CN110978214A - 一种金属仿真植物的制作方法 - Google Patents
一种金属仿真植物的制作方法 Download PDFInfo
- Publication number
- CN110978214A CN110978214A CN201911300586.2A CN201911300586A CN110978214A CN 110978214 A CN110978214 A CN 110978214A CN 201911300586 A CN201911300586 A CN 201911300586A CN 110978214 A CN110978214 A CN 110978214A
- Authority
- CN
- China
- Prior art keywords
- metal
- gypsum
- plant
- making
- steps
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种金属仿真植物的制作方法，目的在于解决金属仿真植物采用传统失蜡法铸造工艺存在的蜡模制作技术要求高，成型工艺复杂等的缺陷，本发明免于制作复杂蜡模，工艺相对简单，对技术的要求相对较低，适合工业化生产，样模取材多元化，成本低廉，制作的产品仿真度高，纹理逼真自然。
Description
技术领域
本发明涉及金属工艺品加工技术领域，特别涉及一种金属仿真植物的制作方法。
背景技术
金属工艺品是采用金、银、铜、铁、锡等金属材料，或以金属材料为主辅以其他材料，加工制作而成的工艺品，具有厚重、雄浑、华贵、典雅、精细的风格。中国最早的金属工艺品，是新石器中期的马家窑文化、大汶口文化及稍晚的乔家文化等遗址中出土的铜制工艺品。商代出现金制工艺品。战国时期，有多种金属材料结合和金属与非金属材料(玉石、琉璃)结合制作而成的工艺品。汉代能生产精巧的金银丝编结、堆垒和镶嵌制品。唐代是金属工艺品尤其是银制工艺品的鼎盛时期，创造了浮雕般艺术效果的金银錾凿工艺。在宋、元、明、清约千年中，由于冶炼技术的进步，金属材料的增多,金属工艺品有了很大发展,不仅有多种金属和多种材料并用的工艺品，而且有多种工艺相结合的工艺品。中国古代著名的金属工艺品有商代的青铜器、战国的金银错、唐代的铜镜和首饰、明代的宣德炉、清代的景泰蓝。20世纪70～80年代，又出现了铝合金、钛、铂等金属工艺品，并创新了腐蚀填漆、钛阴极氧化着色及负氧离子镀等新工艺。
众所周知，金属制品或工艺品制造往往采用模具铸造或者熔模铸造（失蜡法）等传统的铸造工艺技术，无论哪一种铸造工艺技术，其制造工艺和流程往往比较复杂，制造周期也比较长，且需要较高的技术工艺。金属植物由于其结构的复杂纤细一般采用失蜡法来制造，传统失蜡法铸造工艺存在的蜡模制作技术要求高，成型工艺复杂等的缺陷。
发明内容
本发明的目的在于解决金属仿真植物采用传统失蜡法铸造工艺存在的蜡模制作技术要求高，成型工艺复杂等的缺陷，提供一种金属仿真植物的制作方法，工艺相对简单，对技术的要求相对较低，适合工业化生产，样模取材多元化，成本低廉，制作的产品仿真度高，纹理逼真自然。
本发明解决其技术问题所采用的技术方案是：
一种金属仿真植物的制作方法，包括以下步骤：
（1）配置石膏浆；
（2）以刷涂或浸渍的方式用石膏浆给植物样品上浆，待石膏自然固化20-40min后对样品整形；
（3）将步骤（2）上浆固化后的植物样品放入一模腔中，并将石膏浆倒入模腔中使之充满并定型，并在植物样品尾部预制浇铸口，待石膏自然固化30-120min后得石膏模；模腔为常规的金属方形或圆形模腔；
（4）将石膏模放入110-130℃烘箱中烘1-2小时，然后以1-5℃/min的升温速度升温至600-700℃，保温1-2小时使得植物样品熔融炭化，自然冷却至室温；
（5）将步骤（4）处理后的石膏模通过尾部预制的浇铸口清理出炭化的废料并用气枪吹扫干净内部成型型腔；
（6）通过浇铸口向石膏模的成型型腔内浇铸金属融液，浇筑完成后自然冷却成型，最后将外部的石膏壳去除取出里面已冷却定型的金属植物制品，并将尾部的浇铸口切割清除，获得金属仿真植物制品。
