CN102372475A - 一种新型相变储能石膏板的配比与制备 - Google Patents

一种新型相变储能石膏板的配比与制备 Download PDF

Info

Publication number
CN102372475A
CN102372475A CN2010102481830A CN201010248183A CN102372475A CN 102372475 A CN102372475 A CN 102372475A CN 2010102481830 A CN2010102481830 A CN 2010102481830A CN 201010248183 A CN201010248183 A CN 201010248183A CN 102372475 A CN102372475 A CN 102372475A
Authority
CN
China
Prior art keywords
phase change
change material
energy storage
proportioning
composite energy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2010102481830A
Other languages
English (en)
Inventor
袁艳平
白力
牛犇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2010102481830A priority Critical patent/CN102372475A/zh
Publication of CN102372475A publication Critical patent/CN102372475A/zh
Pending legal-status Critical Current

Abstract

一种含相变材料的复合储能石膏板的配比与制备方法。相变材料由质量比为85.7％∶14.3％的癸酸和棕榈酸在恒温下融化并均匀混合，在自然降温后制得，然后将石膏粉与相变材料按质量比10∶3混合，发热反应硬化脱模后制得复合储能石膏板。该相变材料相变温度为25.39℃，相变潜热为153.58kJ/kg。复合储能石膏板制作简单，成本低，可广泛应用于建筑领域。

Description

一种新型相变储能石膏板的配比与制备
技术领域：
本发明涉及一种含相变材料的复合储能石膏板的配比与制备方法。
背景技术：
目前，相变材料被广泛应用于建筑围护结构中储存能量。一般是将相变材料直接加入建筑基材，或者将相变材料做成微胶囊或封装起来加入建筑墙体中。由于受材料选择、使用地区和成本等问题的困扰建筑墙体用相变材料大多成本较高、相变潜热小、性能稳定性差、腐蚀性较强，同时建筑墙体用相变材料还要求与建筑基材结合性好，不易发生化学反应。由于受材料选择、使用地区和成本等问题的困扰，导致含相变材料的墙体只能发挥有限作用。
发明内容：
为了克服现有含相变材料墙体功能的不足，本发明配置出一种相变温度为25.39℃，相变潜热为153.58J/g的相变材料，并与石膏粉相复合，制成一种含相变材料的复合储能石膏板，该储能石膏板制作简单，成本低、环保，热稳定性好，便于在建筑上应用。
具体实施方式：
一、相变材料的配比及制备
电子天平称量质量比为85.7％∶14.3％的癸酸和棕榈酸，混合均匀放入玻璃容器内，然后放入80℃的恒温箱内保温2h，再将它放入超声波发生仪的水浴中，控制水浴温度为60℃左右，超声波振动2分钟后取出使其自然降温。该混合材料相变温度为25.39℃，相变潜热为153.58kJ/kg。
二、复合相变储能石膏板的制备
将普通石膏粉和已制得的相变材料按质量比10∶3混合，并加入适量的纤维素及水和PVA的混合物，快速搅拌，迅速倒入模具中压实并刮平，发热反应硬化后脱模，在通风处晾干。
采用该方法所获得的相变材料具有相变温度适宜、相变潜热大、过冷度小、化学稳定性好的优点。将其与石膏板相结合制得的复合储能石膏板制作简单、成本低，可广泛应用于建筑领域。

Claims (4)

1.一种含相变材料的复合储能石膏板的配比与制备方法，其特征在于：先制备出合适的相变材料，再将相变材料与石膏粉相复合，最终制备出一种复合储能石膏板。
2.按照权利要求1所述的配比与制备方法，其特征在于相变材料的配比与制作方法为：电子天平称量质量比为85.7％∶14.3％的癸酸和棕榈酸，混合均匀放入玻璃容器内，然后放入80℃的恒温箱内保温2h，再将它放入超声波发生仪的水浴中，控制水浴温度为60℃左右，超声波振动2分钟后取出使其自然降温。
3.按照权利要求2制得的相变材料，其特征在于：相变温度为25.39℃，相变潜热为153.58kJ/kg。
4.按照权利要求1所述的配比与制备方法，其特征在于复合储能石膏板的配比与制作方法为：将按照权利要求2制得的相变材料与普通石膏粉按质量比3∶10混合，并加入适量的纤维素及水和PVA的混合物，快速搅拌，迅速倒入模具中压实并刮平，发热反应硬化后脱模，在通风处晾干，即得复合储能石膏板。
CN2010102481830A 2010-08-09 2010-08-09 一种新型相变储能石膏板的配比与制备 Pending CN102372475A (zh)