CN102383578B - Pvc植绒卷材地板的生产方法 - Google Patents

Pvc植绒卷材地板的生产方法 Download PDF

Info

Publication number
CN102383578B
CN102383578B CN 201110346893 CN201110346893A CN102383578B CN 102383578 B CN102383578 B CN 102383578B CN 201110346893 CN201110346893 CN 201110346893 CN 201110346893 A CN201110346893 A CN 201110346893A CN 102383578 B CN102383578 B CN 102383578B
Authority
CN
China
Prior art keywords
pvc
parts
coiled material
baking oven
enhancement layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN 201110346893
Other languages
English (en)
Other versions
CN102383578A (zh
Inventor
张海江
孙佩英
吴炳杰
陈帅帅
张小华
陆冬清
曹建洲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Bei Xin elastic floor Co., Ltd.
Original Assignee
CHANGZHOU LIBERTY DISENO NEW MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGZHOU LIBERTY DISENO NEW MATERIALS Co Ltd filed Critical CHANGZHOU LIBERTY DISENO NEW MATERIALS Co Ltd
Priority to CN 201110346893 priority Critical patent/CN102383578B/zh
Publication of CN102383578A publication Critical patent/CN102383578A/zh
Application granted granted Critical
Publication of CN102383578B publication Critical patent/CN102383578B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种PVC植绒卷材地板，包括PVC增强层、纤维加强层和发泡缓冲层；其特征是在PVC增强层上设有植绒布面层，在植绒布面层和PVC增强层之间设有PVC连接层。本发明还涉及该PVC植绒卷材地板的生产方法。本发明具有舒适踩踏感和柔和视觉感的优点。

Description

PVC植绒卷材地板的生产方法
技术领域
本发明涉及一种PVC植绒卷材地板，尤其涉及一种PVC植绒卷材地板及其生产方法。 
背景技术
目前的PVC卷材地板包括PVC耐磨层、PVC增强层、纤维加强层和发泡缓冲层；PVC卷材地板所具有的特点是：铺设方便、日常维护方便和使用成本低；但PVC卷材地板主要由PVC材料制成，在室内铺设后在踩踏感上比较僵硬，视觉感上都比较冷淡。 
发明内容
针对上述缺点，本发明目的在于提供一种具有舒适的踩踏感和柔和的视觉感的PVC植绒卷材地板。 
   本发明的技术内容为：一种PVC植绒卷材地板，包括PVC增强层、纤维加强层和发泡缓冲层；其特征是在PVC增强层上设有植绒布面层，在植绒布面层和PVC增强层之间设有PVC连接层。 
    本发明的另一目的在于提供上述PVC植绒卷材地板的生产方法。 
一种PVC植绒卷材地板的生产方法，其步骤如下： 
(1)、将邻苯二甲酸二辛酯（DOP）:55～65份、PVC糊树脂　440　:95～105份、钡锌稳定剂：1～3份和石粉填充剂：95～105份混合后搅拌均匀制得PVC连接层浆液；再将DOP:55～65份、PVC糊树脂1702:125～135份、钡锌稳定剂：1～3份和石粉填充剂：120～130份混合后搅拌均匀制得PVC增强层浆液；再将DOP:55～65份、PVC糊树脂450:95～105份、钡锌稳定剂：1～3份、石粉填充剂：120～130份和偶氮二甲酰胺（AC）：2～3份混合后搅拌均匀制得发泡缓冲层浆液；
(2)、通过涂刮机在植绒布背面涂上0.45～0.55mm厚的步骤（1）中制得的PVC连接层浆液后进入烘箱加热即制得卷材地板面层，其烘箱加热温度为160℃～180℃，加热时间为1～3分钟； 
(3)、通过涂刮机在离型纸上涂刮0.6mm～0.8mm厚的步骤（1）中制得的PVC增强层浆液，再在PVC增强层的涂层上贴上玻纤网格布，然后进入烘箱加热，其中烘箱加热温度为205℃～215℃，加热时间为1～2分钟；在冷却后再在贴有玻纤网格布的PVC增强层上通过涂刮机涂刮0.75mm～0.85mm厚的步骤（1）中制得的发泡缓冲层浆液后进入烘箱加热即制得卷材地板底层，其中烘箱加热温度为210℃～220℃，加热时间为2～4分钟；
 (4)、在步骤（2）中制得的卷材地板面层的PVC连接层表面和在步骤（3）中制得的卷材地板底层的PVC增强层表面分别涂上360A PVC革料、布料复合胶，然后进入温度为30～40℃的烘箱加热40～50秒钟后进行压合，在冷却后即为成品PVC植绒卷材地板。
在上述PVC植绒卷材地板的生产方法中石粉填充剂的细度为30～60目。 
本发明与现有技术相比所具有的优点是：通过在原有PVC卷材地板的表面贴合一层植绒布，使得其在铺设后有舒适的踩踏感和柔和的视觉感。 
附图说明
图1为本发明的结构示意图。 
具体实施例
下面通过实施例进一步描述本发明，但未限于所举的实施例。 
在下列实施例中：植绒布为上海思乐地毯有限公司生产；邻苯二甲酸二辛酯（DOP）为洛阳市嘉瑞塑业有限公司生产，其闪点≥192℃；PVC糊树脂440为上海氯碱化工股份有限公司生产，其聚合度1200～1500；PVC糊树脂1702为上海氯碱化工股份有限公司，其聚合度1600～1800；PVC糊树脂450为上海氯碱化工股份有限公司生产，其聚合度900～1200；钡锌稳定剂为杭州东旭助剂有限公司生产；石粉填充剂为南京道润化工有限公司生产，其细度为40目；偶氮二甲酰胺（AC）为济南华尔沃化工有限公司生产，其纯度≥99%；360A PVC革料、布料复合胶为上海晨祥胶粘剂有限公司生产。 
例1：(1)、将邻苯二甲酸二辛酯（DOP）:60份、PVC糊树脂　440　:100份、钡锌稳定剂：2份和石粉填充剂：100份混合后搅拌均匀制得PVC连接层浆液；将DOP:60份、PVC糊树脂　1702:130份、钡锌稳定剂：2份和石粉填充剂：125份混合后搅拌均匀制得PVC增强层浆液；将DOP:60份、PVC糊树脂　450:100份、钡锌稳定剂：2份、石粉填充剂：125份和偶氮二甲酰胺（AC）：2.5份混合后搅拌均匀制得发泡缓冲层浆液； 
(2)、再通过涂刮机上在植绒布背面涂上0.5mm厚的步骤（1）中制得的PVC连接层浆液后进入烘箱加热即制得卷材地板面层，其烘箱加热温度为170℃，加热时间为2分钟； 
(3)、由通过涂刮机在离型纸上涂刮0.7mm厚的步骤（1）中制得的PVC增强层浆液，再在PVC增强层的涂层上贴上玻纤网格布，然后进入烘箱加热，其中烘箱加热温度为210℃，加热时间为2分钟；在冷却后再在贴有玻纤网格布的PVC增强层上通过涂刮机涂刮0.8mm厚的步骤（1）中制得的发泡缓冲层浆液后进入烘箱加热即制得卷材地板底层，其中烘箱加热温度为215℃，加热时间为3分钟；
 (4)、在步骤（2）中制得的卷材地板面层的PVC连接层表面和在步骤（3）中制得的卷材地板底层的PVC增强层表面分别涂上360A PVC革料、布料复合胶，然后进入温度为35℃的烘箱加热45秒钟后进行压合，在冷却后即为成品PVC植绒卷材地板。
如图1所示，该成品PVC植绒卷材地板包括PVC增强层1、纤维加强层2和发泡缓冲层3；其特征是在PVC增强层1上设有植绒布面层4，在植绒布面层4和PVC增强层1之间设有PVC连接层5。 

