CN102363695A - 水性双组分透明漆及其制备方法 - Google Patents

水性双组分透明漆及其制备方法 Download PDF

Info

Publication number
CN102363695A
CN102363695A CN2011101815913A CN201110181591A CN102363695A CN 102363695 A CN102363695 A CN 102363695A CN 2011101815913 A CN2011101815913 A CN 2011101815913A CN 201110181591 A CN201110181591 A CN 201110181591A CN 102363695 A CN102363695 A CN 102363695A
Authority
CN
China
Prior art keywords
component
parts
agent
aqueous
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2011101815913A
Other languages
English (en)
Other versions
CN102363695B (zh
Inventor
吕跃文
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHENGDU BEIDA COATING Co Ltd
Original Assignee
CHENGDU BEIDA COATING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHENGDU BEIDA COATING Co Ltd filed Critical CHENGDU BEIDA COATING Co Ltd
Priority to CN 201110181591 priority Critical patent/CN102363695B/zh
Publication of CN102363695A publication Critical patent/CN102363695A/zh
Application granted granted Critical
Publication of CN102363695B publication Critical patent/CN102363695B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种水性双组分透明漆及其制备方法，属于涂料领域，它由组分A和组分B组成，所述组分A的重量配比为：聚丙烯酸多元醇50～60份，分散剂0.1～0.5份，防沉剂0.1～0.5份，消泡剂0.1～0.5份，颜填料5～10份，流平剂0.1～0.5份，成膜助剂0.1～2.0份，水1.0～5.0份；所述组分B为阴离子改性HDI多异氰酸酯；所述组分A与组分B的重量比为：组分A︰组分B=1︰0.2～0.3。本发明具有优异的光泽和外观，耐污染性和化学品性优，不黄变、防锈、耐高温，可与乳胶漆等其他油漆同时施工。

