CN102412035A - 一种高强度胶布带及其制造方法 - Google Patents

一种高强度胶布带及其制造方法 Download PDF

Info

Publication number
CN102412035A
CN102412035A CN2011104504916A CN201110450491A CN102412035A CN 102412035 A CN102412035 A CN 102412035A CN 2011104504916 A CN2011104504916 A CN 2011104504916A CN 201110450491 A CN201110450491 A CN 201110450491A CN 102412035 A CN102412035 A CN 102412035A
Authority
CN
China
Prior art keywords
polyester
cloth
dacron
seccotine
high strength
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011104504916A
Other languages
English (en)
Inventor
张云
周敏玉
杨正龙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
YANGZHOU TENGFEI ELECTRIC CABLE AND APPLIANCE MATERIALS CO Ltd
Original Assignee
YANGZHOU TENGFEI ELECTRIC CABLE AND APPLIANCE MATERIALS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by YANGZHOU TENGFEI ELECTRIC CABLE AND APPLIANCE MATERIALS CO Ltd filed Critical YANGZHOU TENGFEI ELECTRIC CABLE AND APPLIANCE MATERIALS CO Ltd
Priority to CN2011104504916A priority Critical patent/CN102412035A/zh
Publication of CN102412035A publication Critical patent/CN102412035A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种高强度胶布带及其制造方法。包括聚酯涤纶强力纱布层和设置在聚酯涤纶强力纱布层两面的聚酯强力胶层。依据本发明生产出的的产品在保证抗外界压力条件外，还具有生产成本低、生产制造简单、缆结构重量减轻、阻燃、阻水、耐高温（熔点260℃）等优点，可广泛运用一般要求铠装电缆，要求非金属类特种电缆制造、海缆等制造中。