Claims (1)

1.PVC植绒卷材地板的生产方法，其步骤如下：
(1)、将邻苯二甲酸二辛酯（DOP）:55～65份、PVC糊树脂　440　:95～105份、钡锌稳定剂：1～3份和石粉填充剂：95～105份混合后搅拌均匀制得PVC连接层浆液；再将DOP:55～65份、PVC糊树脂1702:125～135份、钡锌稳定剂：1～3份和石粉填充剂：120～130份混合后搅拌均匀制得PVC增强层浆液；再将DOP:55～65份、PVC糊树脂450:95～105份、钡锌稳定剂：1～3份、石粉填充剂：120～130份和偶氮二甲酰胺（AC）：2～3份混合后搅拌均匀制得发泡缓冲层浆液；其中石粉填充剂的细度为30～60目；
(2)、通过涂刮机在植绒布背面涂上0.45～0.55mm厚的步骤（1）中制得的PVC连接层浆液后进入烘箱加热即制得卷材地板面层，其烘箱加热温度为160℃～180℃，加热时间为1～3分钟； 
(3)、通过涂刮机在离型纸上涂刮0.6mm～0.8mm厚的步骤（1）中制得的PVC增强层浆液，再在PVC增强层的涂层上贴上玻纤网格布，然后进入烘箱加热，其中烘箱加热温度为205℃～215℃，加热时间为1～2分钟；在冷却后再在贴有玻纤网格布的PVC增强层上通过涂刮机涂刮0.75mm～0.85mm厚的步骤（1）中制得的发泡缓冲层浆液后进入烘箱加热即制得卷材地板底层，其中烘箱加热温度为210℃～220℃，加热时间为2～4分钟；
 (4)、在步骤（2）中制得的卷材地板面层的PVC连接层表面和在步骤（3）中制得的卷材地板底层的PVC增强层表面分别涂上360A PVC革料、布料复合胶，然后进入温度为30～40℃的烘箱加热40～50秒钟后进行压合，在冷却后即为成品PVC植绒卷材地板。
CN 201110346893 2011-11-07 2011-11-07 Pvc植绒卷材地板的生产方法 Active CN102383578B (zh)