Description

水性双组分透明漆及其制备方法
技术领域
本发明属于涂料领域，具体涉及一种水性双组分透明漆及其制备方法。
背景技术
现在市面上的各种涂料种类繁多，主要分为有机涂料和无机涂料，有机涂料根据使用的溶剂不同又分为有机溶剂型涂料和有机水性涂料。有机溶剂型涂料由于VOC高，不能满足人们日益增强的对环保的要求。
有机水性涂料，即水性涂料，现在日益成为研究的热点，以丙烯酸为主要成分的水性木器漆，主要特点是附着力好，不会加深木器的颜色，但耐磨及抗化学性较差，漆膜硬度较软，铅笔法则试为 HB ，丰满度较差，综合性能一般，施工易产生缺陷。
现有的涂料容易造成漆膜不均匀、一段时间后性能下降、没有附着力等漆病，而且耐污染性和化学品性差，容易黄变、防锈能力差、不耐高温等。
发明内容
本发明要解决的技术问题是现有技术中涂料容易造成漆膜不均匀、一段时间后性能下降、没有附着力等漆病，而且耐污染性和化学品性差，容易黄变、防锈能力差、不耐高温的问题，提供一种水性双组分透明漆及其制备方法。
本发明的技术方案如下：一种水性双组分透明漆，它由组分A和组分B组成，所述组分A的重量配比为：聚丙烯酸多元醇 50～60份，分散剂 0.1～0.5份，防沉剂0.1～0.5份，消泡剂0.1～0.5份，颜填料5～10份，流平剂0.1～0.5份，成膜助剂0.1～2.0份，水1.0～5.0份；所述组分B为阴离子改性HDI多异氰酸酯；所述组分A与组分B的重量比为：组分A︰组分B=1︰0.2～0.3。
其中，上述所述组分A的重量配比为：聚丙烯酸多元醇55份，分散剂0.3份，防沉剂0.3份，消泡剂0.3份，颜填料8份，流平剂0.3份，成膜助剂1份，水3份。
其中，上述所述组分A与组分B的重量比为1︰0.25。
其中，上述所述成膜助剂为醇酯-12。
本发明还提供一种水性双组分透明漆的制备方法，它包括以下步骤：
a、制备组分A：按重量份数向容器内依次加入聚丙烯酸多元醇50～60份、分散剂0.1～0.5份、防沉剂 0.1～0.5份、消泡剂 0.1～0.5份，600～800转/分钟搅拌均匀并缓慢加入颜填料5.0～10.0份，调整搅拌速度到1200～1500转/分钟搅拌10～15分钟，然后依次加入流平剂0.1～0.5份、成膜助剂 0.1～2.0份，在600～800转/分钟搅拌下搅拌均匀，用水1.0～5.0份清洗设备和调整粘度，过滤得到组分A；
b、将a步骤得到的组分A与组分B按重量比1︰0.2～0.3的配比加水调配均匀，即得成品，所述组分B为阴离子改性HDI多异氰酸酯。
其中，上述所述调整粘度是指调整粘度到120～130KU。
本发明是以水为溶剂或分散介质的涂料，它具有重要的环保意义，无毒环保，不含苯类等有害溶剂，不含游离TDI，由溶剂型PU向水性PU的无形转变。
本发明采用聚丙烯酸多元醇与多异氰酸酯经过化学交联发应，生成一种高性能的聚氨酯聚合物。解决了聚丙烯酸多元醇与阴离子改性HDI多异氰酸酯在低剪切力下的完美乳化，易于混合；解决了由于未键合的乳化剂在涂层中迁移而造成漆膜不均匀、一段时间后性能下降、没有附着力等漆病，确保乳化剂基团连接到聚合物链上且均匀分布，使涂层具有长期稳定性。
本发明具有优异的光泽和外观，耐污染性和化学品性优，不黄变、防锈、耐高温，可与乳胶漆等其他油漆同时施工。
具体实施方式
下列实施例中，聚丙烯酸多元醇采用德国拜耳公司的Bayhydrol A145，成膜助剂选用醇酯-12，阴离子改性HDI多异氰酸酯为德国拜耳的Bayhydur3100。
实施例1
a、按重量，在搅拌容器依次加入聚丙烯酸多元醇50份、分散剂（德国毕克的BYK 194）0.1份、防沉剂（帝斯巴隆LA350）0.1份、消泡剂（迪高公司的Tego 902W）0.1份，搅拌均匀，在700转/分钟搅拌下缓慢加入颜填料5.0份，调整搅拌速度到1200转/分钟搅拌10分钟，然后依次加入流平剂（德国毕克的BYK346）0.1份、成膜助剂 0.1份，在700转/分钟搅拌下搅拌均匀，用水1.0份清洗设备和调整粘度到120KU，过滤得到组分A。
b、按组分A︰组分B︰水=1︰0.2︰0.3的配比调配均匀，即得成品，所述组分B为阴离子改性HDI多异氰酸酯。
实施例2
a、按重量，在搅拌容器依次加入聚丙烯酸多元醇60份、分散剂（迪高公司的Tego730W）0.5份、防沉剂（帝斯巴隆LA350）0.5份、消泡剂（德国毕克的BYK028）0.5份搅拌均匀，在700转/分钟搅拌下缓慢加入颜填料10.0份，调整搅拌速度到1500转/分钟搅拌15分钟，然后依次加入流平剂（德国毕克的BYK346）0.5份、成膜助剂 2.0份，在700转/分钟搅拌下搅拌均匀，用水5.0份清洗设备和调整粘度到130KU，过滤得到组分A。
b、按组分A︰组分B︰水=1︰0.3︰0.5的配比调配均匀，即得成品，所述组分B为阴离子改性HDI多异氰酸酯。
实施例3
a、按重量，在搅拌容器依次加入聚丙烯酸多元醇55份、分散剂（德国毕克的BYK194）0.3份、防沉剂（帝斯巴隆LA350）0.3份、消泡剂（德国毕克的BYK028）0.3份搅拌均匀，在700转/分钟搅拌下缓慢加入颜填料8份，调整搅拌速度到1400转/分钟搅拌12分钟，然后依次加入流平剂(埃夫卡公司的EFKA3600)0.3份、成膜助剂1份，在700转/分钟搅拌下搅拌均匀，用水3份清洗设备和调整粘度到125KU，过滤得到组分A。
b、按组分A︰组分B︰水=1︰0.25︰0.4的配比调配均匀，即得成品，所述组分B为阴离子改性HDI多异氰酸酯。
实施例4
a、按重量，在搅拌容器依次加入聚丙烯酸多元醇53份、分散剂（德国毕克的BYK194）0.2份、防沉剂（帝斯巴隆LA350）0.4份、消泡剂（迪高公司的Tego801）0.2份搅拌均匀，在700转/分钟搅拌下缓慢加入颜填料8份，调整搅拌速度到1200转/分钟搅拌13分钟，然后依次加入流平剂（德国毕克的BYK346）0.3份、成膜助剂 1.5份，在700转/分钟搅拌下搅拌均匀，用水4份清洗设备和调整粘度到120KU，过滤得到组分A。
b、按组分A︰组分B︰水=1︰0.3︰0.4的配比调配均匀，即得成品，所述组分B为阴离子改性HDI多异氰酸酯。
实施例5
a、按重量，在搅拌容器依次加入聚丙烯酸多元醇53份、分散剂（德国毕克的BYK194）0.2份、防沉剂（帝斯巴隆LA350）0.4份、消泡剂（德国毕克的BYK025）0.2份搅拌均匀，在700转/分钟搅拌下缓慢加入颜填料7份，调整搅拌速度到1300转/分钟搅拌12分钟，然后依次加入流平剂（迪高公司的Tego 410）0.4份、成膜助剂1.7份，在700转/分钟搅拌下搅拌均匀，用水4份清洗设备和调整粘度到128KU，过滤得到组分A。
b、按组分A︰组分B︰水=1︰0.3︰0.45的配比调配均匀，即得成品，所述组分B为阴离子改性HDI多异氰酸酯。
 
