CN102407287A - 一种彩色银饰材料的合成及加工工艺 - Google Patents
一种彩色银饰材料的合成及加工工艺 Download PDFInfo
- Publication number
- CN102407287A CN102407287A CN2011103556167A CN201110355616A CN102407287A CN 102407287 A CN102407287 A CN 102407287A CN 2011103556167 A CN2011103556167 A CN 2011103556167A CN 201110355616 A CN201110355616 A CN 201110355616A CN 102407287 A CN102407287 A CN 102407287A
- Authority
- CN
- China
- Prior art keywords
- casting
- silver
- powder
- wax
- cast
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种彩色银饰材料的材料合成及加工工艺，涉及珠宝首饰品的生产加工。工艺步骤包括如下步骤：准备蜡模：准备好生产产品的蜡模；种蜡树：将产品的蜡模熔接在蜡杆上，方向倾斜向上，做好的蜡树放入铸粉筒内；制作石膏模：首先制做铸粉浆，然后将铸粉浆倒入铸粉筒内进行干燥；烧粉除蜡：将铸粉筒放入炉内烧制；产品铸造：将配好的银料及红银补口放入真空吸铸机中进行铸造，红银补口主要成分为Ag、Cu及微量Si、Ge，设定熔铸温度960℃；冲水：将铸好的铸粉筒放置冷却20分钟后可以开始冲水，冲干净包裹银件的铸粉和清洗。通过该材料及铸造方法解决了银工艺品材质颜色单一、生产过程中容易变形，且不利于镶嵌问题。该工艺可广泛应用于银饰材料的合成和加工中。
Description
技术领域
本发明涉及一种珠宝首饰品的生产加工，进一步涉及一种彩色银饰材料的合成及加工工艺。
背景技术
银饰是用银制成的各种各样的装饰品，银为贵金属之一，银白色，银饰采用各种加工工艺，加工成的饰品种类繁多，基本分为耳饰、颈饰、手饰、足饰和服饰5个大类。
由于银自然硬度较低，生产过程中容易变形，且不利于镶嵌，不适合高品质珠宝饰品款式的工艺品质要求。另外，银饰品在空气环境下容易氧化生成黑色的氧化银，影响饰品的美观。
而且，目前银饰品材料只有白色，材质颜色单一；银饰品需要改变颜色只能靠表面电镀的方法，提高了银饰产品的制造成本，而且所产生的电镀废液也会对环境产生污染。
发明内容
鉴于以上内容，有必要提供一种可以节省成本，对环境无污染且能持久保持外观的彩色银饰的加工合成方法。
本发明提供了一种彩色银饰材料的材料合成及加工工艺，该工艺包括：
(1)准备蜡模：准备好生产产品的蜡模；
(2)种蜡树：将产品的蜡模熔接在蜡杆上，方向倾斜向上，做好的蜡树放入铸粉筒内；
(3)制作石膏模：首先制做铸粉浆，然后将铸粉浆倒入铸粉筒内进行干燥；
(4)烧粉除蜡：将铸粉筒放入炉内烧制；
(5)产品铸造：将配好的银料及红银补口材料放入真空吸铸机中进行铸造，设定熔铸温度960℃；
(6)冲水：将铸好的铸粉筒放置冷却20分钟后可以开始冲水，冲干净包裹银件的铸粉；
(7)清洗：将银件放入磷酸溶液中浸泡约酸洗，洗后再一次冲水，冲干净银件上的残留物。
优选的，步骤(2)中倾斜向上的角度为70度；
优选的，步骤(3)中具体的工艺为：1、制做铸粉浆：按铸粉要求比例配水，充分搅匀，搅匀后放入抽真空机抽真空1分钟；2、将铸粉浆倒入铸粉筒内，抽真空2分钟，铸粉凝固后放入抽湿机干燥4-6小时；
