CN102363650B - 高弹性、高硬度橡胶 - Google Patents

高弹性、高硬度橡胶 Download PDF

Info

Publication number
CN102363650B
CN102363650B CN 201110243534 CN201110243534A CN102363650B CN 102363650 B CN102363650 B CN 102363650B CN 201110243534 CN201110243534 CN 201110243534 CN 201110243534 A CN201110243534 A CN 201110243534A CN 102363650 B CN102363650 B CN 102363650B
Authority
CN
China
Prior art keywords
rubber
carbon black
percent
equal
produced
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 201110243534
Other languages
English (en)
Other versions
CN102363650A (zh
Inventor
潘琦俊
杨建辉
施先锋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhu Hetian Automotive Industry Co Ltd
Original Assignee
Wuhu Hetian Automotive Industry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhu Hetian Automotive Industry Co Ltd filed Critical Wuhu Hetian Automotive Industry Co Ltd
Priority to CN 201110243534 priority Critical patent/CN102363650B/zh
Publication of CN102363650A publication Critical patent/CN102363650A/zh
Application granted granted Critical
Publication of CN102363650B publication Critical patent/CN102363650B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种高强度、高弹性橡胶，所述的橡胶含有恒粘天然胶、氧化锌、硬脂酸、防老剂RD、三氧化二硼、碳黑N550、碳黑N330、聚合硫、N-氧二乙撑基-2-苯骈噻唑次磺酰胺、二硫化二苯骈噻唑、二硫化四甲基秋兰姆、防焦剂CTP，本发明与现有技术相比，通过对各种材料及用量的选择，使橡胶的硬度≥82、拉伸强度≥18MPa，扯断伸长率≥350％，压缩永久变形率小于22％，回弹性大于65％。

Description

高弹性、高硬度橡胶
技术领域
本发明涉及橡胶，具体涉及用于汽车减震产品“衬套”的高硬度、高弹性橡胶。
背景技术
目前用于汽车使用的减震产品“衬套”的橡胶的硬度为15、拉伸强度为15Mpa，扯断伸长率为320％，压缩永久变形率为28％，回弹性为35％，压缩永久变形率是28％(70℃×22h)，上述性能的橡胶远远不能满足实际的需要。
发明内容
本发明所要解决的技术问题是提供一种橡胶回弹性大于50％的高强度、高弹性的橡胶。
本发明解决技术问题的技术方案为：高强度、高弹性橡胶，含有以下重量份的物质：
Figure BDA0000085573000000011
Figure BDA0000085573000000021
优选的高强度、高弹性橡胶，含有以下重量份的物质：
Figure BDA0000085573000000022
所述的防老剂RD为2，2，4-三甲基-1，2-二氢化喹啉，由中国台湾顺聚公司生产。
所述的防老剂4010NA为N-异丙基-N-本集对苯二胺类，由台湾顺聚公司生产。
防焦剂CTP-80由博兴科源新材料有限责任公司生产。
本发明的橡胶制备方法与现有的制备方法相同。
本发明与现有技术相比，通过对各种材料及用量的选择，使橡胶的硬度≥82、拉伸强度≥18Mpa，扯断伸长率≥350％，压缩永久变形率小于22％，回弹性大于50％。
具体实施方式
下面结合实施例对本发明作详细的说明。
本发明的恒粘天然胶(CV60)由泰国生产；
氧化锌由广州台翔公司生产；
硬脂酸由印尼1801公司生产；
防老剂RD由中国台湾顺聚公司生产；
防老剂4010NA由中国台湾顺聚公司生产；
碳黑N550由美国哥伦比亚公司生产；
碳黑N330由美国哥伦比亚公司生产；
聚合硫IS-60由美国Harwick公司生产；
N-氧二乙撑基-2-苯骈噻唑次磺酰胺(促进剂NOBS-80)由德国莱茵公司生产；
二硫化二苯骈噻唑(促进剂DM)由德国莱茵公司生产；
二硫化四甲基秋兰姆(促进剂TMTD)由德国莱茵公司生产；
防焦剂CTP由由博兴科源新材料有限责任公司公司生产；
实施例1：
  序号   材料名称   重量份
  1   恒粘天然胶(CV60)   100
  2   氧化锌   5
  3   硬脂酸   2
  4   防老剂RD   1
  5   防老剂4010NA   1.5
  6   碳黑N550   70
  7   碳黑N330   35
  8   聚合硫IS-60   1
  9   促进剂NOBS-80   2.2
  10   促进剂DM   1
  11   促进剂TMTD   1
  12   防焦剂CTP   0.3
实施例2：
  序号   材料名称   重量份
  1   恒粘天然胶(CV60)   80
  2   氧化锌   3
  3   硬脂酸   0.5
  4   防老剂RD   1.5
  5   防老剂4010NA   1
  6   碳黑N550   50
  7   碳黑N330   10
  8   聚合硫IS-60   0.5
  9   促进剂NOBS-80   1
  10   促进剂DM   1
  11   促进剂TMTD   0.5
  12   防焦剂CTP   0.1
实施例3：
  序号   材料名称   重量份
  1   恒粘天然胶(CV60)   110
  2   氧化锌   10
  3   硬脂酸   3
  4   防老剂RD   3
  5   防老剂4010NA   3
  6   碳黑N550   80
  7   碳黑N330   50
  8   聚合硫IS-60   1.5
  9   促进剂NOBS-80   2.0
  10   促进剂DM   0.5
  11   促进剂TMTD   0.5
  12   防焦剂CTP   0.3
实施例4：除碳黑N550为40份、N330为60份外，其余与实施例1相同。
本发明的硬度按照国标GB/T6031-1998的标准进行检测，单位为IRHD；
拉伸强度按照国标GB/T528-1998标准进行检测，单位为MPa；
扯断伸长率按照国标GB/T528-1998标准进行检测，单位为％；
压缩永久变形率按照国标GB1683-84的标准进行检测，单位为％；
回弹性按照国标GB/T1681-1991的标准进行检测，单位为％；
实施例1、2、3所生产的橡胶如表1所示：
 序号   硬度   拉伸强度   扯断伸长率   压缩永久变形率   回弹性
 实施例1   82   21   423   20.8％   61％
 实施例2   85   20   352   21％   51％
 实施例3   86   18   380   22％   53％
 实施例4   70   15   300   30％   35％

Claims (2)

1.高强度、高弹性橡胶，含有以下重量份的物质：
Figure FDA0000191756381
2.根据权利要求1所述的高强度、高弹性橡胶，其特征在于：含有以下重量份的物质：
Figure FDA0000191756383
CN 201110243534 2011-08-24 2011-08-24 高弹性、高硬度橡胶 Expired - Fee Related CN102363650B (zh)