本发明为了适合比较纤细，容易弯折变形的植物的模具制作，先给样品上薄薄一层石膏浆料，这样的好处是不会因为直接浇注石膏浆导致植物的叶片、枝条或花瓣等变形，上完薄薄一层石膏浆料后石膏固化就是为了初步定型，从而维持样品再后续造模时不发生变形。接着浇铸石膏模，然后石膏模经预热后再缓慢升温使得植物样品熔融炭化，这样的好处是防止精细的石膏模型由于植物样品熔融炭化时发生开裂变形。
作为优选，步骤（1）中所述石膏浆由石膏粉和水按照1.4-1.6:1的重量比混合而成。
作为优选，对调配好的石膏浆进行真空脱泡。
作为优选，步骤（2）中，上浆厚度为0.2-0.5mm。
作为优选，所述植物样品包含花卉、松树、柏树。本发明的工艺除了适合植物样品之外，其它动物样品也可用。
作为优选，所述植物样品为塑料仿真植物或真实植物。真实植物为干燥或新鲜植物。
作为优选，所述金属融液的金属选自铜、铁、银、铝、金中的一种。
作为优选，所述金属融液由黄铜边角料、助熔剂硼砂以及低熔点金属锡和铝混合后加热熔融而得。在金属熔融的同时添加少许低熔点的金属和相应的助熔剂，降低金属熔融的温度和增加熔融金属的流动性。
作为优选，锡的用量为黄铜边角料重量的1-2%，铝的用量为黄铜边角料重量的0.5-1%，硼砂用量为黄铜边角料重量的0.3-0.5%。
本发明的有益效果是：本发明通过研发人的研发，开发了一种新型的免于制作复杂蜡模的金属仿真花卉的铸造制作工艺和方法。工艺相对简单，对技术的要求相对较低，适合工业化生产，样模取材多元化，成本低廉，制作的产品仿真度高，纹理逼真自然。
附图说明
图1是本发明一种产品图。
图2是本发明另一种产品图。
具体实施方式
下面通过具体实施例，对本发明的技术方案作进一步的具体说明。
本发明中，若非特指，所采用的原料和设备等均可从市场购得或是本领域常用的。下述实施例中的方法，如无特别说明，均为本领域的常规方法。
实施例1：
一种金属仿真植物的制作方法，包括以下步骤：
（1）按照石膏粉和水按照1.4:1的重量比混合而成获得石膏浆，对调配好的石膏浆进行真空脱泡；
（2）以刷涂的方式用石膏浆给植物样品（塑料荷花）上浆，刷涂3-4次，至上浆厚度约0.5mm，待石膏自然固化40min后对样品手工整形；
（3）将步骤（2）上浆固化后的植物样品放入一长方形金属模腔中，并将石膏浆倒入模腔中使之充满并定型，并在植物样品尾部预制浇铸口，待石膏自然固化30min后得石膏模；
（4）将石膏模放入110℃烘箱中烘2小时，然后以1℃/min的升温速度升温至600℃，保温2小时使得植物样品熔融炭化，自然冷却至室温；
（5）将步骤（4）处理后的石膏模通过尾部预制的浇铸口清理出炭化的废料并用气枪吹扫干净内部成型型腔；
（6）通过浇铸口向石膏模的成型型腔内浇铸金属融液，浇筑完成后自然冷却成型，最后将外部的石膏壳去除取出里面已冷却定型的金属植物制品，并将尾部的浇铸口切割清除，获得金属仿真植物制品。所述金属融液由黄铜边角料、助熔剂硼砂以及低熔点金属锡和铝混合后加热熔融而得，锡的用量为黄铜边角料重量的1%，铝的用量为黄铜边角料重量的0.5%，硼砂用量为黄铜边角料重量的0.3%。
实施例2：
一种金属仿真植物的制作方法，包括以下步骤：
（1）按照石膏粉和水按照1.5:1的重量比混合而成获得石膏浆，对调配好的石膏浆进行真空脱泡；
（2）以刷涂的方式用石膏浆给植物样品（新鲜葵花）上浆，刷涂2-3次，至上浆厚度约0.3mm，待石膏自然固化30min后对样品手工整形；
（3）将步骤（2）上浆固化后的植物样品放入一圆形金属模腔中，并将石膏浆倒入模腔中使之充满并定型，并在植物样品尾部预制浇铸口，待石膏自然固化60min后得石膏模；
（4）将石膏模放入130℃烘箱中烘1小时，然后以2℃/min的升温速度升温至650℃，保温1.5小时使得植物样品熔融炭化，自然冷却至室温；
（5）将步骤（4）处理后的石膏模通过尾部预制的浇铸口清理出炭化的废料并用气枪吹扫干净内部成型型腔；