表1各实施例产品性能参数表：
测试项目 溶剂型 实施例1 实施例2 实施例3 实施例4 实施例5
漆膜外观 平整光滑 平整光滑 平整光滑 平整光滑 平整光滑 平整光滑
环保性 含苯等有害溶剂 不含苯等有害溶剂 不含苯等有害溶剂 不含苯等有害溶剂 不含苯等有害溶剂 不含苯等有害溶剂
游离TDI 含 不含 不含 不含 不含 不含
附着力 0级 0级 0级 0级 0级 0级
铅笔硬度 HB HB HB HB HB HB
耐化学品性 优 优 优 优 优 优
消泡性 优 一般 优 一般 优 优
流平性 优 优 一般 一般 优 优
表干（min） 10-20 13 15 12 16 13
指压干（h） 2-4 3 3 3 3 3
打磨性 好 好 好 好 好 好
VOC（g/l） 小于580 ＜200 ＜200 ＜200 ＜200 ＜200
施工性 易 易 易 易 易 易
从表1看出，本发明的产品VOC含量明显低于溶剂型的漆，并且不含苯及游离TDI，更加环保，其他指标也与溶剂型差别不大。

Claims (6)

1.一种水性双组分透明漆，其特征在于：它由组分A和组分B组成，所述组分A的重量配比为：聚丙烯酸多元醇 50～60份，分散剂 0.1～0.5份，防沉剂0.1～0.5份，消泡剂0.1～0.5份，颜填料5～10份，流平剂0.1～0.5份，成膜助剂0.1～2.0份，水1.0～5.0份；所述组分B为阴离子改性HDI多异氰酸酯；所述组分A与组分B的重量比为：组分A︰组分B=1︰0.2～0.3。
2.根据权利要求1所述的水性双组分透明漆，其特征在于：所述组分A的重量配比为：聚丙烯酸多元醇55份，分散剂0.3份，防沉剂0.3份，消泡剂0.3份，颜填料8份，流平剂0.3份，成膜助剂1份，水3份。
3.根据权利要求1所述的水性双组分透明漆，其特征在于：所述组分A与组分B的重量比为1︰0.25。
4.根据权利要求1所述的水性双组分透明漆，其特征在于：所述成膜助剂为醇酯-12。
5.水性双组分透明漆的制备方法，其特征在于：它包括以下步骤：
a、制备组分A：按重量份数向容器内依次加入聚丙烯酸多元醇50～60份、分散剂0.1～0.5份、防沉剂 0.1～0.5份、消泡剂 0.1～0.5份，600～800转/分钟搅拌均匀并缓慢加入颜填料5.0～10.0份，调整搅拌速度到1200～1500转/分钟搅拌10～15分钟，然后依次加入流平剂0.1～0.5份、成膜助剂 0.1～2.0份，在600～800转/分钟搅拌下搅拌均匀，用水1.0～5.0份清洗设备和调整粘度，过滤得到组分A；
b、将a步骤得到的组分A与组分B按重量比1︰0.2～0.3的配比加水调配均匀，即得成品，所述组分B为阴离子改性HDI多异氰酸酯。
6.根据权利要求5所述的水性双组分透明漆的制备方法，其特征在于：所述调整粘度是指调整粘度到120～130KU。
CN 201110181591 2011-06-30 2011-06-30 水性双组分透明漆及其制备方法 Expired - Fee Related CN102363695B (zh)