CN102352212A - 一种高强度金属胶粘剂及其制备方法 - Google Patents

一种高强度金属胶粘剂及其制备方法 Download PDF

Info

Publication number
CN102352212A
CN102352212A CN2011102622123A CN201110262212A CN102352212A CN 102352212 A CN102352212 A CN 102352212A CN 2011102622123 A CN2011102622123 A CN 2011102622123A CN 201110262212 A CN201110262212 A CN 201110262212A CN 102352212 A CN102352212 A CN 102352212A
Authority
CN
China
Prior art keywords
preparation
strength metal
metal adhesive
parts
constitutive material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2011102622123A
Other languages
English (en)
Other versions
CN102352212B (zh
Inventor
杜建
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BENGBU LIQUN ELECTRONICS Co Ltd
Original Assignee
BENGBU LIQUN ELECTRONICS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BENGBU LIQUN ELECTRONICS Co Ltd filed Critical BENGBU LIQUN ELECTRONICS Co Ltd
Priority to CN 201110262212 priority Critical patent/CN102352212B/zh
Publication of CN102352212A publication Critical patent/CN102352212A/zh
Application granted granted Critical
Publication of CN102352212B publication Critical patent/CN102352212B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种高强度金属胶粘剂及其制备方法，其主要是将组成原料E-44环氧树脂、硅烷偶联剂、环氧丙烷苯基醚、三乙胺、凹凸棒土、甲基三乙酰氧基硅烷、顺丁烯二酸酐和石墨粉按组成原料的重量份比例混合搅拌反应得到高强度金属胶粘剂。本发明制备方法简单，操作方便，成本低，制得的高强度金属胶粘剂粘合强度高、耐热性好，适用性强。

Description

一种高强度金属胶粘剂及其制备方法
技术领域
本发明涉及一种胶黏剂，具体涉及一种高强度金属胶粘剂及其制备方法。
背景技术
随着橡胶工业的飞速发展，橡胶复合材料得到广泛的应用，而橡胶与高强度金属胶粘剂的质量是复合材料成功的关键，复合制品种类的增多及应用领域的拓展，对粘合技术的要求越来越苛刻。传统的氯化橡胶法、异氰酸酯法等技术已不能满足新的要求。
发明内容
针对现有技术的不足，本发明的目的在于提供一种粘合强度高、耐热性好、价格低的高强度金属胶粘剂及其制备方法。
为了实现上述目的本发明采用如下技术方案：
高强度金属胶粘剂，其特征在于其组成原料的重量份为：E-44环氧树脂50-60份、硅烷偶联剂15-25份、环氧丙烷苯基醚5-10份、三乙胺1-3份、凹凸棒土1-3份、甲基三乙酰氧基硅烷20-25份、顺丁烯二酸酐5-10份和石墨粉1-2份。
高强度金属胶粘剂的制备方法，其特征在于包括以下步骤：
（1）按组成原料的重量份混合E-44环氧树脂、环氧丙烷苯基醚、甲基三乙酰氧基硅烷和顺丁烯二酸酐，搅拌均匀，得到混合液A；
（2）在步骤（1）得到的混合液A中按组成原料重量份加入三乙胺、凹凸棒土、硅烷偶联剂和石墨粉，反应3-4小时，控制温度80-85℃，反应冷却后出料。
本发明的有益效果：
本发明制备方法简单，操作方便，成本低，制得的高强度金属胶粘剂粘合强度高、耐热性好，适用性强。
具体实施方式
实施例1：高强度金属胶粘剂，其组成原料的重量份为：E-44环氧树脂50份、硅烷偶联剂15份、环氧丙烷苯基醚5份、三乙胺1份、凹凸棒土1份、甲基三乙酰氧基硅烷20份、顺丁烯二酸酐5份和石墨粉1份。
高强度金属胶粘剂的制备方法，包括以下步骤：
（1）按组成原料的重量份混合E-44环氧树脂、环氧丙烷苯基醚、甲基三乙酰氧基硅烷和顺丁烯二酸酐，搅拌均匀，得到混合液A；
（2）在步骤（1）得到的混合液A中按组成原料重量份加入三乙胺、凹凸棒土、硅烷偶联剂和石墨粉，反应3-4小时，控制温度80-85℃，反应冷却后出料。
实施例2：高强度金属胶粘剂，其组成原料的重量份为：E-44环氧树脂55份、硅烷偶联剂20份、环氧丙烷苯基醚8份、三乙胺2份、凹凸棒土2份、甲基三乙酰氧基硅烷22份、顺丁烯二酸酐8份和石墨粉1.5份。
高强度金属胶粘剂的制备方法，包括以下步骤：
（1）按组成原料的重量份混合E-44环氧树脂、环氧丙烷苯基醚、甲基三乙酰氧基硅烷和顺丁烯二酸酐，搅拌均匀，得到混合液A；
（2）在步骤（1）得到的混合液A中按组成原料重量份加入三乙胺、凹凸棒土、硅烷偶联剂和石墨粉，反应3-4小时，控制温度80-85℃，反应冷却后出料。
实施例3：高强度金属胶粘剂，其组成原料的重量份为：E-44环氧树脂60份、硅烷偶联剂25份、环氧丙烷苯基醚10份、三乙胺3份、凹凸棒土3份、甲基三乙酰氧基硅烷25份、顺丁烯二酸酐10份和石墨粉2份。
高强度金属胶粘剂的制备方法，包括以下步骤：
（1）按组成原料的重量份混合E-44环氧树脂、环氧丙烷苯基醚、甲基三乙酰氧基硅烷和顺丁烯二酸酐，搅拌均匀，得到混合液A；
（2）在步骤（1）得到的混合液A中按组成原料重量份加入三乙胺、凹凸棒土、硅烷偶联剂和石墨粉，反应3-4小时，控制温度80-85℃，反应冷却后出料。
实施例4：本发明制备的金属胶粘剂与普通金属胶粘剂性能对比：
性能 本发明金属胶粘剂 普通金属胶粘剂
定位时间（min） 2.8 2.4
储存稳定性（h） 110 30
拉伸剪切强度（Mpa） 28.8 28.6
老化后的拉伸剪切强度（Mpa） 31.2 29.7

Claims (2)

1.一种高强度金属胶粘剂，其特征在于其组成原料的重量份为：E-44环氧树脂50-60份、硅烷偶联剂15-25份、环氧丙烷苯基醚5-10份、三乙胺1-3份、凹凸棒土1-3份、甲基三乙酰氧基硅烷20-25份、顺丁烯二酸酐5-10份和石墨粉1-2份。
2.一种如权利要求1所述的高强度金属胶粘剂的制备方法，其特征在于包括以下步骤：
（1）按组成原料的重量份混合E-44环氧树脂、环氧丙烷苯基醚、甲基三乙酰氧基硅烷和顺丁烯二酸酐，搅拌均匀，得到混合液A；
（2）在步骤（1）得到的混合液A中按组成原料重量份加入三乙胺、凹凸棒土、硅烷偶联剂和石墨粉，反应3-4小时，控制温度80-85℃，反应冷却后出料。
CN 201110262212 2011-09-06 2011-09-06 一种高强度金属胶粘剂及其制备方法 Expired - Fee Related CN102352212B (zh)