Description

一种高强度胶布带及其制造方法
技术领域
本发明涉及一种高强度胶布带及其制造方法，适用于电缆行业中的绕包之用。 
背景技术
目前电缆制造业中，如需防外界压力或需强抗拉力，一般均使用镀锌钢带或不锈钢带绕包或纵包，不锈钢带因成本高，使用少，而一般镀锌钢带因易生锈，以及钢带边缘有金属刺容易刺入绝缘层易发生事故，特别是在非金属类电缆中（如特种光缆），不能含有金属成份制成的电缆。 
发明内容
本发明针对上述缺陷，目的在于提供一种由非金属材料制造成的高强度胶布带及其制造方法，可应用与电缆行业制造中的绕包之用。 
为此本发明采用的技术方案是：本发明包括聚酯涤纶强力纱布层和设置在聚酯涤纶强力纱布层两面的聚酯强力胶层。 
本发明的涂胶布带按以下工艺步骤进行： 
1）织布：用聚酯涤纶纱做经纱和纬纱织成聚酯涤纶强力纱布，其经纱和纬纱密度为20-25根/cm，布厚为0.3-0.35mm，克重为300-400g/m2；
2）涂胶：通过涂布机将聚酯强力胶涂设在聚酯涤纶强力纱布两面，制成涂胶布带；其中聚酯强力胶组成及其重量比为：聚酯强力胶40-50%、阻燃剂T2O35-8%、晶硅砂42-55%；
3）烘干：通过烘干机将涂胶布带烘干、并高温烘滚整平；
4）收卷：强风冷却并收卷，最后经过分切机分切成品。
所述的聚酯涤纶纱线密度为1500dtex。 
所述烘干机烘干温度为180-200℃。 
所述烘滚温度为180-190℃。 
本发明的优点是：依据本发明生产出的的产品在保证抗外界压力条件外，还具有生产成本低、生产制造简单、缆结构重量减轻、阻燃、阻水、耐高温（熔点260℃）等优点，可广泛运用一般要求铠装电缆，要求非金属类特种电缆制造、海缆（内层绕包，起抗强压力、防水作用）等制造中。 
附图说明
图1为本发明的结构示意图。 
图中1为聚酯涤纶强力纱布层、2为聚酯强力胶层。 
具体实施方式
实施例一： 
本发明包括聚酯涤纶强力纱布层1和设置在聚酯涤纶强力纱布层1两面的聚酯强力胶层2。
本发明按以下工艺步骤进行： 
1）织布：用聚酯涤纶纱做经纱和纬纱织成聚酯涤纶强力纱布，其经纱和纬纱密度为20根/cm，布厚为0.35mm，克重为300g/m2；
2）涂胶：通过涂布机将聚酯强力胶涂设在聚酯涤纶强力纱布两面，制成涂胶布带；其中聚酯强力胶组成及其重量比为：聚酯强力胶40%、阻燃剂T2O35-8%、晶硅粉55%；
3）烘干：通过烘干机将涂胶布带烘干、并高温烘滚整平；
4）收卷：强风冷却并收卷，最后经过分切机分切成品。
所述烘干机烘干温度为180℃。 
所述烘滚温度为180℃。 
实施例二： 
本发明包括聚酯涤纶强力纱布层1和设置在聚酯涤纶强力纱布层1两面的聚酯强力胶层2。
本发明按以下工艺步骤进行： 
1）织布：用聚酯涤纶纱做经纱和纬纱织成聚酯涤纶强力纱布，其经纱和纬纱密度为25根/cm，布厚为0.3mm，克重为400g/m2；
2）涂胶：通过涂布机将聚酯强力胶涂设在聚酯涤纶强力纱布两面，制成涂胶布带；其中聚酯强力胶组成及其重量比为：聚酯强力胶50%、阻燃剂T2O38%、晶硅粉42%；
3）烘干：通过烘干机将涂胶布带烘干、并高温烘滚整平；
4）收卷：强风冷却并收卷，最后经过分切机分切成品。
所述的聚酯涤纶纱线密度为1500dtex。 
所述烘干机烘干温度为200℃。 
所述烘滚温度为190℃。 
实施例三： 
本发明包括聚酯涤纶强力纱布层1和设置在聚酯涤纶强力纱布层1两面的聚酯强力胶层2。
本发明按以下工艺步骤进行： 
1）织布：用聚酯涤纶纱做经纱和纬纱织成聚酯涤纶强力纱布，其经纱和纬纱密度为22根/cm，布厚为0.32mm，克重为350g/m2；
2）涂胶：通过涂布机将聚酯强力胶涂设在聚酯涤纶强力纱布两面，制成涂胶布带；其中聚酯强力胶组成及其重量比为：聚酯强力胶45%、阻燃剂T2O37%、晶硅砂48%；
3）烘干：通过烘干机将涂胶布带烘干、并高温烘滚整平；
4）收卷：强风冷却并收卷，最后经过分切机分切成品。
所述的聚酯涤纶纱线密度为1500dtex。 
所述烘干机烘干温度为200℃。 
所述烘滚温度为185℃。 
经检测：本发明具有以下性质： 
Figure 449307DEST_PATH_IMAGE001
本发明的聚酯强力胶将聚酯强力胶、阻燃剂、晶硅砂三种材料按比例相混合，通过高速搅拌而成，搅拌机速度大于800转/分。

Claims (5)

1.一种高强度涂胶布带，其特征在于，包括聚酯涤纶强力纱布层和设置在聚酯涤纶强力纱布层两面的聚酯强力胶层。
2.一种高强度涂胶布带的制造方法，其特征在于，按以下工艺步骤进行：
1）织布：用聚酯涤纶纱做经纱和纬纱织成聚酯涤纶强力纱布，其经纱和纬纱密度为20-25根/cm，布厚为0.3-0.35mm，克重为300-400g/m2；
2）涂胶：通过涂布机将聚酯强力胶涂设在聚酯涤纶强力纱布两面，制成涂胶布带；其中聚酯强力胶组成及其重量比为：聚酯强力胶40-50%、阻燃剂T2O35-8%、晶硅砂42-55%；
 3）烘干：通过烘干机将涂胶布带烘干、并高温烘滚整平；
4）收卷：强风冷却并收卷，最后经过分切机分切成品。
3.根据权利要求2所述的一种高强度涂胶布带的制造方法，其特征在于，所述的聚酯涤纶纱线密度为1500dtex。
4.根据权利要求2所述的一种高强度涂胶布带的制造方法，其特征在于，所述烘干机烘干温度为180-200℃。
5.根据权利要求2或4所述的一种高强度涂胶布带的制造方法，其特征在于，所述烘滚温度为180-190℃。
CN2011104504916A 2011-12-29 2011-12-29 一种高强度胶布带及其制造方法 Pending CN102412035A (zh)