（6）通过浇铸口向石膏模的成型型腔内浇铸金属融液，浇筑完成后自然冷却成型，最后将外部的石膏壳去除取出里面已冷却定型的金属植物制品，并将尾部的浇铸口切割清除，获得金属仿真植物制品如图1，图1中的花瓶为后配。所述金属融液由黄铜边角料、助熔剂硼砂以及低熔点金属锡和铝混合后加热熔融而得，锡的用量为黄铜边角料重量的2%，铝的用量为黄铜边角料重量的1%，硼砂用量为黄铜边角料重量的0.5%。
实施例3：
一种金属仿真植物的制作方法，包括以下步骤：
（1）按照石膏粉和水按照1.6:1的重量比混合而成获得石膏浆，对调配好的石膏浆进行真空脱泡；
（2）以浸渍的方式用石膏浆给植物样品（新鲜松枝）上浆，上浆厚度约0.2mm，待石膏自然固化20min后对样品手工整形；
（3）将步骤（2）上浆固化后的植物样品放入一长方形金属模腔中，并将石膏浆倒入模腔中使之充满并定型，并在植物样品尾部预制浇铸口，待石膏自然固化120min后得石膏模；
（4）将石膏模放入120℃烘箱中烘1.5小时，然后以5℃/min的升温速度升温至700℃，保温1小时使得植物样品熔融炭化，自然冷却至室温；
（5）将步骤（4）处理后的石膏模通过尾部预制的浇铸口清理出炭化的废料并用气枪吹扫干净内部成型型腔；
（6）通过浇铸口向石膏模的成型型腔内浇铸金属融液，浇筑完成后自然冷却成型，最后将外部的石膏壳去除取出里面已冷却定型的金属植物制品，并将尾部的浇铸口切割清除，获得金属仿真植物制品如图2，图2中的底座为后配。所述金属融液由黄铜边角料、助熔剂硼砂以及低熔点金属锡和铝混合后加热熔融而得，锡的用量为黄铜边角料重量的1.5%，铝的用量为黄铜边角料重量的0.8%，硼砂用量为黄铜边角料重量的0.4%。
实施例4：
本实施例与实施例3不同之处在于植物样品为柏树枝，形成金属融液的金属为银。
以上所述的实施例只是本发明的一种较佳的方案，并非对本发明作任何形式上的限制，在不超出权利要求所记载的技术方案的前提下还有其它的变体及改型。
Claims (9)
1.一种金属仿真植物的制作方法，其特征在于，包括以下步骤：
（1）配置石膏浆；
（2）以刷涂或浸渍的方式用石膏浆给植物样品上浆，待石膏自然固化20-40min后对样品整形；
（3）将步骤（2）上浆固化后的植物样品放入一模腔中，并将石膏浆倒入模腔中使之充满并定型，并在植物样品尾部预制浇铸口，待石膏自然固化30-120min后得石膏模；
（4）将石膏模放入110-130℃烘箱中烘1-2小时，然后以1-5℃/min的升温速度升温至600-700℃，保温1-2小时使得植物样品熔融炭化，自然冷却至室温；
（5）将步骤（4）处理后的石膏模通过尾部预制的浇铸口清理出炭化的废料并用气枪吹扫干净内部成型型腔；
（6）通过浇铸口向石膏模的成型型腔内浇铸金属融液，浇筑完成后自然冷却成型，最后将外部的石膏壳去除取出里面已冷却定型的金属植物制品，并将尾部的浇铸口切割清除，获得金属仿真植物制品。
2.根据权利要求1所述的一种金属仿真植物的制作方法，其特征在于：步骤（1）中所述石膏浆由石膏粉和水按照1.4-1.6:1的重量比混合而成。
3.根据权利要求2所述的一种金属仿真植物的制作方法，其特征在于：对调配好的石膏浆进行真空脱泡。
4.根据权利要求1所述的一种金属仿真植物的制作方法，其特征在于：步骤（2）中，上浆厚度为0.2-0.5mm。
5.根据权利要求1所述的一种金属仿真植物的制作方法，其特征在于：所述植物样品包含花卉、松树、柏树。
6.根据权利要求5所述的一种金属仿真植物的制作方法，其特征在于：所述植物样品为塑料仿真植物或真实植物。
7.根据权利要求1所述的一种金属仿真植物的制作方法，其特征在于：所述金属融液的金属选自铜、铁、银、铝、金中的一种。
8.根据权利要求1所述的一种金属仿真植物的制作方法，其特征在于：所述金属融液由黄铜边角料、助熔剂硼砂以及低熔点金属锡和铝混合后加热熔融而得。
9.根据权利要求8所述的一种金属仿真植物的制作方法，其特征在于：锡的用量为黄铜边角料重量的1-2%，铝的用量为黄铜边角料重量的0.5-1%，硼砂用量为黄铜边角料重量的0.3-0.5%。