优选的，步骤(4)中烧粉除蜡的具体工艺为：将铸粉筒放入炉内烧制12-14小时，烧粉炉温度控制需严格按照温控程式进行，烧粉炉温控程式：0-150℃＝1小时、150℃＝2小时、150-300℃＝1小时、300-500℃＝1小时、500-600℃＝1小时、600℃＝6小时；
与现有技术相比，本发明的优点在于：
(1)本发明通过制模铸造的方法，提高了银制品的成型效率；
(2)通过蜡件角度、烧粉时间、铸造温度及冲水时间控制，配合特殊比例的红银补口，有效地改变了银饰材料的颜色及硬度。
附图说明
下面参照附图结合实施例对本发明作进一步的描述。
图1是本发明制造银工艺品的加工工艺流程图。
具体实施方式
请参阅图1的工艺流程图，本发明装较佳实施例的银工艺品加工工艺步骤包括如下步骤：
(1)准备蜡模：准备好生产产品的蜡模；
(2)种蜡树：将产品的蜡模熔接在蜡杆上，方向倾斜向上，倾斜角度为60度，做好的蜡树放入铸粉筒内；
(3)制作石膏模：1、制做铸粉浆：按铸粉要求比例配水，充分搅匀，搅匀后放入抽真空机抽真空1分钟；2、将铸粉浆倒入铸粉筒内，抽真空2分钟，铸粉凝固后放入抽湿机干燥4-6小时；
(4)烧粉除蜡：将铸粉筒放入炉内烧制12-14小时，烧粉炉温度控制需严格按照温控程式进行，烧粉炉温控程式：0-150℃＝1小时、150℃＝2小时、150-300℃＝1小时、300-500℃＝1小时、500-600℃＝1小时、600℃＝6小时；
(5)产品铸造：将配好的银料和红银补口材料放入真空吸铸机中进行铸造，设定熔铸温度960℃；
(6)冲水：将铸好的铸粉筒放置冷却20分钟后可以开始冲水，冲干净包裹银件的铸粉；
(7)清洗：将银件放入磷酸溶液中浸泡约酸洗，洗后再一次冲水，冲干净银件上的残留物。
通过上述步骤获得银工艺品，通过常规检测，所的参数如下：产品成份：Ag、Cu及微量Si、Ge
色泽：红色
比重(g/cm3)：9.89
铸粉温度：480-600℃
熔炼温度：960℃
退火温度：600℃
冷却时间：15-20分钟
维氏硬度：101.5
因此，该银工艺品表现了良好的硬度、表面光泽度。
本发明主要针对银工艺品工艺流程所进行的改进，以上所述仅为本发明较佳实施例而已，非因此即局限本发明的专利范围，故举凡用本发明说明书及图式内容所为的简易变化及等效变换，均应包含于本发明的专利范围内。
Claims (4)
1.一种彩色银饰材料的材料合成及加工工艺，包括银饰铸造，其特征在于，工艺包括如下步骤：
(1)准备蜡模：准备好生产产品的蜡模；
(2)种蜡树：将产品的蜡模熔接在蜡杆上，方向倾斜向上，做好的蜡树放入铸粉筒内；
(3)制作石膏模：首先制做铸粉浆，然后将铸粉浆倒入铸粉筒内进行干燥；
(4)烧粉除蜡：将铸粉筒放入炉内烧制；
(5)产品铸造：将配好的银料及红银补口放入真空吸铸机中进行铸造，设定熔铸温度960℃；
(6)冲水：将铸好的铸粉筒放置冷却20分钟后可以开始冲水，冲干净包裹银件的铸粉；
(7)清洗：将银件放入磷酸溶液中浸泡约酸洗，洗后再一次冲水，冲干净银件上的残留物。
2.根据权利要求1所述彩色银饰材料的合成及加工工艺，其特征在于：步骤(2)中倾斜向上的角度为70度。
3.根据权利要求1所述彩色银饰材料的合成及加工工艺，其特征在于：步骤(3)中具体的工艺为：1、制做铸粉浆：按铸粉要求比例配水，充分搅匀，搅匀后放入抽真空机抽真空1分钟；2、将铸粉浆倒入铸粉筒内，抽真空2分钟，铸粉凝固后放入抽湿机干燥4-6小时。
4.根据权利要求1所述彩色银饰材料的合成及加工工艺，其特征在于：步骤(4)中烧粉除蜡的具体工艺为：将铸粉筒放入炉内烧制12-14小时，烧粉炉温度控制需严格按照温控程式进行，烧粉炉温控程式：0-150℃＝1小时、150℃＝2小时、150-300℃＝1小时、300-500℃＝1小时、500-600℃＝1小时、600℃＝6小时。