属光泽的颜色,能达到透过率低于50%的要求,并且这种玻璃的附着力、铅笔硬度、强度、耐溶剂性都很优异。但是这种镀膜玻璃的隔音效果不是很好,而且是单色镜面产品,产生美感不足。
综上所述,针对有技术的缺陷,特别需要一种即节能,又能跟上时代发展的镀膜玻璃,以解决现有技术的不足。
发明内容
本发明的目的是提供一种镀膜玻璃,使用起来可以达到节能、环宝,而且达到的美感好。从而实现本发明的目的。
本发明所解决的技术问题可以采用以下技术方案来实现:
一种镀膜玻璃,包括玻璃层和镀膜层,玻璃层与镀膜层中间设置有辐射板,辐射板上设置有若干小孔。
在本发明的一个实施例中,所述的玻璃层为透明层、半透明层、或不透明层。
在本发明的一个实施例中,所述的镀膜层材料为彩色印纸。
进一步,所述的玻璃层的厚度为300纳米至600纳米之间。
在本发明的一个实施例中,所述的辐射板里边设置有金属丝。
本发明的优点在于:结构简单,节能性高,达到了安全环宝的要求,而且颜色丰富,达到了良好的视觉要求,而且可以根据需要来选择透明玻璃或者半透明及不透明,使的灵活性增强。利于推广使用。
附图说明
图1是本发明所述的一种镀膜玻璃的结构示意图。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体图示,进一步阐述本发明。
如图1所示,本发明所述的一种镀膜玻璃,包括玻璃层120和镀膜层110,玻璃层120与镀膜层110中间设置有辐射板130,辐射板130上设置有若干小孔。在本发明的一个实施例中,所述的玻璃层120为透明层、半透明层、或不透明层。所述的镀膜层110材料为彩色印纸。进一步,所述的玻璃层120的厚度为300纳米至600纳米之间。另外,所述的辐射板130里边设置有金属丝。以便达到更好的防副射效果,结构简单,节能性高,达到了安全环宝的要求,而且颜色丰富,达到了良好的视觉要求,而且可以根据需要来选择透明玻璃或者半透明及不透明,使的灵活性增强。利于推广使用。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都在要求保护的本发明范围内,本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (5)
1.一种镀膜玻璃,包括玻璃层和镀膜层,其特征在于:玻璃层与镀膜层中间设置有辐射板,辐射板上设置有若干小孔。
2.如权利要求1所述的一种镀膜玻璃,其特征在于,所述的玻璃层为透明层、半透明层、或不透明层。
3.如权利要求1所述的一种镀膜玻璃,其特征在于,所述的镀膜层材料为彩色印纸。
4.如权利要求1所述的一种镀膜玻璃,其特征在于,所述的玻璃层的厚度为300纳米至600纳米之间。
5.如权利要求1所述的一种镀膜玻璃,其特征在于,所述的辐射板里边设置有金属丝。